우드칩을 연료로 하는 열병합발전소의 회분 퇴적 및 설비 고장 원인 분석
Investigating the Cause of Ash Deposition and Equipment Failure in Wood Chip-Fueled Cogeneration Plant
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The use of biomass is increasing as a response to the convention on climate change. In Korea, a method applied to replace fossil fuels is using wood chips in a cogeneration plant. To remove air pollutants generated by burning wood chips, a selective denitrification facility (Selective catalytic reduction, SCR) is installed downstream. However, problems such as ash deposition and descaling of the equipment surface have been reported. The cause is thought to be unreacted ammonia slip caused by ammonia ions injected into the reducing agent and metal corrosion caused by an acidic environment. Element analysis confirmed that ash contained alkali metals and sulfur that could cause catalyst poisoning, leading to an increase in the size of ash particle and deposition. Measurement of the size of ash deposited inside the facility confirmed that the size of ash deposited on the catalyst was approximately three times larger than the size of generally formed ash. Therefore, it was concluded that a reduction in pore area of the catalyst by ash deposition on the surface of the catalyst could lead to a problem of increasing differential pressure in a denitrification facility.
Abstract
The use of biomass is increasing as a response to the convention on climate change. In Korea, a method applied to replace fossil fuels is using wood chips in a cogeneration plant. To remove air pollutants generated by burning wood chips, a selective denitrification facility (Selective catalytic reduction, SCR) is installed downstream. However, problems such as ash deposition and descaling of the equipment surface have been reported. The cause is thought to be unreacted ammonia slip caused by ammonia ions injected into the reducing agent and metal corrosion caused by an acidic environment. Element analysis confirmed that ash contained alkali metals and sulfur that could cause catalyst poisoning, leading to an increase in the size of ash particle and deposition. Measurement of the size of ash deposited inside the facility confirmed that the size of ash deposited on the catalyst was approximately three times larger than the size of generally formed ash. Therefore, it was concluded that a reduction in pore area of the catalyst by ash deposition on the surface of the catalyst could lead to a problem of increasing differential pressure in a denitrification facility.
참고문헌 (16)
- Mahendra K. Misra, "Wood ash composition as a function of furnace temperature", Biomass and Bioenergy, 4(2), pp.103~116 (1993), Elsevier BV[DOI]
- Yafei Guo, "CO2 capture and sorbent regeneration performances of some wood ash materials", Applied Energy, 137, pp.26~36 (2015), Elsevier BV[DOI]
- 이동복, "바이오매스 발전시 염소가스에 의한 고온부식", 한국표면공학회지, 49(1), pp.14~19 (2016), 한국표면공학회[DOI]
- 백승기, "순환유동층보일러의 과열기 튜브 부식에 알칼리 금속과 염소가 미치는 영향", 공업화학, 28(1), pp.29~34 (2017), 한국공업화학회[DOI]
- Luciana Lisi, "Poisoning of SCR Catalysts by Alkali and Alkaline Earth Metals", Catalysts, 10(12), pp.1475~ (2020), MDPI AG[DOI]
- 여종현, "알칼리 금속 이온(Na, K)이 V", W, 공업화학, pp.2020, 31(5)[DOI]
- Kai Guo, "Conquering ammonium bisulfate poison over low-temperature NH3-SCR catalysts: A critical review", Applied Catalysis B: Environmental, 297, pp.120388~ (2021), Elsevier BV[DOI]
- Xiangmin Wang, "Understanding the deposition and reaction mechanism of ammonium bisulfate on a vanadia SCR catalyst: A combined DFT and experimental study", Applied Catalysis B: Environmental, 260, pp.118168~ (2020), Elsevier BV[DOI]
- 김대희, "석탄 보일러에서 회분 부착성향 예측 접근 방법에 대한 고찰", 한국연소학회지, 22(4), pp.27~34 (2017), 한국연소학회[DOI]
- 정광후, "고온의 대기 및 SO2 가스환경 하에서 AISI 304강의 산화 및 부식 특성", 한국마린엔지니어링학회지, 42(7), pp.554~559 (2018), 한국마린엔지니어링학회[DOI]
- S. Lee, "A study on characteristics of HRSG boiler inner tube scale", Corrosion Science and Technology, 11, pp.82~ (2012)
- M. C. Fatah, "Failure Investigation of Fire-Side Water-Wall Tube Boiler", CORROSION SCIENCE AND TECHNOLOGY, 20(5), pp.242~248 (2021), 한국부식방식학회[DOI]
- Luciana Lisi, "Poisoning of SCR Catalysts by Alkali and Alkaline Earth Metals", Catalysts, 10(12), pp.1475~ (2020), MDPI AG[DOI]
- Haiping Xiao, "The Effect of K Salts on SO2–SO3 Conversion and Denitration Behavior over V2O5–WO3", TiO2 Catalysts, 2019, pp.23(1), 41~51[DOI]
- Kunling Jiao, "Status and development for detection and control of ammonium bisulfate as a by-product of SCR denitrification", Scientific Reports, 11(1), pp.10457~ (2021), Springer Science and Business Media LLC[DOI]
- 김성종, "650°C 의 SO2 가스 환경 하에서 T22와 T92 강의 고온 부식특성", CORROSION SCIENCE AND TECHNOLOGY, 18(6), pp.285~291 (2019), 한국부식방식학회[DOI]