알루미늄 5182-폴리프로필렌 샌드위치 판재의 상온 및 고온 인장실험에 따른 인장물성의 변화
Tensile Properties Variation of AA5182/Polypropylene/AA5182 Sandwich Panels Following as Room and Elevated Temperature Tensile Tests
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
To fabricate the 5182 aluminum-polymer sandwich panels, the strength of 5182 aluminum panels, which are the skin sheets that constitutes the sandwich composite panels, is changed according to the degree of heat treatment after rolling, and the characteristics of sandwich panel are also changed. In addition, in the stress-strain curves of the sandwich panel, the serration behavior observed in the 5182 aluminum alloy sheet is also observed. This serration behavior causes surface roughness during sheet forming, which is a serious problem in application to automotive body sheet. In this study, the tensile properties of the 5182 aluminum sandwich panels at room and elevated temperature were carefully investigated by tensile test. It can be found that when the aluminum surface sheets having insufficient heat treatment time is applied, the serration behavior does not completely disappear from the temperature of the room temperature to 160℃.
Abstract
To fabricate the 5182 aluminum-polymer sandwich panels, the strength of 5182 aluminum panels, which are the skin sheets that constitutes the sandwich composite panels, is changed according to the degree of heat treatment after rolling, and the characteristics of sandwich panel are also changed. In addition, in the stress-strain curves of the sandwich panel, the serration behavior observed in the 5182 aluminum alloy sheet is also observed. This serration behavior causes surface roughness during sheet forming, which is a serious problem in application to automotive body sheet. In this study, the tensile properties of the 5182 aluminum sandwich panels at room and elevated temperature were carefully investigated by tensile test. It can be found that when the aluminum surface sheets having insufficient heat treatment time is applied, the serration behavior does not completely disappear from the temperature of the room temperature to 160℃.
참고문헌 (7)
- K. S. Shin, "Mechanical Properties of Aluminum", Polypropylene, Metals and Materials, pp.1999, 5(6)[DOI]
- K. J. KIM, "PLASTIC STRAIN RATIOS AND PLANAR ANIOSOTROPY OF AA5182", POLYPROPYLENE, International Journal of Automotive Technology, pp.2005, 6(3)[DOI]
- 김기주, "SERRATION MECHANISM OF AA5182", POLYPROPYLENE, International Journal of Automotive Technology, pp.2006, 7(4)[DOI]
- 김기주, "알루미늄5182", 폴리프로필렌, 한국자동차공학회 논문집, pp.2004, 12(3)[DOI]
- J. M. Robinson, "The Influence of Specimen Geometry on the Portevin-Le Chatelier Effect in an Al-Mg Alloy", Mat. Sci. & Eng., A159, pp.159~165 (1992)
- J. M. Robinson, "Observations on Deformation Characteristics and Microstructure in an Al-Mg Alloy during Serrated Flow", Mat. Sci. &Eng, A174, pp.1~7 (1994)
- G. Han, "Effect of the Factors on the Formation of Lüders Line in Al-Mg Alloys", J. of the Korean Inst. of Met. & Mater, 34(4), pp.470~477 (1996)