Surface microhardness of three thicknesses of mineral trioxide aggregate in different setting conditions
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Objectives: This study aimed to compare the surface microhardness of mineral trioxide aggregate (MTA) samples having different thicknesses and exposed to human blood from one side and with or without a moist cotton pellet on the other side. Materials and Methods: Ninety cylindrical molds with three heights of 2, 4, and 6 mm were fabricated. In group 1 (dry condition), molds with heights of 2, 4, and 6 mm (10 molds of each) were filled with ProRoot MTA (Dentsply Tulsa Dental), and the upper surface of the material was not exposed to any additional moisture. In groups 2 and 3, a distilled water- or phosphate-buffered saline (PBS)-moistened cotton pellet was placed on the upper side of MTA, respectively. The lower side of the molds in all the groups was in contact with human blood-wetted foams. After 4 day, the Vickers microhardness of the upper surface of MTA was measured. Results: In the dry condition, the 4 and 6 mm-thick MTA samples showed significantly lower microhardness than the 2 mm-thick samples (p = 0.003 and p = 0.001, respectively). However, when a distilled water- or PBS-moistened cotton pellet was placed over the MTA, no significant difference was found between the surface microhardness of samples having the abovementioned three thicknesses of the material (p = 0.210 and p = 0.112, respectively). Conclusions: It could be concluded that a moist cotton pellet must be placed over the 4 to 6 mm-thick MTA for better hydration of the material. However, this might not be necessary when 2 mm-thick MTA is used.
Abstract
Objectives: This study aimed to compare the surface microhardness of mineral trioxide aggregate (MTA) samples having different thicknesses and exposed to human blood from one side and with or without a moist cotton pellet on the other side. Materials and Methods: Ninety cylindrical molds with three heights of 2, 4, and 6 mm were fabricated. In group 1 (dry condition), molds with heights of 2, 4, and 6 mm (10 molds of each) were filled with ProRoot MTA (Dentsply Tulsa Dental), and the upper surface of the material was not exposed to any additional moisture. In groups 2 and 3, a distilled water- or phosphate-buffered saline (PBS)-moistened cotton pellet was placed on the upper side of MTA, respectively. The lower side of the molds in all the groups was in contact with human blood-wetted foams. After 4 day, the Vickers microhardness of the upper surface of MTA was measured. Results: In the dry condition, the 4 and 6 mm-thick MTA samples showed significantly lower microhardness than the 2 mm-thick samples (p = 0.003 and p = 0.001, respectively). However, when a distilled water- or PBS-moistened cotton pellet was placed over the MTA, no significant difference was found between the surface microhardness of samples having the abovementioned three thicknesses of the material (p = 0.210 and p = 0.112, respectively). Conclusions: It could be concluded that a moist cotton pellet must be placed over the 4 to 6 mm-thick MTA for better hydration of the material. However, this might not be necessary when 2 mm-thick MTA is used.
참고문헌 (32)
- Torabinejad M, "Clinical applications of mineral trioxide aggregate", J Endod, 25, pp.197~205 (1999)
- Lee SJ, "Sealing ability of a mineral trioxide aggregate for repair of lateral root perforations", J Endod, 19, pp.541~544 (1993)
- Dominguez MS, "Histological and scanning electron microscopy assessment of various vital pulp-therapy materials", J Endod, 29, pp.324~333 (2003)
- de Souza Costa CA, "Cytotoxic effects and pulpal response caused by a mineral trioxide aggregate formulation and calcium hydroxide", Am J Dent, 21, pp.255~261 (2008)
- Camp JH., "Diagnosis dilemmas in vital pulp therapy: treatment for the toothache is changing, especially in young, immature teeth", Pediatr Dent, 30, pp.197~205 (2008)
- Camilleri J, "The constitution of mineral trioxide aggregate", Dent Mater, 21, pp.297~303 (2005)
