Effects of coloring procedures on zirconia/veneer ceramics bond strength
2
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
PURPOSE. The most common failure seen in restorations with a zirconia core is total or layered delamination of the ceramic veneer. In the present study, the shear bond strengths between veneering ceramics and colored zirconia oxide core materials were evaluated. MATERIALS AND METHODS. Zirconia discs (15 x 12 x 1.6 mm) were divided into 11 groups of 12 discs each. Groups were colored according to the Vita Classic scale: A3, B1, C4, D2, and D4. Each group was treated with the recommended shading time for 3 s, or with prolonged shading for 60 s, except for the control group. Samples were veneered with 3 mm thick and 3.5 mm in diameter translucent ceramic and subjected to shear test in a universal testing machine with a crosshead speed of 1 mm/min. One-way analysis of variance (ANOVA) and Tukey’s HSD tests were used for comparisons of the groups having the same shading times. A paired t-test was used for groups of the same color (3 s/60 s). RESULTS. Among the 11 groups investigated C4 (3 s) had the highest bond strength with a value of 36.40 MPa, while A3 (3 s) showed the lowest bond strength with a value of 29.47 MPa. CONCLUSION. Coloring procedures can affect zirconia/ceramic bond strength. However, the results also showed that bond strengths of all the investigated groups were clinically acceptable.
Abstract
PURPOSE. The most common failure seen in restorations with a zirconia core is total or layered delamination of the ceramic veneer. In the present study, the shear bond strengths between veneering ceramics and colored zirconia oxide core materials were evaluated. MATERIALS AND METHODS. Zirconia discs (15 x 12 x 1.6 mm) were divided into 11 groups of 12 discs each. Groups were colored according to the Vita Classic scale: A3, B1, C4, D2, and D4. Each group was treated with the recommended shading time for 3 s, or with prolonged shading for 60 s, except for the control group. Samples were veneered with 3 mm thick and 3.5 mm in diameter translucent ceramic and subjected to shear test in a universal testing machine with a crosshead speed of 1 mm/min. One-way analysis of variance (ANOVA) and Tukey’s HSD tests were used for comparisons of the groups having the same shading times. A paired t-test was used for groups of the same color (3 s/60 s). RESULTS. Among the 11 groups investigated C4 (3 s) had the highest bond strength with a value of 36.40 MPa, while A3 (3 s) showed the lowest bond strength with a value of 29.47 MPa. CONCLUSION. Coloring procedures can affect zirconia/ceramic bond strength. However, the results also showed that bond strengths of all the investigated groups were clinically acceptable.
참고문헌 (29)
- Sundh A., "Fracture resistance of yttrium oxide partially-stabilized zirconia all-ceramic bridges after veneering and mechanical fatigue testing", Dent Mater, 21, pp.476~482 (2005)
- Vult von Steyern P., "All-ceramic fixed partial dentures designed according to the DC-Zirkon tech nique. A 2-year clinical study", J Oral Rehabil, 32, pp.180~187 (2005)
- Aboushelib MN., "Microtensile bond strength of different components of core veneered all-ceramic restorations", Dent Mater, 21, pp.984~991 (2005)
- Koutayas SO., "Zirconia in dentistry : part 2. Evidence-based clinical breakthrough", Eur J Esthet Dent, 4, pp.348~380 (2009)
- Kim HJ., "Effect of zirconia surface treatments on the shear bond strength of veneering ceramic", JOURNAL OF PROSTHETIC DENTISTRY, 105(5), pp.315~322 (2011), MOSBY-ELSEVIER
- Sundh A., "Fracture resistance of all-ceramic zirconia bridges with differing phase stabilizers and quality of sintering", Dent Mater, 22, pp.778~784 (2006)
- Hjerppe J., "Effect of shading the zirconia framework on biaxial strength and surface microhardness", Acta Odontol Scand, 66, pp.262~267 (2008)
- Deville S., "A critical comparison of methods for the determination of the aging sensitivity in biomedical grade yttria-stabilized zirconia", J Biomed Mater Res B Appl Biomater, 72, pp.239~245 (2005)
- Pittayachawan P., "The biaxial flexural strength and fatigue property of Lava Y-TZP dental ceramic", Dent Mater, 23, pp.1018~1029 (2007)
- Aboushelib MN., "Effect of zirconia type on its bond strength with different veneer ceramics", J Prosthodont, 17, pp.401~408 (2008)
- Ramin Mosharraf, "Influence of surface modification techniques on shear bond strength between different zirconia cores and veneering ceramics", The Journal of Advanced of Prosthodontics, 3(4), pp.221~228 (2011), 대한치과보철학회
- Craig RG., "Dental materials: properties and manipulation", pp.578~580 (2004), Mosby
- Al-Dohan HM., "Shear strength of core-veneer interface in bi-layered ceramics", J Prosthet Dent, 91, pp.349~355 (2004)
- Saito A., "A comparison of bond strength of layered veneering porcelains to zirconia and metal", J Prosthet Dent, 104, pp.247~257 (2010)
- Guess PC., "Shear bond strengths between different zirconia cores and veneering ceramics and their susceptibility to thermocycling", Dent Mater, 24, pp.1556~1567 (2008)
- 최부경, "Shear bond strength of veneering porcelain to zirconia and metal cores", The Journal of Advanced of Prosthodontics, 1(3), pp.129~135 (2009), 대한치과보철학회
- Ishibe M., "Shear bond strengths of pressed and layered veneering ceramics to high-noble alloy and zirconia cores", J Prosthet Dent, 106, pp.29~37 (2011)
- Schweitzer DM., "Comparison of bond strength of a pressed ceramic fused to metal versus feldspathic porcelain fused to metal", J Prosthodont, 14, pp.239~247 (2005)
- Ereifej N., "Experimental and FE shear-bonding strength at core", veneer interfaces in bilayered ceramics, 2011, pp.27, 590~597
- Komine F., "Effect of cooling rate on shear bond strength of veneering porcelain to a zirconia ceramic material", J Oral Sci, 52, pp.647~652 (2010)
- Ozkurt Z., "In vitro evaluation of shear bond strength of veneering ceramics to zirconia", Dent Mater J, 29, pp.138~146 (2010)
- Fischer J., "Effect of zirconia surface treatments on the shear strength of zirconia", veneering ceramic composites, 2008, pp.27, 448~454
- Fischer J., "Impact of thermal misfit on shear strength of veneering ceramic", zirconia composites, 2009, pp.25, 419~423
- Nakamura T., "Tensile bond strength between tooth-colored porcelain and sandblasted zirconia framework", J Prosthodont Res, 53, pp.116~119 (2009)
- Cömlekoğlu ME., "Evaluation of bond strength of various margin ceramics to a zirconia ceramic", J Dent, 36, pp.822~827 (2008)
- Aboushelib MN., "Microtensile bond strength of different components of core veneered all-ceramic restorations. Part II : Zirconia veneering ceramics", Dent Mater, 22, pp.857~863 (2006)
- AAboushelib MN., "Microtensile bond strength of different components of core veneered allceramic restorations. Part 3 : double veneer technique", J Prosthodont, 17, pp.9~13 (2008)
- Aboushelib MN., "Microtensile bond strength and impact energy of fracture of CAD-veneered zirconia restorations", J Prosthodont, 18, pp.211~216 (2009)
- Mecholsky JJ Jr., "Fractography: determining the sites of fracture initiation", Dent Mater, 11, pp.113~116 (1995)