황산염에 노출된 구조용 합성섬유와 라텍스 개질 시멘트 모르타르의 부착특성에 미치는 광물질 혼화재의 효과
Effect of Mineral Admixture on Bond between Structural Synthetic Fiber and Latex Modified Cement Mortar under Sulfate Environments
2
조회
0
다운로드
5
인용
0
참고문헌
키워드
초록
It has been well known that concrete structures exposed to acid and sulfate environments such as sewer etc. show significant decrease in their durability due to chemical attack. Such deleterious acid and sulfate attacks lead to expansion and cracking in concrete,and thus, eventually result in damage to cement mortar by forming expansive hydration products due to the reaction between cement hydration products and acid and sulfate ions. In this study, the effect of fly ash and blast furnace slag on the bond performances of structural synthetic fiber in latex modified cement mortar under sulfate environments. Fly ash and blast furnace slag contents ranging from 0 % to 20 % are used in the mix proportions. The latex modified cement mortar specimens were immersed in fresh water, 8 %sodium sulfate (Na2SO4) solutions for 28 and 50 days, respectively. Pullout tests are conducted to measure the bond performance of structural synthetic fiber from latex modified cement mortar after sulfate environments exposure. Test results are found that the incorporation of fly ash and blast furnace slag can effectively enhance the PVA fiber-latex modified cement mortar interfacial bond properties (bond behavior, bond strength and interface toughness) after sulfate environments exposure. The microstructural observation confirms the findings on the interface bond mechanism drawn from the fiber pullout test results under sulfate environments.
Abstract
It has been well known that concrete structures exposed to acid and sulfate environments such as sewer etc. show significant decrease in their durability due to chemical attack. Such deleterious acid and sulfate attacks lead to expansion and cracking in concrete,and thus, eventually result in damage to cement mortar by forming expansive hydration products due to the reaction between cement hydration products and acid and sulfate ions. In this study, the effect of fly ash and blast furnace slag on the bond performances of structural synthetic fiber in latex modified cement mortar under sulfate environments. Fly ash and blast furnace slag contents ranging from 0 % to 20 % are used in the mix proportions. The latex modified cement mortar specimens were immersed in fresh water, 8 %sodium sulfate (Na2SO4) solutions for 28 and 50 days, respectively. Pullout tests are conducted to measure the bond performance of structural synthetic fiber from latex modified cement mortar after sulfate environments exposure. Test results are found that the incorporation of fly ash and blast furnace slag can effectively enhance the PVA fiber-latex modified cement mortar interfacial bond properties (bond behavior, bond strength and interface toughness) after sulfate environments exposure. The microstructural observation confirms the findings on the interface bond mechanism drawn from the fiber pullout test results under sulfate environments.
참고문헌 (16)
- Al-Amoudi, O. S. B., "Sulfate Attack and Reinforcement Corrosion in Plain and Blended Cements Exposed to Sulfate Environments", Building and Environment, 33(1), pp.53~61 (1998)
- 배수호, "콘크리트의 황산 및 황산염 침투 저항성에 미치는 광물질 혼화재의 영향", 콘크리트학회 논문집, 22(2), pp.219~228 (2010), 한국콘크리트학회
- Bentur, A., "Fibre reinforced cementitious composites" (1990), Elsevier Applied Science
- Chan, Y. W., "Effect of silica fume on steel fiber bond characteristics in reactive powder concrete", Cement and Concrete Research, 34(7), pp.1167~1172 (2004)
- Kim, J. H., "Effects of the geometry recycled PET fiber reinforcement on shrinkage of cement-based composites", Composites Part B: Engineering, 39(3), pp.442~450 (2008)
- 이진형, "하이브리드섬유보강 시멘트 복합재료에서 구조용 합성섬유의 인발거동에 미치는 폴리비닐알코올섬유 혼입률의 효과", 콘크리트학회 논문집, 23(4), pp.461~469 (2011), 한국콘크리트학회
- 이진형, "폴리올레핀계 합성 섬유와 시멘트 모르타르와의 부착 특성에 미치는 광물질 혼화재의 효과", 콘크리트학회 논문집, 23(3), pp.339~346 (2011), 한국콘크리트학회
- Mangat, P. S., "Influence of Fly Ash, Silica Fume, and Slag on Sulfate Resistance of Concrete", ACI Materials Journal, 92(5), pp.542~552 (1995)
- Mehta, P. K., "Mechanism of Sulfate of Attack on Portland Cement Concrete-Another Look", Cement and Concrete Research, 13(3), pp.401~406 (1983)
- 박성기, "배합변수에 따른 라텍스 개질 콘크리트 내에 정착된 보강철근의 부식개시시기 예측", 한국농공학회논문집, 50(6), pp.49~60 (2008), 한국농공학회
- 박성기, "라텍스개질 콘크리트의(LMC)의 강도특성 및 배합인자 결정방법", 한국농공학회논문집, 50(5), pp.39~50 (2008), 한국농공학회
- 박성기, "LMC(Latex Modified Concrete)의 염소이온 확산 특성", 한국농공학회논문집, 50(4), pp.27~37 (2008), 한국농공학회
- 박찬기, "폴리올레핀계 구조용 합성섬유보강 콘크리트의 휨성능 및 화재 저항성", 한국농공학회논문집, 50(1), pp.49~60 (2008), 한국농공학회
- Santhanam, M, "Mechanism of Sulfate Attack : A Fresh Look Part 2 : Proposed Mechanisms", Cement and Concrete Research, 33(3), pp.341~346 (2003)
- Shazali, M. A., "Predicting Residual Strength in UnsaturatedConcrete Exposed to Sulfate Attack", Journal of Materialsin Civil Engineering, 18(3), pp.343~354 (2006)
- Wee, T. H., "Sulfate Resistance of Concrete Containing Mineral Admixtures", ACI Materials Journal, 97(5), pp.536~549 (2000)