SiC coating on various nuclear-grade graphite substrates by chemical vapor reaction
1
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
The dependence of high-temperature oxidation and the thermal shock resistance behavior of α-SiC coated nuclear-grade graphite substrates were investigated at elevated temperatures. The surfaces of three kinds of nuclear-grade graphite substrates were coated with α-SiC by chemical vapor reaction (CVR) at a temperature of 1600 o C and a pressure of 1.3 Pa in a pure polysilicon gas atmosphere. Thermal shock and oxidation resistance tests were performed at 1000 o C and 1300 o C respectively, in which the samples were taken out of a box furnace and directly exposed to air at room temperature. It was found that the initial microstructure of the graphite substrates plays an important role in determining the final thermal properties of the α-SiC coatings when using the CVR method.
Abstract
The dependence of high-temperature oxidation and the thermal shock resistance behavior of α-SiC coated nuclear-grade graphite substrates were investigated at elevated temperatures. The surfaces of three kinds of nuclear-grade graphite substrates were coated with α-SiC by chemical vapor reaction (CVR) at a temperature of 1600 o C and a pressure of 1.3 Pa in a pure polysilicon gas atmosphere. Thermal shock and oxidation resistance tests were performed at 1000 o C and 1300 o C respectively, in which the samples were taken out of a box furnace and directly exposed to air at room temperature. It was found that the initial microstructure of the graphite substrates plays an important role in determining the final thermal properties of the α-SiC coatings when using the CVR method.
참고문헌 (12)
- J.R. Strife, , J. Ceram. Bull, 67, pp.369~374 (1988)
- A. Yamaguchi, , Taikabutsu, 35, pp.617~622 (1983)
- Y. -L. Zhang, , Surf. Eng, 28(7), pp.544~547 (2012)
- Q S. Zhu, , J. Nucl. Mater, 254, pp.221~225 (1998)
- B. Schroder, , NEA Workshop on High Temperature Engineering Research Facilities and Experiments (1977), ECN-Pettern
- C. H. Tang, , J. Nucl. Mater, 224, pp.103~108 (1995)
- D.M. Shuford, "U.S. Patent 4471023", ~ (1984)
- O. Yamamoto, , Carbon, 33, pp.359~365 (1995)
- J. -H. Kang, , Progress in Organic Coatings, 61, pp.291~299 (2008)
- Q. Zhu, , Carbon, 37, pp.1475~1484 (1999)
- O. H. Kwon, , J. Euro. Ceram. Soc, 23, pp.3119~3124 (2003)
- X. -Y. Yao, , Corros. Sci, 57, pp.148~153 (2012)