SiC 입자 강화 알루미늄기 복합재료의 표면미소 피로균열 발생 및 초기진전거동
Initiation and Growth Behavior of Small Surface Fatigue Crack on SiC Particle Reinforced Aluminum Composite
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Reversed plane bending fatigue tests were conducted on SiC particle aluminum composite. The initiation and growth behaviors of small surface fatigue cracks were continuously monitored by the replica technique and investigated in detail. The fatigue life of MMC is shorter than that of matrix because there exists interface debonding of SiC particles and matrix on the whole face of the notch part in the casting metal matrix composite(MMC). The coalescence of micro-cracks was observed in the tests conducted at high stress levels. Due to the coalescence, a higher crack growth rate of small cracks rather than those of long cracks was recognized in da/dn-Κmax relationship.
Abstract
Reversed plane bending fatigue tests were conducted on SiC particle aluminum composite. The initiation and growth behaviors of small surface fatigue cracks were continuously monitored by the replica technique and investigated in detail. The fatigue life of MMC is shorter than that of matrix because there exists interface debonding of SiC particles and matrix on the whole face of the notch part in the casting metal matrix composite(MMC). The coalescence of micro-cracks was observed in the tests conducted at high stress levels. Due to the coalescence, a higher crack growth rate of small cracks rather than those of long cracks was recognized in da/dn-Κmax relationship.
참고문헌 (17)
- K.Murayama, "Activation of Yses Development in Advanced Composite Materials", Material System, 11, pp.5~12 (1992)
- S.Kumai, "Fatigue crack growth in SiC particulate reinforced aluminium alloys", atigue90, .Ⅱ,, pp.869~874 (1990)
- P.Paris, "A Critical Analysis of Crack propagation Laws", Trans. ASMESer.D, 85, pp.528~533 (1963)
- The Significance of Fatigue Crack Closure, "W.Elber", 230~242, pp.ASTM,STP486 (1971)
- J.K.Shang, "On the particle-size dependence of fatigue crack propagation thresholds in SiC-particulate-reinforced aluminum-alloy composites:Role of crack closure and crack trapping", Acta metall, 37(8), pp.2267~2278 (1989)
- 小林俊郞(外4名), "SiC粒子强化6061アルミニウムの疲勞龜裂傳播特性", 日本金屬學會誌, 55(1), pp.72~78 (1991)
- A.F Whitehouse, "Cavity Formation During Tensile Stringing of Particulate and short Fiber Metal Matrix Composites", Acta. Metall. Mater, 41(6), pp.1701~1711 (1993)
- 小磯信重, "SiC 粒子强化 Al 合金의 疲勞特性", 材料, 38(433), pp.1206~1211 (1989)
- S.B. Biner, "Growth of Fatigue Cracks Emanating from Notches in SiC particulate Aluminum Composite", Fatigue Fract. Engng. Mater. Struct, 13(6), pp.637~646 (1990)
- E.R.de los Rios, "Short crack fatigue behaviour in a medium carbon steel", Fatigue Engng. mater. struct, 7, pp.97~108 (1984)
- M.H.El Haddad, "Fatigue crack propagation of short cracks", ASME Journal of Engng. Mater. and Technology, 101, pp.42~46 (1979)
- S.Pearson, "Initiation of Fatigue Cracks in Commercial Alloys and the subsequent propagation of very short cracks", Eng. Fract. Mech, 7, pp.235~247 (1975)
- J.Lankford, "The Growth of Long Fatigue Crack Growth in a SiC Reinforced Aluminum Alloy", Fatigue Fract. Engng. Mater. Struct, 5(3), pp.233~248 (1982)
- J.K.Shang, "Crack Bridging by uncracked Ligaments during Fatigue-Crack Growth in SiC-Reinforced Aluminum-Alloy Composites", Metall. Trans. A, 20A, pp.897~908 (1989)
- 增田千利, "SiC ウイスカ-强化及び SiC 粒子分散 複合材料の疲勞破壞 機構", 鐵と鋼, 75(9), pp.1753~1760 (1989)
- Stress intensity factor equations for cracks in three-dimensional finite bodies, "J.C.Newman", 238~265, pp.ASTM STP 791 (1983)
- 皮籠石紀雄, "Al合金鑄物のき裂傳ぱ特性に及ばす熱處理の影響", 日本機械學會論文集, 55(516), pp.1733~1739 (1989)