Alloy 600에 전기 도금한 Ni-P-Fe 및 Ni-P-B 층의 열적 안정성 연구
Study on Thermal Stability of Ni-P-Fe and Ni-P-B Layers Electroplated on Alloy 600
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, thermal stability of the mechanical properties of Ni-P-B and Ni-P-Fe layers electroplated on Alloy 600 material was evaluated by measuring their microhardness, tensile strength, and elongation after heat treatment at 325℃ and 400℃. According to the results, there was no noticeable change in microhardness of the two electrodeposits before and after heat treatment at the temperatures for 30 days. In the case of a Ni-P-B electrodeposit, ultimate tensile strength (UTS) slightly increases with heat treatment time, while its elongation decreases, showing good thermal stability in the mechanical properties at high temperature. On the other hand, UTS and elongation of Ni-P-Fe decrease with heat treatment time, which is very unusual observation. This result was attributed to the bad microstructure of Ni-P-Fe having many defects in the deposit formed early stage of an electroplating process and their redistribution to link to become large ones during heat treatment
Abstract
In this study, thermal stability of the mechanical properties of Ni-P-B and Ni-P-Fe layers electroplated on Alloy 600 material was evaluated by measuring their microhardness, tensile strength, and elongation after heat treatment at 325℃ and 400℃. According to the results, there was no noticeable change in microhardness of the two electrodeposits before and after heat treatment at the temperatures for 30 days. In the case of a Ni-P-B electrodeposit, ultimate tensile strength (UTS) slightly increases with heat treatment time, while its elongation decreases, showing good thermal stability in the mechanical properties at high temperature. On the other hand, UTS and elongation of Ni-P-Fe decrease with heat treatment time, which is very unusual observation. This result was attributed to the bad microstructure of Ni-P-Fe having many defects in the deposit formed early stage of an electroplating process and their redistribution to link to become large ones during heat treatment
참고문헌 (10)
- P. M. Scott, , Corrosion, 56, pp.771~ (2000)
- H. P. Kim, "Stress Corrosion Cracking of a Kori 1 Retired Steam Generator Tube", EUROCORR2004 (2004)
- G. Palumbo, , Nanostructured Materials, 9, pp.737~ (1997)
- M. da Silva, , Mater. Sci. Eng. A, 445, pp.31~ (2007)
- D. J. Kim, , Surf. Coat. Technol., 192, pp.88~ (2005)
- D. J. Kim, , Surf. Coat. Technol, 202, pp.2519~ (2008)
- KAERI, Assessment of Corrosion Characteristics and Development of Remedial Technology in Nuclear Materials, "J. S. Kim", ~, pp.KAERI (2004), RR-2514[DOI]
- A. M. Alfantazi, , Mater. Sci. Eng. A, 212, pp.123~ (1996)
- M. H. Seo, , Surf. Coat. Technol., 176(2), pp.135~ (2004)
- K. Krishnaveni, , Surf. Coat. Technol., 190, pp.115~ (2005)