A micro-computed tomographic study using a novel test model to assess the filling ability and volumetric changes of bioceramic root repair materials
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Objectives: New premixed bioceramic root repair materials require moisture for setting. Using micro-computed tomography (micro-CT), this study evaluated the filling ability and volumetric changes of calcium silicate-based repair materials (mineral trioxide aggregate repair high-plasticity [MTA HP] and Bio-C Repair, Angelus), in comparison with a zinc oxide and eugenol-based material (intermediate restorative material [IRM]; Dentsply DeTrey). Materials and Methods: Gypsum models with cavities 3 mm deep and 1 mm in diameter were manufactured and scanned using micro-CT (SkyScan 1272. Bruker). The cavities were filled with the cements and scanned again to evaluate their filling capacity. Another scan was performed after immersing the samples in distilled water for 7 days to assess the volumetric changes of the cements. The statistical significance of differences in the data was evaluated using analysis of variance and the Tukey test with a 5% significance level. Results: Bio-C Repair had a greater filling ability than MTA HP (p < 0.05). IRM was similar to Bio-C and MTA HP (p > 0.05). MTA HP presented the largest volumetric change (p < 0.05), showing more volume loss than Bio-C and IRM, which were similar (p > 0.05). Conclusions: Bio-C Repair is a new endodontic material with excellent filling capacity and low volumetric change. The gypsum model proposed for evaluating filling ability and volumetric changes by micro-CT had appropriate and reproducible results. This model may enhance the physicochemical evaluation of premixed bioceramic materials, which need moisture for setting.
Abstract
Objectives: New premixed bioceramic root repair materials require moisture for setting. Using micro-computed tomography (micro-CT), this study evaluated the filling ability and volumetric changes of calcium silicate-based repair materials (mineral trioxide aggregate repair high-plasticity [MTA HP] and Bio-C Repair, Angelus), in comparison with a zinc oxide and eugenol-based material (intermediate restorative material [IRM]; Dentsply DeTrey). Materials and Methods: Gypsum models with cavities 3 mm deep and 1 mm in diameter were manufactured and scanned using micro-CT (SkyScan 1272. Bruker). The cavities were filled with the cements and scanned again to evaluate their filling capacity. Another scan was performed after immersing the samples in distilled water for 7 days to assess the volumetric changes of the cements. The statistical significance of differences in the data was evaluated using analysis of variance and the Tukey test with a 5% significance level. Results: Bio-C Repair had a greater filling ability than MTA HP (p < 0.05). IRM was similar to Bio-C and MTA HP (p > 0.05). MTA HP presented the largest volumetric change (p < 0.05), showing more volume loss than Bio-C and IRM, which were similar (p > 0.05). Conclusions: Bio-C Repair is a new endodontic material with excellent filling capacity and low volumetric change. The gypsum model proposed for evaluating filling ability and volumetric changes by micro-CT had appropriate and reproducible results. This model may enhance the physicochemical evaluation of premixed bioceramic materials, which need moisture for setting.
참고문헌 (32)
- Torabinejad M, "Mineral trioxide aggregate and other bioactive endodontic cements: an updated overview - part II: other clinical applications and complications", Int Endod J, 51, pp.284~317 (2018)
- Makbule Bilge Akbulut, "The push-out bond strength of BIOfactor mineral trioxide aggregate, a novel root repair material", Restorative Dentistry and Endodontics, 44(1), pp.1~9 (2019), 대한치과보존학회[DOI]
- Prati C, "Calcium silicate bioactive cements: biological perspectives and clinical applications", Dent Mater, 31, pp.351~370 (2015)
- Ferreira CMA, "Physicochemical, cytotoxicity and in vivo biocompatibility of a high-plasticity calcium-silicate based material", Sci Rep, 9, pp.3933~ (2019)
- Jiménez-Sánchez MDC, "MTA HP Repair stimulates in vitro an homogeneous calcium phosphate phase coating deposition", J Clin Exp Dent, 11, pp.e322~e326 (2019)
- Cintra LTA, "Cytotoxicity, biocompatibility, and biomineralization of the new high-plasticity MTA material", J Endod, 43, pp.774~778 (2017)
