Polyurethane foam was used as a precursor for fabricating SiC-based ceramic foam filters. Two recoating slurry processes were adopted to enhance the strength of ceramic foam. One was the recoating slurry of stoved green body and another was the recoating slurry of pre-sintered green body. The differences in weight increase and thermal shock resistance of ceramic foams fabricated by the two recoating slurry processes were investigated. The effects of pre-sintering temperature on weight increase and thermal shock resistance are discussed. Thermal shock resistance of ceramic foams fabricated by two recoating slurry processes is lower than that by the single coating slurry process. Compared with recoating slurry of pre-sintered green bodies, with the same slurry, the weight increase of ceramic foams fabricated by recoating slurry of the stoved green bodies is less, but the number of thermal cycles to failure is much higher. For ceramic foams fabricated by recoating slurry of presintered green bodies with the same slurry, the weight increase and the number of thermal cycles to failure decreased with the pre-sintering temperature.
Abstract
Polyurethane foam was used as a precursor for fabricating SiC-based ceramic foam filters. Two recoating slurry processes were adopted to enhance the strength of ceramic foam. One was the recoating slurry of stoved green body and another was the recoating slurry of pre-sintered green body. The differences in weight increase and thermal shock resistance of ceramic foams fabricated by the two recoating slurry processes were investigated. The effects of pre-sintering temperature on weight increase and thermal shock resistance are discussed. Thermal shock resistance of ceramic foams fabricated by two recoating slurry processes is lower than that by the single coating slurry process. Compared with recoating slurry of pre-sintered green bodies, with the same slurry, the weight increase of ceramic foams fabricated by recoating slurry of the stoved green bodies is less, but the number of thermal cycles to failure is much higher. For ceramic foams fabricated by recoating slurry of presintered green bodies with the same slurry, the weight increase and the number of thermal cycles to failure decreased with the pre-sintering temperature.
참고문헌 (13)
- U.F. Vogta, , J. Phys. Chem. Solids, 68(5-6), pp.1234~1238 (2007)
- F.Z. Ren, , Mater. Sci. Eng. A, 515(1-2), pp.113~116 (2009)
- Fengzhang Ren, "Microstructure and quality of SiC foam filters for casting", Journal of Ceramic Processing Research, 12(6), pp.691~694 (2011), 세라믹공정연구센터
- X. W. Zhu, , J. Am. Ceram. Soc, 84(7), pp.1654~1656 (2001)
- X. M. Yao, , Ceram. Int, 32(2), pp.137~142 (2006)
- Y. Liu, , J. Chin. Ceram. Soc, 32(2), pp.107~112 (2004)
- U.F. Vogt, , J. Phys. Chem. Sol, 68(5-6), pp.1234~1238 (2007)
- X. P. Pu, , J. Am. Ceram. Soc, 87(7), pp.1392~1394 (2004)
- X.P. Pu, , J. Inorg. Mater, 20(6), pp.1431~1437 (2005)
- J.L. Cheng, , J. Shenyang Univ. Chem. Technol, 24(3), pp.263~266 (2010)
- F.Z. Ren, , J. Henan Univ. Sci. Technol, 33(5), pp.19~22 (2012)
- "ASTM C1424-04 Standard Test Method for Monotonic Compressive Strength of Advanced Ceramics at Ambient Temperature, ASTM Book of Standards Volume 15.01Refractories, Activated Carbon; Advanced Ceramics", 01Refractories, ~ (2004)
- "ASTM C773-88(2006) Standard Test Method for Compressive (Crushing) Strength of Fired Whiteware Materials, ASTM Book of Standards Volume 15.02-Glass;Ceramic Whitewares", ~ (2006)