- Walker MP, "Effect of setting conditions on mineral trioxide aggregate flexural strength", J Endod, 32, pp.334~336 (2006)
- Witherspoon DE, "One-visit apexification: technique for inducing root-end barrier formation in apical closures", Pract Proced Aesthet Dent, 13, pp.455~460 (2001)
- Matt GD, "Comparative study of white and gray mineral trioxide aggregate (MTA) simulating a one- or two-step apical barrier technique", J Endod, 30, pp.876~879 (2004)
- Gancedo-Caravia L, "Influence of humidity and setting time on the push-out strength of mineral trioxide aggregate obturations", J Endod, 32, pp.894~896 (2006)
- Budig CG, "In vitro comparison of the setting of dry ProRoot MTA by moisture absorbed through the root", J Endod, 34, pp.712~714 (2008)
- DeAngelis L, "In vitro assessment of mineral trioxide aggregate setting in the presence of interstitial fluid alone", J Endod, 39, pp.402~405 (2013)
- Eid AA, "Characterization of the mineral trioxide aggregate-resin modified glass ionomer cement interface in different setting conditions", J Endod, 38, pp.1126~1129 (2012)
- Tsujimoto M, "Timing for composite resin placement on mineral trioxide aggregate", J Endod, 39, pp.1167~1170 (2013)
- Sarkar NK, "Physicochemical basis of the biologic properties of mineral trioxide aggregate", J Endod, 31, pp.97~100 (2005)
- Reyes-Carmona JF, "Biomineralization ability and interaction of mineral trioxide aggregate and white portland cement with dentin in a phosphate-containing fluid", J Endod, 35, pp.731~736 (2009)
- Shokouhinejad N, "Gorjestani H, Dummer PM. Bioactivity of EndoSequence root repair material and bioaggregate", Int Endod J, 45, pp.1127~1134 (2012)
- Giuliani V, "The use of MTA in teeth with necrotic pulps and open apices", Dental Traumatol, 18, pp.217~221 (2002)
- Hachmeister DR, "The sealing ability and retention characteristics of mineral trioxide aggregate in a model of apexification", J Endod, 28, pp.386~390 (2002)
- Lee YL, "Effects of physiological environments on the hydration behavior of mineral trioxide aggregate", Biomaterials, 25, pp.787~793 (2004)
- Nekoofar MH, "The effect of condensation pressure on selected physical properties of mineral trioxide aggregate", Int Endod J, 40, pp.453~461 (2007)
- Danesh G, "A comparative study of selected properties of ProRoot mineral trioxide aggregate and two Portland cements", Int Endod J, 39, pp.213~219 (2006)
- Namazikhah MS, "The effect of pH on surface hardness and microstructure of mineral trioxide aggregate", Int Endod J, 41, pp.108~116 (2008)
- Kayahan MB, "Effect of acid-etching procedure on selected physical properties of mineral trioxide aggregate", Int Endod J, 42, pp.1004~1014 (2009)
- Chandler H., "Hardness testing. 2nd ed. Materials Park", pp.1~13 (1999), ASM International
- Nekoofar MH, "An evaluation of the effect of blood and human serum on the surface microhardness and surface microstructure of mineral trioxide aggregate", Int Endod J, 43, pp.849~858 (2010)
- Kaveh Oloomi, "Evaluation of the effect of blood contamination on the compressive strength of MTA modified with hydration accelerators", Restorative Dentistry and Endodontics, 38(3), pp.128~133 (2013), 대한치과보존학회
- Vanderweele RA, "Effect of blood contamination on retention characteristics of MTA when mixed with different liquids", J Endod, 32, pp.421~424 (2006)
- 장석우, "Chemical characteristics of mineral trioxide aggregate and its hydration reaction", Restorative Dentistry and Endodontics, 37(4), pp.188~193 (2012), 대한치과보존학회
- Pelliccioni GA, "Proroot mineral trioxide aggregate cement used as a retrograde filling without addition of water: an in vitro evaluation of its microleakage", J Endod, 33, pp.1082~1085 (2007)
- Tay FR, "Calcium phosphate phase transformation produced by the interaction of the portland cement component of white mineral trioxide aggregate with a phosphate-containing fluid", J Endod, 33, pp.1347~1351 (2007)
- Gandolfi MG, "Apatite formation on bioactive calcium-silicate cements for dentistry affects surface topography and human marrow stromal cells proliferation", Dent Mater, 26, pp.974~992 (2010)