이종재료 계면균열의 균열진전거동에 관한 연구
A Study on the Crack Propagation Behavior of Interfacial Crack in Bimaterials
2
조회
0
다운로드
6
인용
0
참고문헌
키워드
초록
In this study, the crack initiation and propagation behavior of interfacial crack in bimaterial are discussed. Normal crack opening displacements(NCOD) and stresses are analyzed by finite element method using ANSYS and used for extracting fracture parameters. The energy release rates can not explained the initiation and crack propagation velocity of interfacial crack. Initial velocity of crack propagation is dependent upon the normal and shear stress behind of crack tip. The crack propagation velocity of interfacial crack is very dependent upon the normal and shear stress behind of crack tip. In case of negative shear displacements increase in interfacial crack, initiation delay of crack propagation is dependent upon the negative shear stress ahead of crack tip due to the suppressing of crack opening. In case of positive shear displacements increase in interfacial crack, initiation delay of crack propagation is dependent upon the stress behind of crack tip due to the stress decrease. The fracture toughness increase is due to the initiation delay of crack propagation.
Abstract
In this study, the crack initiation and propagation behavior of interfacial crack in bimaterial are discussed. Normal crack opening displacements(NCOD) and stresses are analyzed by finite element method using ANSYS and used for extracting fracture parameters. The energy release rates can not explained the initiation and crack propagation velocity of interfacial crack. Initial velocity of crack propagation is dependent upon the normal and shear stress behind of crack tip. The crack propagation velocity of interfacial crack is very dependent upon the normal and shear stress behind of crack tip. In case of negative shear displacements increase in interfacial crack, initiation delay of crack propagation is dependent upon the negative shear stress ahead of crack tip due to the suppressing of crack opening. In case of positive shear displacements increase in interfacial crack, initiation delay of crack propagation is dependent upon the stress behind of crack tip due to the stress decrease. The fracture toughness increase is due to the initiation delay of crack propagation.
참고문헌 (15)
- S. Y. Oh, "Impact Damage Behavior in Laminated Brittle Dissimilar Circular Plates in Biaxial Bending Mode", J. Kor. Soc. Mech. Tech, 6(1), pp.87~92 (2004)
- 박성완, "연성접착제를 사용한 접착이음의 강도평가에 대한 해석", 한국기계기술학회지, 11(2), pp.23~32 (2009), 한국기계기술학회
- M. L. Williams, "The Stresses around a Fault or Crack in Dissimilar Media", Bulletin of the Seismological Society of America, 49, pp.199~204 (1959)
- B. M. Malyshev, "The Strength of Adhesive Joints Using the Theory of Cracks", Int. J. Fract. Mech, 1, pp.114~128 (1965)
- H. C. Cao, "An Experimental Study of the Fracture Resistance of Bimaterial Interfaces", Mechanics of Materials, 7, pp.295~304 (1989)
- J. S. Wang, "Experimental Determination of Interfacial Toughness using Brazil-Nut-Sandwich", Acta. Metal., 38, pp.1279~1290 (1990)
- K. M. Liechti, "Biaxial Loading Experiments for Determining Interfacial Fracture Toughness", J. Appl. Mech., 58, pp.680~687 (1991)
- K. M. Liechti, "Asymmetric Shielding in Interfacial Fracture Under In-Plane Shear", J. Appl. Mech, 59, pp.295~304 (1992)
- R. Yuuki, "Mixed Mode Fracture Criteria for an Interface Crack", Eng. Fract. Mech, 47, pp.367~377 (1994)
- Y. S. Chai, "Experimental Analysis of Interfacial Crack(I)-Determination of Specimen Geometry and Development of Biaxial Delamination Tester", J. Kor. Soc. Comp. Mate, 8(1), pp.1~12 (1995)
- B. S. Choi, "Experimental Analysis of Interfacial Crack(II)-Interfacial Delamination Experiments and Effect of Mode Mixity", J. Kor. Soc. Comp. Mate, 9(1), pp.72~84 (1996)
- B. S. Choi, "Interfacial Crack Propagation under Various Mode-Mixes", KSME Int. J, 16(1), pp.39~45 (2002)
- J. R. Rice, "Elastic Fracture Mechanics Concepts for Interfacial Cracks", J. Appl. Mech, 55, pp.98~103 (1988)
- P. G. Charalambides, "A Test Specimen for Determining the Fracture Resistance of Bimaterial Interfaces", J. Appl. Mech, 56, pp.77~82 (1989)
- Swanson Analysis Systems, Inc., "ANSYS User's Manual for Revision 7.0", ~ (2002)