- Tomás-Catalá CJ, "Comparative analysis of the biological effects of the endodontic bioactive cements MTA-Angelus, MTA Repair HP and NeoMTA Plus on human dental pulp stem cells", Int Endod J, 50(Supplement 2), pp.e63~e72 (2017)
- Benetti F, "Cytotoxicity, biocompatibility and biomineralization of a new ready-for-use Bioceramic Repair material", Braz Dent J, 30, pp.325~332 (2019)
- López-García S, "Biological effects of new hydraulic materials on human periodontal ligament stem cells", J Clin Med, 8, pp.1216~ (2019)
- Biočanin V, "Marginal gaps between 2 calcium silicate and glass ionomer cements and apical root dentin", J Endod, 44, pp.816~821 (2018)
- 장석우, "Chemical characteristics of mineral trioxide aggregate and its hydration reaction", Restorative Dentistry and Endodontics, 37(4), pp.188~193 (2012), 대한치과보존학회[DOI]
- Torres Fernanda Ferrari Esteves, "Micro-computed tomographic evaluation of the flow and filling ability of endodontic materials using different test models", Restorative Dentistry and Endodontics, 45(2), pp.1~9 (2020), 대한치과보존학회[DOI]
- Torres FFE, "Effect of immersion in distilled water or phosphate-buffered saline on the solubility, volumetric change and presence of voids within new calcium silicate-based root canal sealers", Int Endod J, 53, pp.385~391 (2020)
- Zordan-Bronzel CL, "Evaluation of physicochemical properties of a new calcium silicate-based sealer, Bio-C sealer", J Endod, 45, pp.1248~1252 (2019)
- Darvell BW, "“MTA”-an hydraulic silicate cement: review update and setting reaction", Dent Mater, 27, pp.407~422 (2011)
- Silva Almeida LH, "Are premixed calcium silicate-based endodontic sealers comparable to conventional materials? a systematic review of in vitro studies", J Endod, 43, pp.527~535 (2017)
- International Organization for Standardization, "ISO 6876: dental root canal sealing materials", International Organization for Standardization, ~ (2012)
- Torres FFE, "Evaluation of physicochemical properties of root-end filling materials using conventional and micro-CT tests", J Appl Oral Sci, 25, pp.374~380 (2017)
- Guo YJ, "Physical properties and hydration behavior of a fast-setting bioceramic endodontic material", BMC Oral Health, 16, pp.23~ (2016)
- Camilleri J, "Porosity and root dentine to material interface assessment of calcium silicate-based root-end filling materials", Clin Oral Investig, 18, pp.1437~1446 (2014)
- Gandolfi MG, "Calcium silicate and calcium hydroxide materials for pulp capping: biointeractivity, porosity, solubility and bioactivity of current formulations", J Appl Biomater Funct Mater, 13, pp.43~60 (2015)
- Kim S, "Modern endodontic surgery concepts and practice: a review", J Endod, 32, pp.601~623 (2006)
- Torres FF, "Micro-computed tomography high resolution evaluation of dimensional and morphological changes of 3 root-end filling materials in simulated physiological conditions", J Mater Sci Mater Med, 31, pp.14~ (2020)
- Hashem AA, "ProRoot MTA, MTA-Angelus and IRM used to repair large furcation perforations: sealability study", J Endod, 34, pp.59~61 (2008)
- Övsay E, "The repair of furcal perforations in different diameters with Biodentine, MTA, and IRM repair materials: a laboratory study using an E. Faecalis leakage model", BioMed Res Int, 2018, pp.5478796~ (2018)
- Lertmalapong P, "Bacterial leakage and marginal adaptation of various bioceramics as apical plug in open apex model", J Investig Clin Dent, 10, pp.e12371~ (2019)
- Tanomaru-Filho M, "A novel model for evaluating the flow of endodontic materials using micro-computed tomography", J Endod, 43, pp.796~800 (2017)
- Maura Cristiane Gonçales Orçati Dorileo, "Comparative analysis of physicochemical properties of root perforation sealer materials", Restorative Dentistry and Endodontics, 39(3), pp.201~209 (2014), 대한치과보존학회[DOI]
- Elyassi Y, "Characterization of leachates from 6 root canal sealers", J Endod, 45, pp.623~627 (2019)
- 송유석, "In vitro evaluation of a newly produced resin-based endodontic sealer", Restorative Dentistry and Endodontics, 41(3), pp.189~195 (2016), 대한치과보존학회
- Guimarães BM, "Physicochemical properties of calcium silicate-based formulations MTA Repair HP and MTA Vitalcem", J Appl Oral Sci, 26, pp.e2017115~ (2018)
- Singh S, "Solubility of a new calcium silicate-based root-end filling material", J Conserv Dent, 18, pp.149~153 (2015)