Color stability and solubility of Biodentine and NeoPutty in contact with different irrigation solutions
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Objectives This study aimed to evaluate the color stability and solubility of Biodentine and NeoPutty in contact with different irrigation solutions. Materials and Methods Biodentine and NeoPutty were set in cylindrical molds with 7 mm diameter and 1.5 mm high and immersed in distilled water, 17% ethylenediaminetetraacetic acid (EDTA), 2% chlorhexidine (CHX), 9% 1-hydroxyethylidene 1,1-diphosphonate (HEDP), and 5% sodium hypochlorite (NaOCl) solutions for 24 hours. The color change was measured with a spectrophotometer. The solubility values were calculated as the mass loss was expressed as a percentage of the original mass using an analytical balance with 10−4 g accuracy. Data were analyzed with Kruskal-Wallis followed by Mann-Whitney U tests, and 2-way analysis of variance test followed by Bonferroni corrections for pairwise comparisons for solubility and color stability with a 5% significance threshold, respectively. Results Biodentine exhibited higher color changes compared to the NeoPutty contact with all solutions except distilled water (p < 0.05). Both hydraulic cements (HCs) showed higher discoloration values immersion in CHX followed by NaOCl. No statistically significant difference was found between Biodentine and NeoPutty regardless of irrigation solution in terms of solubility (p > 0.05). Solubility values were lower in the distilled water group compared to EDTA and CHX (p < 0.05). Conclusions Tested HCs showed solubility and color changes at various rates. NeoPutty could be an appropriate material in aesthetic areas. The usage of HEDP as an irrigant solution can be considered suitable for various endodontic treatments due to its relatively lower solubility and discoloration values.
Abstract
Objectives This study aimed to evaluate the color stability and solubility of Biodentine and NeoPutty in contact with different irrigation solutions. Materials and Methods Biodentine and NeoPutty were set in cylindrical molds with 7 mm diameter and 1.5 mm high and immersed in distilled water, 17% ethylenediaminetetraacetic acid (EDTA), 2% chlorhexidine (CHX), 9% 1-hydroxyethylidene 1,1-diphosphonate (HEDP), and 5% sodium hypochlorite (NaOCl) solutions for 24 hours. The color change was measured with a spectrophotometer. The solubility values were calculated as the mass loss was expressed as a percentage of the original mass using an analytical balance with 10−4 g accuracy. Data were analyzed with Kruskal-Wallis followed by Mann-Whitney U tests, and 2-way analysis of variance test followed by Bonferroni corrections for pairwise comparisons for solubility and color stability with a 5% significance threshold, respectively. Results Biodentine exhibited higher color changes compared to the NeoPutty contact with all solutions except distilled water (p < 0.05). Both hydraulic cements (HCs) showed higher discoloration values immersion in CHX followed by NaOCl. No statistically significant difference was found between Biodentine and NeoPutty regardless of irrigation solution in terms of solubility (p > 0.05). Solubility values were lower in the distilled water group compared to EDTA and CHX (p < 0.05). Conclusions Tested HCs showed solubility and color changes at various rates. NeoPutty could be an appropriate material in aesthetic areas. The usage of HEDP as an irrigant solution can be considered suitable for various endodontic treatments due to its relatively lower solubility and discoloration values.
참고문헌 (35)
- Mehta DL, "Spectrophotometric analysis of the color stability of white mineral trioxide aggregate in contact with four different irrigating solutions-an in vitro study", J Conserv Dent, 23, pp.377~383 (2020)
- Athanassiadis B, "A critical analysis of research methods and experimental models to study tooth discolouration from endodontic materials", Int Endod J, 55(Supplement 2), pp.370~383 (2022)
- Camilleri J, "Present status and future directions : hydraulic materials for endodontic use", Int Endod J, 55(Supplement 3), pp.710~777 (2022)
- Taha NA, "Coronal discoloration induced by calcium silicate-based cements used in full pulpotomy in mature permanent molars : a randomized clinical trial", Clin Oral Investig, 27, pp.1723~1730 (2023)
- Torabinejad M, "Clinical applications of mineral trioxide aggregate", J Endod, 25, pp.197~205 (1999)
- Parirokh M, "Mineral trioxide aggregate : a comprehensive literature review--part III : clinical applications, drawbacks, and mechanism of action", J Endod, 36, pp.400~413 (2010)
