산성비 환경을 모사한 수용액에서 염화물 농도에 따른 전기자동차 배터리 하우징용 재료의 전기화학적 특성 연구
Investigation on Electrochemical Characteristics of Battery Housing Material for Electric Vehicles in Solution Simulating an Acid Rain Environment with Chloride Concentrations
0
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
Electrochemical characteristics and damage behavior of 6061-T6 aluminum alloy used as a battery housing material for electric vehicles were investigated in solution simulating the acid rain environment with chloride concentrations. Potentiodynamic polarization test was performed to analyze electrochemical characteristics. Damage behavior was analyzed through Tafel analysis, measurement of damage area, weight loss, and surface observation. Results described that corrosion current density was increased rapidly when chloride concentration excceded 600 PPM, and it was increased about 7.7 times in the case of 1000 PPM compared with 0 PPM. Potentiodynamic polarization experiment revealed that corrosion damage area and mass loss of specimen increased with chloride concentrations. When chloride concentration was further increased, the corrosion damage area extended to the entire surface. To determine damage tendency of pitting corrosion according to chloride concentration, the ratio of damage depth to width was calculated. It was found that the damage tendency decreased with chloride concentrations. Thus, 6061-T6 aluminum alloy damage becomes larger in the width direction than in the depth direction when a small amount of chloride is contained in an acid rain environment.
Abstract
Electrochemical characteristics and damage behavior of 6061-T6 aluminum alloy used as a battery housing material for electric vehicles were investigated in solution simulating the acid rain environment with chloride concentrations. Potentiodynamic polarization test was performed to analyze electrochemical characteristics. Damage behavior was analyzed through Tafel analysis, measurement of damage area, weight loss, and surface observation. Results described that corrosion current density was increased rapidly when chloride concentration excceded 600 PPM, and it was increased about 7.7 times in the case of 1000 PPM compared with 0 PPM. Potentiodynamic polarization experiment revealed that corrosion damage area and mass loss of specimen increased with chloride concentrations. When chloride concentration was further increased, the corrosion damage area extended to the entire surface. To determine damage tendency of pitting corrosion according to chloride concentration, the ratio of damage depth to width was calculated. It was found that the damage tendency decreased with chloride concentrations. Thus, 6061-T6 aluminum alloy damage becomes larger in the width direction than in the depth direction when a small amount of chloride is contained in an acid rain environment.
참고문헌 (34)
- B. G. Pollet, "Current status of hybrid, battery and fuel cell electric vehicles: From electrochemistry to market prospects", Electrochemica Acta, 84, pp.235~ (2012)[DOI]
- Joachim Baumeister, "Applications of Aluminum Hybrid Foam Sandwiches in Battery Housings for Electric Vehicles", Procedia Materials Science, 4, pp.317~321 (2014), Elsevier BV[DOI]
- Shashank Arora, "Review of mechanical design and strategic placement technique of a robust battery pack for electric vehicles", Renewable and Sustainable Energy Reviews, 60, pp.1319~1331 (2016), Elsevier BV[DOI]
- G. Schuh, "Flexible Production Concept of a Low-Cost Battery Pack Housing for Electric Vehicles", 53rd CIRP Conference on Manufacturing Systems, 93, pp.137~ (2020)
- Achim Kampker, "Battery Pack Housing for Electric Vehicles Made by Laser Beam Welding", ATZ worldwide, 121(6), pp.72~77 (2019), Springer Science and Business Media LLC[DOI]
- F. Fiedler, "Laser Welding Process Development for Jigless Joining of a Low-Cost Battery Pack Housing", 72nd IIW Annual Assembly and International Conference (2019)
- Sungwook Kang, "Welding Deformation Analysis, Using an Inherent Strain Method for Friction Stir Welded Electric Vehicle Aluminum Battery Housing, Considering Productivity", Applied Sciences, 9(18), pp.3848~ (2019), MDPI AG[DOI]
