영하온도에서 UP-MMA 폴리머 모르타르의 강도 발현에 미치는 골재 및 양생온도의 영향
Effects of Aggregate and Curing Temperature on Strength Development of UP-MMA based Polymer Mortar under Sub-Zero Temperature
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this paper, the effects of aggregate and curing temperature on strength development characteristics of UP (Unsaturated Polyester)-MMA (Methyl Methacrylate) based polymer mortar under sub-zero temperature are experimentally investigated to provide a criterion for repair and production of precast products. The result showed that the setting time of the binder was 4 minutes at 20 °C whereas 35 minutes at －20 °C. The result also revealed that the compressive, flexural, and splitting tensile strengths of UP-MMA based polymer mortar significantly decreased as the aggregate and curing temperatures decreased. However, sufficient strengths which can be implemented in actual practices – 36.6 MPa of compressive strength, 6.11 MPa of flexural strength, and 5.81 MPa of splitting tensile strength – were obtained even though both aggregate and curing temperatures were －20°C. Strength development of polymer mortar is largely affected by curing temperature rather than aggregate temperature. It was found that the effects of aggregate temperature on strength development become smaller as the curing temperature becomes lower. Also, toughness, a ratio of compressive strength to flexural strength, increased from 3.5 to 5.9 as both aggregate and curing temperatures decreased from 20 °C to －20 °C.
Abstract
In this paper, the effects of aggregate and curing temperature on strength development characteristics of UP (Unsaturated Polyester)-MMA (Methyl Methacrylate) based polymer mortar under sub-zero temperature are experimentally investigated to provide a criterion for repair and production of precast products. The result showed that the setting time of the binder was 4 minutes at 20 °C whereas 35 minutes at －20 °C. The result also revealed that the compressive, flexural, and splitting tensile strengths of UP-MMA based polymer mortar significantly decreased as the aggregate and curing temperatures decreased. However, sufficient strengths which can be implemented in actual practices – 36.6 MPa of compressive strength, 6.11 MPa of flexural strength, and 5.81 MPa of splitting tensile strength – were obtained even though both aggregate and curing temperatures were －20°C. Strength development of polymer mortar is largely affected by curing temperature rather than aggregate temperature. It was found that the effects of aggregate temperature on strength development become smaller as the curing temperature becomes lower. Also, toughness, a ratio of compressive strength to flexural strength, increased from 3.5 to 5.9 as both aggregate and curing temperatures decreased from 20 °C to －20 °C.
참고문헌 (25)
- Ahn, Namshik, "The Effects of Metallic Monomers on The Mechanical Properties of Polymer Concrete Made With Wet Aggregates", Proceedings of the 10th ICPIC, 통권 : 3, pp.1~20 (2001)
- Aitcin, P. C, "Effect of Coarse- Aggregate Characteristics on Mechanical Properties of High-Strength Concrete", ACI Materials Journal, pp.103~107 (1990)
- Chandra, S, "Polymers in Concrete", pp.138~140 (1994), CRC press
- Dattatreya. J. K, "A Comparative Study of Mechanical Properties of Epoxy and Vinyl Ester Concretes", Proceedings of the 5th ASPIC, pp.437~444 (2006)
- Fowler, D. W, "Future Trends in Polymer Concrete", ACI Special Publication, 116, pp.129~143 (1989)
- Galan-Marin, C., "Comparative Studies on The Influence of Moisture in The Polymer Mortar Aggregates", 11th ICPIC, 209~214 (2004)
- Haddad, Mustafa. U, "Factors Affecting the Curing and Strength of Polymer", ACI Journal Proceedings, pp.396~402 (1983)
- 한민철, "우리나라 한중콘크리트 적용기간의 변화", 콘크리트학회 논문집, 17(2), pp.237~245 (2005), 한국콘크리트학회
- Herwarth Kranenberg, "Worldwide Applications of Polymer Concrete", Proceedings of the 6th ICPIC, pp.60~64 (1990)
- Hwang, K. R., "Effects of styrene Monomer Content on The Strength Properties of Polyester Resin Concrete", Proceedings of the Korea Architectural Insititute, pp.699~702 (1994)
- Inoue, S, "Strength Development of Cold Setting Epoxy Resin Mortars", Proceedings of the 1st ICPIC, pp.185~190 (1975)
- Kobayashi, T, "Low-Temperature Curing of PolymethylMethacrylate Polymer Concrete", Transportation Research Record 2003, International Symposium on Mechanical Properties of Special Concrete, pp.15~18 (2003)
- Lei Yongming, "Relationships Between monomer-Unsaturated Polyester Ratio and The Properties of Polyester Resin Mortars", Proceedings of the 6th ICPIC, pp.120~124 (1990)
- Mantrala, Syam K, "Nondestructive Evaluation of Polyester Polymer Concrete", ACI Materials Journal, pp.660~668 (1995)
- Maximov, Yu. V, "Polymer Concretes on Methylmethacrylate Base Hardened Under Sub-Zero Temperatures", Proceedings of the 9th ICPIC, pp.589~592 (1998)
- Metin Husem, "The Effect of Low Temperature Curing on the Compressive Strength of Ordinary and High Performance Concrete", Construction and Building Materials, 19, pp.49~53 (2005)
- Mu Shuhe, "Low Temperature (－10 ℃) Hardenable Epoxy Resin Mortar Adhesive", Proceedings of the 6th ICPIC, pp.569~575 (1990)
- Ohama, Y., "Determination Methods for working Life of Polyester Resin Concrete", ACI Special Publication, pp.31~40 (1978)
- Okada, K, "Thermo-Dependent Properties of Polyester Resin Concrete", Proceedings of the 1st ICPIC, pp.210~215 (1975)
- Ozkul, M. H, "Effect of Aggregate on The Properties of Epoxy Concrete", Proceedings of the 8th ICPIC, pp.193~198 (1995)
- Serdar Aydin, "Effect of Aggregate Type on Mechanical Properties of Reactive Powder Concrete", ACI Materials Journal, pp.441~449 (2010)
- Vipulanandan, "Performance of Epoxy and Polyester Polymer Concrete", ACI Materials Journal, pp.241~251 (1990)
- Yeon, K. S, "Effects of Curing Temperature on Early Strength of Polymer Concrete", Proceedings of the Korea concrete Insititute, pp.151~165 (1990)
- Yeon, K. S, "Flexural Behavior of Methyl Methacrylate Modified Unsaturated Polyester Polymer Concrete Beams Reinforced with Glass-Fiber-Reinforced Polymer Sheets", Journal of Applied Polymer Science, 119(6), pp.3297~3304 (2011)
- Zhong Shi-Yun, "Compressive", Flexural Strength Ratio of Latex Modified Mortar with Mineral Admixture, 2006, 315~322