N2 plasma treatment of pigments with minute particle sizes to improve their dispersion properties in deionized water
0
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
Pigments with minute particle sizes, such as carbon black (CB) and pigment red 48:2 (P.R.48:2), are the most important types of pigment and have been widely used in many industrial applications. However, minute particles have large surface areas, high oil absorption and low surface energy. They therefore tend to be repellent to the vehicle and lose stability, resulting in significant increases in viscosity or reaggregation in the vehicle. Therefore, finding the best way to improve the dispersion properties of minute particle size pigments presents a major technical challenge. In this study, minute particle types of CB and P.R.48:2 were treated with nitrogen gas plasma generated via radio frequency-plasma enhanced chemical vapor deposition (RF-PECVD) to increase the dispersion properties of minute particles in deionized (DI) water. The morphologies and particle sizes of untreated and plasma treated particles were evaluated using scanning electron microscopy (SEM) and atomic force microscopy (AFM). The average distributions of particle size were measured using a laser particle sizer. Fourier transform infrared spectroscopy was carried out on the samples to identify changes in molecular interactions during plasma processing. The results of our analysis indicate that N2 plasma treatment is an effective method for improving the dispersibility of minute particles of pigment in DI water.
Abstract
Pigments with minute particle sizes, such as carbon black (CB) and pigment red 48:2 (P.R.48:2), are the most important types of pigment and have been widely used in many industrial applications. However, minute particles have large surface areas, high oil absorption and low surface energy. They therefore tend to be repellent to the vehicle and lose stability, resulting in significant increases in viscosity or reaggregation in the vehicle. Therefore, finding the best way to improve the dispersion properties of minute particle size pigments presents a major technical challenge. In this study, minute particle types of CB and P.R.48:2 were treated with nitrogen gas plasma generated via radio frequency-plasma enhanced chemical vapor deposition (RF-PECVD) to increase the dispersion properties of minute particles in deionized (DI) water. The morphologies and particle sizes of untreated and plasma treated particles were evaluated using scanning electron microscopy (SEM) and atomic force microscopy (AFM). The average distributions of particle size were measured using a laser particle sizer. Fourier transform infrared spectroscopy was carried out on the samples to identify changes in molecular interactions during plasma processing. The results of our analysis indicate that N2 plasma treatment is an effective method for improving the dispersibility of minute particles of pigment in DI water.
참고문헌 (36)
- W. B. Wiegand, , Ind. Eng. Chem, 26(4), pp.413~419 (1934)
- W. Herbst, "Industrial organic pigments : production, properties, applications" (2004), Wiley-VCH
- J. V. Koleske, "Paint and Coating Testing Manual: 15th. Edition of the Gardner-Sward Handbook" (2012), ASTM International
- J. Bieleman, "Additives for coatings" (2000), Wiley-VCH
- N. Steiert, , Macromol. Mater. Eng., 292(10-11), pp.1111~1125 (2007)
- Y. Zhang, , Macromolecules, 34(20), pp.7056~7065 (2001)
- T. Whelan, "Polymer Technology Dictionary" (1994), Springer Netherlands
- C. Sauter, , Ultrason. Sonochem, 15(4), pp.517~523 (2008)
- H. Barthel, "Organosilicon Chemistry II", pp.761~778 (1995), Wiley-VCH Verlag GmbH
- S. Tsantilis, , Langmuir, 20(14), pp.5933~5939 (2004)
- Wiley, "Processing and Finishing of Polymeric Materials" (2012), John Wiley & Sons
- S. -H. Fu, , J. Dispers. Sci. Technol, 29(1), pp.115~119 (2008)
- K. Oh-Ishi, , Metall. Mater. Trans. A, 35(9), pp.2951~2961 (2004)
- M. Yu, , Electrochem. Commun, 34, pp.312~315 (2013)
- Y. Lin, , Langmuir, 18(16), pp.6147~6158 (2002)
- N. Tsubokawa, , Prog. Polym. Sci, 17(3), pp.417~470 (1992)
- P. E. Fanning, , Carbon N. Y, 31(5), pp.721~730 (1993)
- M. Naitō, "Nanoparticle Technology Handbook" (2018), Elsevier
- A. Liang, , Coatings, 8(1), pp.33~ (2018)
- A. M. Wintermyer, , Public Roads, 28(3), pp.55~ (1954)
- E. M. Liston, , J. Adhes. Sci. Technol, 7(10), pp.1091~1127 (1993)
- S. -J. Park, , Carbon N. Y, 41(7), pp.1437~1442 (2003)
- I. Arčona, , Vacuum, 80(1-3), pp.178~183 (2005)
- C. -W. Kan, , Appl. Sci, 8(4), pp.552~ (2018)
- J. Williams, , J. Mater. Sci, 48(3), pp.1005~1013 (2013)
- S. -J. Park, , J. Colloid Interface Sci, 244(2), pp.336~341 (2001)
- R. C. Chatelier, , Langmuir, 11(7), pp.2585~2591 (1995)
- R. Asmatulu, , J. Mater. Sci. Technol. Res, 2(2), pp.43~51 (2016)
- J. Coates, "Encyclopedia of Analytical Chemistry" (2006), John Wiley & Sons, Ltd
- I. Shimada, , J. Polym. Sci. Part A Polym. Chem, 24(8), pp.1989~1995 (1986)
- J. M. O’Reilly, , Carbon N. Y, 21(1), pp.47~51 (1983)
- K. Fatyeyeva, , RSC Adv, 4(59), pp.31036~31046 (2014)
- R. Newman, , J. Am. Inst. Conserv, 19(1), pp.42~62 (1979)
- F. L. Leite, , Int. J. Mol. Sci, 13(12), pp.12773~12856 (2012)
- I. Yildirim, "Surface Free Energy Characterization of Powders", Virginia Tech, 04-May-2001, ~ (2001)
- Y. Lu, , Int. J. Pharm, 465(1-2), pp.25~31 (2014)