- C. Vargel, "Corrosion of Aluminum", pp.12~ (2004), ELSEVIER
- Athanasios K. Sfikas, "Electrochemical Behavior of Al–Al9Co2 Alloys in Sulfuric Acid", Corrosion and Materials Degradation, 1(2), pp.249~272 (2020), MDPI AG[DOI]
- Sarah L’Haridon-Quaireau, "Effects of temperature and pH on uniform and pitting corrosion of aluminium alloy 6061-T6 and characterisation of the hydroxide layers", Journal of Alloys and Compounds, 833, pp.155146~ (2020), Elsevier BV[DOI]
- Z. Qin, "Effect of Surface State on Acid Rain Corrosion Resistance of T6 6005A Aluminum Alloy by BT-FSW Joint", IOP Conference Series : Materials Science and Engineering, 727, pp.012003~ (2020)
- X. K. Yang, "Properties degradation and atmospheric corrosion mechanism of 6061 aluminum alloy in industrial and marine atmosphere environments", Materials and Corrosion, 68(5), pp.529~535 (2016), Wiley[DOI]
- I-Wen Huang, "Dependence on Temperature, pH, and Cl− in the Uniform Corrosion of Aluminum Alloys 2024-T3, 6061-T6, and 7075-T6", Electrochimica Acta, 199, pp.242~253 (2016), Elsevier BV[DOI]
- B. Zaid, "Effects of pH and chloride concentration on pitting corrosion of AA6061 aluminum alloy", Corrosion Science, 50, pp.1814~ (2008)[DOI]
- Xiaoyun Zhang, "Atmospheric Corrosion of 7B04 Aluminum Alloy in Marine Environments", CORROSION SCIENCE AND TECHNOLOGY, 17(1), pp.6~11 (2018), 한국부식방식학회[DOI]
- 김성진, "해양환경용 알루미늄 합금 재료의 전기화학적 부식 손상 특성", 한국표면공학회지, 51(6), pp.421~429 (2018), 한국표면공학회[DOI]
- "ASTM G46-94, Standard practice for calculation of corrosion rates and related information from electrochemical measurements", ASTM International, 3~
- J. H. Kim, "Acid Rain", pp.47~ (2007), SNU Press
- A.U. Malik, "The influence of pH and chloride concentration on the corrosion behaviour of AISI 316L steel in aqueous solutions", Corrosion Science, 33(11), pp.1809~1827 (1992), Elsevier BV[DOI]
- X Zhang, "The pitting behavior of Al-3103 implanted with molybdenum", Corrosion Science, 43(1), pp.85~97 (2001), Elsevier BV[DOI]
- S. Ono, "Crystallographic Pit Growth on Aluminum (100)", Journal of The Electrochemical Society, 152(2), pp.B39~ (2005), The Electrochemical Society[DOI]
- Y. J. Yang, "Electrochemical characteristics of aluminum alloys in sea water for marine environement", Acta Physica Polonica A, 135, pp.1005~ (2019)
- Paulina Arellanes-Lozada, "The Inhibition of Aluminum Corrosion in Sulfuric Acid by Poly(1-vinyl-3-alkyl-imidazolium Hexafluorophosphate)", Materials, 7(8), pp.5711~5734 (2014), MDPI AG[DOI]
- M. Curioni, "The Mechanism of Hydrogen Evolution During Anodic Polarization of Aluminium", Electrochimica Acta, 180, pp.712~721 (2015), Elsevier BV[DOI]
- Athanasios K. Sfikas, "Electrochemical Behavior of Al–Al9Co2 Alloys in Sulfuric Acid", Corrosion and Materials Degradation, 1(2), pp.249~272 (2020), MDPI AG[DOI]
- M. A. Arshadi, "The influence of an isobutane-SO2 pollutant system on the earlier stages of the atmospheric corrosion of metals", Corrosion Science, 23, pp.763~ (1983)[DOI]
- T. E. Graedel, "Corrosion Mechanisms for Aluminum Exposed to the Atmosphere", Journal of The Electrochemical Society, 136(4), pp.204C~212C (1989), The Electrochemical Society[DOI]
- Digby D. Macdonald, "The Point Defect Model for the Passive State", Journal of The Electrochemical Society, 139(12), pp.3434~3449 (1992), The Electrochemical Society[DOI]
- T. P. HOAR, "Breakdown of Passivity of Stainless Steel by Halide Ions", Nature, 216(5122), pp.1299~1301 (1967), Springer Science and Business Media LLC[DOI]
- Paulina Arellanes-Lozada, "The Inhibition of Aluminum Corrosion in Sulfuric Acid by Poly(1-vinyl-3-alkyl-imidazolium Hexafluorophosphate)", Materials, 7(8), pp.5711~5734 (2014), MDPI AG[DOI]
- D. A. Jones, "Principles and prevention of corrosion", pp.267~273 (1996), Prentice Hall
- Z Szklarska-Smialowska, "Pitting corrosion of aluminum", Corrosion Science, 41(9), pp.1743~1767 (1999), Elsevier BV[DOI]
- P. Leblanc, "A Study of Corrosion and Pitting Initiation of AA2024-T3 Using Atomic Force Microscopy", Journal of The Electrochemical Society, 149, pp.239~ (2002)
- R. T. Foley, "The localized corrosion of aluminum alloys –A Review", Corrosion, 42, pp.277~ (1986)