Free Radical 중합에 의한 PEGMA/Na-MMT와 아크릴단량체의 합성 및 물성
Synthesis and Properties of PEGMA/Na-MMT with Acrylic Monomer by Free-Radical Polymerization
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
PEGMA macromer를 Na-MMT에 삽입한 후 MMA 및 MA 단량체와의 공중합을 행하여 PEGMA/(Na-MMT)-co-MMA/MA 나노복합재료를 합성하고 이의 특성결정을 행하였다. 제조된 나노복합재료를 XRD로 관찰한 결과, Na-MMT에 PEGMA를 삽입하였을 경우 Na-MMT 양이 증가함에 따라 Na-MMT의 실리케이트 층간거리는 증가하였다. DSC 측정으로부터 Na-MMT 첨가량이 늘어날수록 Tg는 높아지는 경향을 보였다. TGA 측정을 통하여 PEGMA/(Na-MMT)-co-MMA/MA 나노복합재료는 순수한 PEGMA-co-MMA/MA보다 열안정성이 다소 향상됨을 확인하였다.
Abstract
Na-MMT intercalated with PEGMA macromer was prepared using an EtAc/acetone mixture (1/1 by volume) as a solvent. PEGMA/(Na-MMT)-co-MMA/MA nanocomposites was synthesized by copolymerizing intercalated compound with MMA and MA, and then characterization was performed. The results of X-ray diffraction (XRD) showed that in the case of Na-MMT intercalated with PEGMA macromer the d-spacings of silicate of Na-MMT increased with increasing of Na-MMT loading. As the Na-MMT loading increases Tg showed increasing trend through the DSC measurement. TGA result showed that thermal stability of PEGMA/(Na-MMT)-co-MMA/MA nanocomposites improved a little more than the pure PEGMA-co-MMA/MA.
참고문헌 (18)
- J. L. Hedric, "Polyimides: Material chemistry and characterization", Elsevier Sci., publisher, 61 (1989)
- T. A. Gag, , Polymer, 42, pp.3399~ (2001)
- A. Usuki, , J. Mater. Res., 8, pp.1179~ (1993)
- R. A. Vaia, , Chem. Mater, 6, pp.1017~ (1994)
- P. B. Messersmith, , J. Polym. Sci. Part A: Polym. Chem, 33, pp.1047~ (1995)
- 이양헌, "Nylon 6", Clay Hybrid Nanocomposite 필름의 연신에 따른 구조적 특성, 2004, pp.41(2), 140~150[DOI]
- Y. U. An, , Polymer, 26, pp.381~ (2002)
- J. W. Cho, , Polymer, 42, pp.1083~ (2001)
- Y. Kojima, , J. Appl. Polym. Sci, 49, pp.1259~ (1993)
- K. A. Carrado, , Chem. Mater, 10, pp.1440~ (1998)
- S. J. Park, , J. Colloid Interface Sci, 251, pp.160~ (2002)
- T. J. Pinnavaia, "Polymer-Clay Nanocomposites" (2000), John Wilεy & Sons, Ltd.
- J. H. Shim, , J. of Applied Polym. Sci, 102, pp.4983~ (2007)
- M. Alexandre, , Mater. Sci. Eng. Reports, 28, pp.1~ (2000)
- Y. Kojima, , J. Mater. Res, 8, pp.1185~ (1993)
- H. L. Tyan, , Polymer, 40, pp.4877~ (1999)
- P. Aranda, , Chem. Mater, 4, pp.1395~ (1992)
- J. Wu, , Chem. Mater, 5, pp.835~ (1993)