STS316L 배관 레이저 원주용접 조건 선정을 위한 기계적 특성평가
Mechanical Property Evaluation for Determination of Laser Circumferential Welding Condition of STS316L Pipe
3
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The penetration depth, bead height, width, and internal porosity were analyzed to select the perfect penetration conditions for the STS316L tube material with an outer diameter of 38.1mm and a thickness of 3.4 mm. The welding conditions to secure a penetration depth of 3.4mm or more were selected. In addition, a welding range in which underfill does not occur was selected. The range of the selected conditions is the condition of a welding speed of 0.75 to 1.25m/min with an output of 2.0kW. The selected welding conditions were applied to STS316L tube orbital welding, and as a result of cross-sectional inspection after welding, a welded part of less than 4% of complete penetration and porosity was secured. The strength of the weld was measured to be more than 800kgf, and the hardness of the weld was found to decrease compared to the base material. The decrease in the hardness of the weld is judged by the annealing effect of the heat treated base material.
Abstract
The penetration depth, bead height, width, and internal porosity were analyzed to select the perfect penetration conditions for the STS316L tube material with an outer diameter of 38.1mm and a thickness of 3.4 mm. The welding conditions to secure a penetration depth of 3.4mm or more were selected. In addition, a welding range in which underfill does not occur was selected. The range of the selected conditions is the condition of a welding speed of 0.75 to 1.25m/min with an output of 2.0kW. The selected welding conditions were applied to STS316L tube orbital welding, and as a result of cross-sectional inspection after welding, a welded part of less than 4% of complete penetration and porosity was secured. The strength of the weld was measured to be more than 800kgf, and the hardness of the weld was found to decrease compared to the base material. The decrease in the hardness of the weld is judged by the annealing effect of the heat treated base material.
참고문헌 (10)
- B.K. Ann, "Eco-friendly hydrogen fuel cell vehicle development trend", Journal of the KSME, 52(2), pp.34~38 (2012)
- 김종도, "스테인리스강 배관의 효율적인 접합을 위한 용접 시스템에 대한 연구(Ⅱ) - 맞대기 용접 조건의 최적화 -", 한국마린엔지니어링학회지, 41(9), pp.825~830 (2017), 한국마린엔지니어링학회[DOI]
- H.W. Lee, "A Study on Low Temperature Strength and Fatigue Strength of Austenitic Stainless Steel for Membrane Type LNG Tank", The Korean Welding & Joining Society, 17(3), pp.50~54 (1999)
- 김영균, "9% 니켈강 후판 용접부의 강도 및 잔류응력", 동력시스템공학회지, 18(4), pp.85~90 (2014), 한국동력기계공학회
- 표창민, "선박 극저온 탱크용 고망간강 소재 맞대기 용접부 기계 물성 분석 연구", 한국기계기술학회지, 22(6), pp.1123~1128 (2020), 한국기계기술학회[DOI]
- 정규석, "F316 오스테나이트 스테인리스강의 상변태 및 입계부식저항성에 미치는 입열의 영향", CORROSION SCIENCE AND TECHNOLOGY, 19(3), pp.146~155 (2020), 한국부식방식학회[DOI]
- 김인주, "GMAW를 이용한 V-그루브 초층용접 공정 최적화에 관한 연구", 한국기계기술학회지, 14(5), pp.25~30 (2012), 한국기계기술학회[DOI]
- Kim J., "Laser Welding of ASTM A553-1 (9% Nickel Steel) (PART II: Comparison of Mechanical Properties with FCAW)", Metals, 10, pp.999~ (2020)
- Schneller W., "Effect of HIP Treatment on Microstructure and Fatigue Strength of Selectively Laser Melted AlSi10Mg", J. Manuf. Mater. Process, 3, pp.16~ (2019)
- Sommer, N., "Laser Welding of Grey Cast Iron with Spheroidal Graphite-Influence of Process Parameters on Crack Formation and Hardness", Metals, 11, pp.532~ (2021)