탄화규소/7091알루미늄 복합재료의 부식거동
Corrosion Behavior of Silicon Carbide/7091 Aluminum Matrix Composites
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The effects of volume fraction (15-30%) of SiC particulate reinforcements on the corrosion behavior of SiCp/7091Al composites in the 3.5% NaCl solution were studied by electrochemical techniques and scanning electron microscopy. The results showed that the amount of SiC particulate reinforcements did not cause much difference in the corrosion behavior of SiCp/7091 Al composites but the corrosion rate was proportional to the amount of SiCp reinforcement. And numerous pits and severe dissolution of the matrix was observed probably due to the discontinuities and galvanic effects between Al matrix and SiC reinforcements.
Abstract
The effects of volume fraction (15-30%) of SiC particulate reinforcements on the corrosion behavior of SiCp/7091Al composites in the 3.5% NaCl solution were studied by electrochemical techniques and scanning electron microscopy. The results showed that the amount of SiC particulate reinforcements did not cause much difference in the corrosion behavior of SiCp/7091 Al composites but the corrosion rate was proportional to the amount of SiCp reinforcement. And numerous pits and severe dissolution of the matrix was observed probably due to the discontinuities and galvanic effects between Al matrix and SiC reinforcements.
참고문헌 (12)
- C. E. Da Costa, , Rev. Metal. Madrid, 36, pp.179~ (2000)
- M. Hutchings, "Comprehensive Composite Materials, 3", pp.501~ (2000), Elsevier Science Ltd
- A. Pardo, , Corros. Sci, 47, pp.1750~ (2005)
- G. Huang, , Corros. Sci. Tech, 31, pp.215~ (2002)
- Byoung-Hyun Yoon, "Corrosion Behavior of Arc Weld and Friction Stir Weld in Al 6061-T6 Alloys", CORROSION SCIENCE AND TECHNOLOGY, 5(6), pp.196~200 (2006), 한국부식방식학회
- H. Sun, , Corrosion, 47, pp.742~ (1991)
- C. HE, , J. Mater. Sci. Technol, 18, pp.261~ (2002)
- R. L. Deuis, , Corrosion, 53, pp.880~ (1997)
- K. D. Lore, , Proc. Meeting of the Electrochemical Society (1981)
- A. J. Trowsdate, , Corros. Sci, 38, pp.177~ (1996)
- P. P. Trzaskoma, , J. Electrochem. Soc, 130, pp.1804~ (1983)
- D. M. Aylor, , J. Electrochem. Soc, 132, pp.1277~ (1985)