Evaluation of Cu-coated graphite compacts prepared by pulsed current activated sintering process
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Cu-coated graphite powder for weight reduction and a high thermal conductivity was fabricated using a chemical reactionprocess. First, 4 g of graphite powders, which was treated using an activation and wetting process, was added to an aqueoussolution of copper (Cu) sulfate; also, zinc (Zn) powders (such as 35, 40, 45, and 50 wt.%) was added as a transposition solventto the aqueous solution and stirred for 1 hr for a transposition reaction. After the addition of the fabricated powders mixtureto a 75 wt.% DI water: 10 wt.% H3PO4 : 10 wt.% H2SO4 : 5 wt.% mixture, tartaric acid was added to the aqueous solutionto produce a passivating oxide film, followed by a drying for 24 hrs. The particle size of the fabricated powder, which is coarserthan the initial graphite powder, is approximately 3 µm to 4 µm, and the low-intensity oxide peak of the XRD pattern of thefabricated powders is due to the low Zn powder content. With the use of the Cu-coated graphite powder, Cu-coated graphitesintered bodies were fabricated using a pulse current activated sintering (PCAS) process. The Cu-graphite sintered bodieswere sintered with heating rate of 60, 100 and 150 oC/min, respectively. The Cu-coated graphite powders and compacts wereevaluated using FE-SEM, EDS, XRD, a particle analysis, and the Archimedes method.
Abstract
Cu-coated graphite powder for weight reduction and a high thermal conductivity was fabricated using a chemical reactionprocess. First, 4 g of graphite powders, which was treated using an activation and wetting process, was added to an aqueoussolution of copper (Cu) sulfate; also, zinc (Zn) powders (such as 35, 40, 45, and 50 wt.%) was added as a transposition solventto the aqueous solution and stirred for 1 hr for a transposition reaction. After the addition of the fabricated powders mixtureto a 75 wt.% DI water: 10 wt.% H3PO4 : 10 wt.% H2SO4 : 5 wt.% mixture, tartaric acid was added to the aqueous solutionto produce a passivating oxide film, followed by a drying for 24 hrs. The particle size of the fabricated powder, which is coarserthan the initial graphite powder, is approximately 3 µm to 4 µm, and the low-intensity oxide peak of the XRD pattern of thefabricated powders is due to the low Zn powder content. With the use of the Cu-coated graphite powder, Cu-coated graphitesintered bodies were fabricated using a pulse current activated sintering (PCAS) process. The Cu-graphite sintered bodieswere sintered with heating rate of 60, 100 and 150 oC/min, respectively. The Cu-coated graphite powders and compacts wereevaluated using FE-SEM, EDS, XRD, a particle analysis, and the Archimedes method.
참고문헌 (13)
- H. Wang, , Applied Energy, 176, pp.221~232 (2016)
- R. Mahajan, , Intel Technol. J, 6, pp.55~61 (2002)
- M. Hodes, , J. Electron Package, 124, pp.419~426 (2002)
- T.J. Lu, , Int J. Heat Mass Transf, 43, pp.2245~2256 (2000)
- D. Yoo, , IEEE Trans Dev. Mater. Reliab, 4, pp.641~649 (2004)
- R. Kandasamy, , Appl. Therm. Eng, 27, pp.2822~2832 (2007)
- J.H. You, , Nuclear Materials and Energy, 5, pp.7~18 (2015)
- A. Ebrahimi, , Alexandria Engineering Journal, 54, pp.1003~1017 (2015)
- S.B. Yang, , Journal of the Institute of Industrial Technology, 28, pp.95~ (2000)
- F.L. Zhang, , Scripta Mater, 49, pp.1123~1128 (2003)
- A. Morell, , Bull. Am. Ceram. Soc, 59, pp.626~629 (1980)
- K. Jia, , Nanostruct. Mater, 10, pp.875~891 (1998)
- "ISO22007-4:2008 PlasticsDetermination of thermal conductivity and thermal diffusivitysPart 4: Laser flash method-", ~