중성자 조사에 따른 Ni도금피복재에서의 He발생량평가
He Generation Evaluation on Electrodeposited Ni After Neutron Exposure
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Neutron dose level at bottom head of a reactor pressure vessel (RPV) was calculated using reactor vessel neutron transport for a Korean nuclear power plant A. At 34 EFPY with a 40-year (2042) design life after plating repair, irradiation fast neutron effect was 6.6x1015 n/cm2. As helium(He) gas can be generated by Ni only at 1/106 level of 5 × 1021 n/cm2, He generation possibility in the Ni plating layer is very little during 40 years of operation (2042, 34 EFPY). Thermal neutrons can significantly affect the generation of He from Ni metal. At 10 years after a repair, He can be generated at a level of about 0.06 appm, a level that can add general welding repair without any consideration. After 40 years of repair, 9.8 appm of He may be generated. Although this is a rather high value, it is within the range of 0.1 to 10 appm when welding repair can be applied. Clad repair by Ni electroplating technology is expected to greatly improve the operation efficiency by improving the safety and shortening the maintenance period of the nuclear power plant.
Abstract
Neutron dose level at bottom head of a reactor pressure vessel (RPV) was calculated using reactor vessel neutron transport for a Korean nuclear power plant A. At 34 EFPY with a 40-year (2042) design life after plating repair, irradiation fast neutron effect was 6.6x1015 n/cm2. As helium(He) gas can be generated by Ni only at 1/106 level of 5 × 1021 n/cm2, He generation possibility in the Ni plating layer is very little during 40 years of operation (2042, 34 EFPY). Thermal neutrons can significantly affect the generation of He from Ni metal. At 10 years after a repair, He can be generated at a level of about 0.06 appm, a level that can add general welding repair without any consideration. After 40 years of repair, 9.8 appm of He may be generated. Although this is a rather high value, it is within the range of 0.1 to 10 appm when welding repair can be applied. Clad repair by Ni electroplating technology is expected to greatly improve the operation efficiency by improving the safety and shortening the maintenance period of the nuclear power plant.
참고문헌 (4)
- 황성식, "압력용기 클래드 보수용 전해니켈도금 인자 관계 연구", CORROSION SCIENCE AND TECHNOLOGY, 18(4), pp.148~153 (2019), 한국부식방식학회[DOI]
- Wayne Lunceford, , Proceedings of the ASME 2016 Pressure Vessels and Piping Conference PVP 2016 (2016)
- R. K. Disney, "LTR-REA-00-637, Release of SYNTHE 1.0", ~ (2000)
- M. Griffiths, , Proceedings of 16th Environmental Degradation on Materials in Nuclear Power Systems-Water reactors, ‘Degradation of Ni-alloy Components in CANDU Reactor Cores’ (2013)