Effects of Weld Fume on the Corrosion Protection of Epoxy Coated on Carbon Steel
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Welding was widely used in shipbuilding industries as a joining method. In present study, the effects of welding fume contaminated on steel surface on corrosion protection were examined by water ballast simulation test and condensation chamber test. Pull-off adhesion test, blistering test and cathodic disbondment test were carried out to evaluate the effects of residual welding fume. Consequently, it was clearly indicated that the residual welding fume didn't affect the corrosion protection of epoxy coated on steel when surface was treated by light sweep blasting to heavy sweep blasting which was applied in this study.
Abstract
Welding was widely used in shipbuilding industries as a joining method. In present study, the effects of welding fume contaminated on steel surface on corrosion protection were examined by water ballast simulation test and condensation chamber test. Pull-off adhesion test, blistering test and cathodic disbondment test were carried out to evaluate the effects of residual welding fume. Consequently, it was clearly indicated that the residual welding fume didn't affect the corrosion protection of epoxy coated on steel when surface was treated by light sweep blasting to heavy sweep blasting which was applied in this study.
참고문헌 (36)
- C.G. Munger, "Corrosion Prevention by Protective Coatings, 2nd ed" (1999), NACE
- R.J. Brodd, "Encyclopedia of Electrochemistry of the Elements, vol. 6", pp.35~ (1976), Marcel Decker
- T.K. Ross, , Trans. Inst. Metal Finishing, 40, pp.186~ (1983)
- J. E. O. MAYNE, , Soc. Chem., Ind. Rev, 22, pp.109~ (1944)
- J, E. O. MAYNE, , J. Soc. Chem. Ind, 66, pp.93~ (1947)
- O.O. Knudsen, , Prog. Org. Coat, 54, pp.224~ (2005)
- T. K. Ross, , Trans. Inst. Metal Finishing, 40, pp.186~ (1963)
- D. S. NEWTON, , J.O.C.C, 48, pp.382~ (1965)
- F. THEILER, , Corros. Sci, 14, pp.405~ (1974)
- T. K. Ross, , Corros. Sci, 17, pp.341~ (1977)
- T. SZAUER, , J.O.C.C.A, 67, pp.13~ (1984)
- S. A. LNDQVlST, , J.O.C.C.A, 68, pp.10~ (1985)
- S. FELIU, , J. Coatings Technol, 61, pp.63~ (1989)
- S. FELIU, , J. Coatings Technol, 61, pp.71~ (1989)
- Trinh Anh Truc, "Improvement of Protective Properties of Top Coatings Applied on Zinc-Rich Primer by 3-Aminopropyl-Triethoxysilan and 2(Benzothialylthio) Succinic acid", CORROSION SCIENCE AND TECHNOLOGY, 3(3), pp.107~111 (2004), 한국부식방식학회
- "Annex 1, Resolution MSC.215(82), Performance standard for protective coatings for dedicated seawater water ballast tanks in all types of ships and double side skin spaces of bulk carriers, 8 December", ~ (2006)
- "ISO 6270-1:1998 Paints and varnishes - Determination of resistance to humidity - Part 1:Continuous condensation", ~
- "ISO 4628", 2:2003. Paints and varnishes - Evaluation of degradation of coatings -Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 2. & Part 3
- "ISO 4624:2002. Pull-off test for adhesion", ~ (2002)
- W. A. ANDERTON, , Off. Dig, 36, pp.1210~ (1964)
- R. R. WIGGLE, , J. Paint Technol, 40, pp.174~ (1968)
- H. LEIDHEISER, , Corrosion, 32, pp.69~ (1976)
- A. G. SMITH, , Ind. Engng Chem. Prod. Res. Dev, 17, pp.42~ (1978)
- E. L. KOEHLER, , Corrosion, 33, pp.209~ (1977)
- J. J. RITrER, , J. Coat. Technol, 54, pp.51~ (1982)
- R. C. ADDISON, , Proc. 17th Int. Symp. on AcousticalImaging (1988)
- E. L. KOEHLER, , Corrosion, 40, pp.5~ (1984)
- J. S. HAMMOND, , Corros. Sci, 21, pp.239~ (1981)
- J. E. CASTLE, , Ind. Engng Chem. Prod. Res. Dev, 24, pp.361~ (1985)
- H. LEIDHEISER, , J. Coat. Technol, 53, pp.77~ (1981)
- H. LEIDHEISER, , Prog. Org. Coat, 11, pp.19~ (1983)
- K. MCLEOD, (1984), University of Oxford
- J. D. B. SHARMAN, (1991), University of Oxford
- "ASTM G95 - 07 Standard Test Method for Cathodic Disbondment Test of Pipeline Coatings", ~
- "RECOMMENDED PRACTICE, DNV-RP-B401, Cathodic Protection Design, January", ~ (2005)
- Amy Forsgren, "Corrosion control through organic coatings", pp.106~ (1996), CRC press