Characterization of 3YSZ/LaPO4 composites coatings made by an atmospheric plasma spraying method
2
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
3YSZ/LaPO4 composites applied for thermal barrier coatings (TBC) were deposited by an atmospheric plasma spraying (APS)method. The residual stresses and thermal conductivity of 3YSZ/LaPO4 composite coating samples were investigated. The thickness of the APS coating layer on the substrate metal was about 115 to 130 μm. Residual stresses of APS coating samples were observed to be both compressive and tensile. Residual stresses of APS coating samples were changed by the amount of LaPO4. As the amount of LaPO4 increased, the compressive residual stresses of APS coating samples were increased. The differences of the residual stress of APS coating samples were increased from 49.44MPa of 3YSZ/10 vol% LaPO4 to 305.9 MPa of 3YSZ/40 vol% LaPO4. The thermal conductivity of the 3YSZ/LaPO4 composite coating layer was calculated by utilizing APS coating layer on the substrate metal. The calculated value of the thermal conductivity of coating layers ranges from 0.11to 0.19 W/m·K.
Abstract
3YSZ/LaPO4 composites applied for thermal barrier coatings (TBC) were deposited by an atmospheric plasma spraying (APS)method. The residual stresses and thermal conductivity of 3YSZ/LaPO4 composite coating samples were investigated. The thickness of the APS coating layer on the substrate metal was about 115 to 130 μm. Residual stresses of APS coating samples were observed to be both compressive and tensile. Residual stresses of APS coating samples were changed by the amount of LaPO4. As the amount of LaPO4 increased, the compressive residual stresses of APS coating samples were increased. The differences of the residual stress of APS coating samples were increased from 49.44MPa of 3YSZ/10 vol% LaPO4 to 305.9 MPa of 3YSZ/40 vol% LaPO4. The thermal conductivity of the 3YSZ/LaPO4 composite coating layer was calculated by utilizing APS coating layer on the substrate metal. The calculated value of the thermal conductivity of coating layers ranges from 0.11to 0.19 W/m·K.
참고문헌 (16)
- X. Cao, , J.Euro.Ceram.Soc, 24, pp.1~10 (2004)
- X. Cao, , Adv.Mater, 15, pp.1438~1442 (2003)
- F. Cernuschi, , J.Therm.Spray Technol, 8, pp.102~109 (1999)
- Advanced Gas Turbine Materials and Coatings, "P.W. Schilke", GE Energy, ~, pp.GER-3569
- Advanced Gas Turbine Materials and Coatings, "P.W. Schilke", GE Energy, ~, pp.GER-3569
- D. Zhu, , Int.J.Appl.Ceram.Technol, 1(1), pp.86~94 (2004)
- D. Zhu, "US Patent US 6812176 B1", ~ (2004)
- D. Zhu, , Ceram.Eng.Sci.Proc, 23, pp.533~546 (2002)
- D. Zhu, "NASA TM-2004-212480", ~ (2004)
- D.R. Clarke, , Materials today, 10, pp.22~29 (2005)
- X. Cao, , J.Am.Ceram.Soc, 84(9), pp.2086~2090 (2001)
- R. Vassen, , Advanced Ceramic Coatings and Interfaces II:Ceramic Engineering and Science Proceedings, 28(3), pp.27~38 (2007)
- C.G.Levi, , Current Opinion in Solid State and Materials Science, 8, pp.77~91 (2004)
- S.H. Kim, , Advanced Ceramic Coatings and Interfaces II:Ceramic Engineering and Science Proceedings, 28(3), pp.19~26 (2007)
- S.H. Kim, , Materials Science Forum, pp.909~912 (2007)
- S.H. Kim, , in submitted