Evaluation of Hardness and Fracture Toughness in a Porcelain Stoneware with Pseudoboehmite Additions
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The effect of pseudoboehmite additions to conventional stoneware porcelain is investigated. Green compacts were formed by slip casting of stabilized aqueous suspensions and then sintering at 1,150℃, 1,200℃ and 1,250℃. The phase evolution was followed by XRD, the densification degree was calculated from densities and the microstructures were studied by SEM. Hardness, H and fracture toughness, KIC were measured by Vicker’s indentation. When vitrification occurs the presence of the pseudoboehmite leads to a extra mullitization, which has two consequences: a volume expansion resulting in a high porosity and a decrease of the amount of liquid which causes problems with the densification, by these facts the pseudoboehmite particles decrease the fracture toughness of the bodies.
Abstract
The effect of pseudoboehmite additions to conventional stoneware porcelain is investigated. Green compacts were formed by slip casting of stabilized aqueous suspensions and then sintering at 1,150℃, 1,200℃ and 1,250℃. The phase evolution was followed by XRD, the densification degree was calculated from densities and the microstructures were studied by SEM. Hardness, H and fracture toughness, KIC were measured by Vicker’s indentation. When vitrification occurs the presence of the pseudoboehmite leads to a extra mullitization, which has two consequences: a volume expansion resulting in a high porosity and a decrease of the amount of liquid which causes problems with the densification, by these facts the pseudoboehmite particles decrease the fracture toughness of the bodies.
참고문헌 (22)
- T. Cavalcante, , Ceram. Int, 30, pp.953~963 (2004)
- Z. Ke, , Am. Ceram. Soc. Bull, 69, pp.380~390 (1990)
- E. De Los Monteros, , Bol. Soc. Esp. Ceram. Vidrio, 30(4), pp.11~17 (1991)
- D. Quinn, , J. Am. Ceram. Soc., 90(3), pp.673~680 (2007)
- R. Lawn, , J. Mater. Sci, 10, pp.1049~1081 (1975)
- R. Lawn, , J. Am. Ceram. Soc, 63, pp.574~581 (1980)
- R. Anstis, , J. Am. Ceram. Soc, 64, pp.533~538 (1981)
- K. Shetty, , J. Am. Ceram. Soc., 68, pp.C282~C284 (1985)
- T. Laugier, , J. Mater. Sci. Lett, 6, pp.355~356 (1987)
- H. Juarez, "IV Congreso lberoamericano de Quimica lnorgarnica", pp.483~489 (1999), Guanajuato
- Phd Report, Universidad Michoacana De San Nicolas De Hidalgo, "O. Aguilar", 35~ (2007)
- J. Blendell, , 박사, pp.1979
- M. Liang, , J. Mater. Sci, 25(12), pp.207~214 (1990)
- J. Lankford, , J. Mater. Sci. Lett, 1(11), pp.493~495 (1982)
- K. Niihara, , J. Mater. Sci. Lett, 2, pp.221~223 (1983)
- C. F. Chan, , Ceram. Int, 20, pp.31~37 (1994)
- B. Saruhan, , J. Mater. Sci., 29, pp.3261~3268 (1994)
- V. Yaroshenko, , J. Am. Ceram. Soc, 84(4), pp.850~858 (2001)
- Y. Iqbal, , J. Am. Ceram. Soc, 80(12), pp.3121~3127 (2000)
- F. Batista, , British Ceramic Transactions, 10(6), pp.256~259 (2001)
- R. Braganca, , Ceram. Int, 29, pp.801~806 (2003)
- W.D. Callister, "Materials Science and Engineering", pp.A7~ (2000), John Wiley & Sons Press