- Taha NA, "Outcome of full pulpotomy using Biodentine in adult patients with symptoms indicative of irreversible pulpitis", Int Endod J, 51, pp.819~828 (2018)
- Ramos JC, "1-Year in vitro evaluation of tooth discoloration induced by 2 calcium silicate-based cements", J Endod, 42, pp.1403~1407 (2016)
- Lozano-Guillén A, "Comparative cytocompatibility of the new calcium silicate-based cement NeoPutty versus NeoMTA Plus and MTA on human dental pulp cells : an in vitro study", Clin Oral Investig, 26, pp.7219~7228 (2022)
- Alqahtani AS, "NeoPUTTY® versus NeoMTA 2® as a pulpotomy medicament for primary molars : a randomized clinical trial", Pediatr Dent, 45, pp.240~244 (2023)
- Sun Q, "Manoeuvrability and biocompatibility of endodontic tricalcium silicate-based putties", J Dent, 104, pp.103530~ (2021)
- Cruz Hondares T, "Antibacterial, biocompatible, and mineralization-inducing properties of calcium silicate-based cements", Int J Paediatr Dent (2024)[DOI]
- Mohammadi Z, "Sodium hypochlorite in endodontics : an update review", Int Dent J, 58, pp.329~341 (2008)
- Sobhnamayan F, "Effect of different irrigation solutions on the colour stability of three calcium silicate-based materials", J Dent Biomater, 4, pp.373~378 (2017)
- Boutsioukis C, "Present status and future directions-irrigants and irrigation methods", Int Endod J, 55(Supplement 3), pp.588~612 (2022)
- Shokouhinejad N, "Effect of irrigation solutions on the coronal discoloration induced by mineral trioxide aggregate cements containing different radiopacifiers", Dent Res J, 17, pp.447~451 (2020)
- Zehnder M, "Chelation in root canal therapy reconsidered", J Endod, 31, pp.817~820 (2005)
- Zollinger A, "Effects of endodontic irrigants on blood and blood-stained dentin", Heliyon, 5, pp.e01794~ (2019)
- Eren SK, "Effect of irrigants on the color stability, solubility, and surface characteristics of calcium-silicate based cements", Restor Dent Endod, 47, pp.e10~ (2022)
- Torabinejad M, "Physical and chemical properties of a new root-end filling material", J Endod, 21, pp.349~353 (1995)
- Rath PP, "The effects of sequential and continuous chelation on dentin", Dent Mater, 36, pp.1655~1665 (2020)
- Vallés M, "Influence of light and oxygen on the color stability of five calcium silicate-based materials", J Endod, 39, pp.525~528 (2013)
- Yang WC, "Tooth discoloration and the effects of internal bleaching on the novel endodontic filling material SavDen® MTA", J Formos Med Assoc, 120, pp.476~482 (2021)
- Ruyter IE, "Color stability of dental composite resin materials for crown and bridge veneers", Dent Mater, 3, pp.246~251 (1987)
- Keskin C, "Color stabilities of calcium silicate-based materials in contact with different irrigation solutions", J Endod, 41, pp.409~411 (2015)
- Carvalho JA, "Spectrophotometric analysis of coronal discoloration in vitro induced by bioceramic cements", Dent J(Basel), 11, pp.180~ (2023)
- Alazrag MA, "Marginal adaptation, solubility and biocompatibility of TheraCal LC compared with MTA-angelus and biodentine as a furcation perforation repair material", BMC Oral Health, 20, pp.298~ (2020)
- Palma PJ, "Six-month color stability assessment of two calcium silicate-based cements used in regenerative endodontic procedures", J Funct Biomater, 10, pp.14~ (2019)
- Guimarães BM, "Color stability, radiopacity, and chemical characteristics of white mineral trioxide aggregate associated with 2 different vehicles in contact with blood", J Endod, 41, pp.947~952 (2015)
- Możyńska J, "Tooth discoloration induced by different calcium silicate-based cements : a systematic review of in vitro studies", J Endod, 43, pp.1593~1601 (2017)
- Türkoğlu Kayaci Ş, "Spectrophotometric analysis of color stability induced by various calcium silicate cements in full pulpotomy of permanent molars : Theracal PT, Biodentine, and ProRoot MTA", J Endod, 50, pp.229~234 (2024)
- Oliveira LV, "Biological parameters, discolouration and radiopacity of calcium silicate-based materials in a simulated model of partial pulpotomy", Int Endod J, 54, pp.2133~2144 (2021)
- Camilleri J, "Methods for testing solubility of hydraulic calcium silicate cements for root-end filling", Sci Rep, 12, pp.7100~ (2022)
- Pushpa S, "Effect of pH on solubility of white mineral trioxide aggregate and Biodentine : an in vitro study", J Dent Res Dent Clin Dent Prospect, 12, pp.201~207 (2018)
- Quintana RM, "Bone tissue reaction, setting time, solubility, and pH of root repair materials", Clin Oral Investig, 23, pp.1359~1366 (2019)