Feasibility study of inorganic anti-corrosion agents with self-healing capabilities for reinforced concrete structures
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
This study focuses on development of anti-corrosion agent with crack self-healing capabilities for reinforced concretestructures. New inorganic mix-proportions with swelling and expansion properties for crack self-healing capabilities weredesigned to conduct such as paste, mortar and concrete experiments. For the flow tests, W/C ratio of 0.35 was used for thecementitious paste. In case of mortar test, W/C ratio of 0.5 and C/S ratio of 1:3 were used. In case of concrete, mixingproportions of concrete; a W/B ratio of 52% and S/A ratio of 48% were applied to all concretes for the fluidity test,compressive strength, corrosion-ratio of steel bar on the NaCl 6% addition to mix-proportion. EPMA results revealedparticular trends in the chemical composition, such as the formation of calcium alumina silicate materials in cracks. Moreover,Cl ions was decreased from surface to internal area in the concrete by self-healing effects. From these results, it was confirmedthe fluidity, compressive strength, and anti-corrosion effect with self-healing capabilities.
Abstract
This study focuses on development of anti-corrosion agent with crack self-healing capabilities for reinforced concretestructures. New inorganic mix-proportions with swelling and expansion properties for crack self-healing capabilities weredesigned to conduct such as paste, mortar and concrete experiments. For the flow tests, W/C ratio of 0.35 was used for thecementitious paste. In case of mortar test, W/C ratio of 0.5 and C/S ratio of 1:3 were used. In case of concrete, mixingproportions of concrete; a W/B ratio of 52% and S/A ratio of 48% were applied to all concretes for the fluidity test,compressive strength, corrosion-ratio of steel bar on the NaCl 6% addition to mix-proportion. EPMA results revealedparticular trends in the chemical composition, such as the formation of calcium alumina silicate materials in cracks. Moreover,Cl ions was decreased from surface to internal area in the concrete by self-healing effects. From these results, it was confirmedthe fluidity, compressive strength, and anti-corrosion effect with self-healing capabilities.
참고문헌 (20)
- B. Elsener, , Cement and Concrete Composite, 24, pp.65~72 (2002)
- J. M. Gaidis, , Cement and Concrete Composite, 26, pp.181~189 (2004)
- K. Petterson, "Corrosion and Corrosion Protection of Steel in Concrete", pp.461~ (1994), Academic Press
- M. Koichi, , Cement Science and Concrete Technology, 68, pp.218~225 (2014)
- 문병철, "응결시간 조절형 아질산계 방청제 개발과 전기화학적 방식성능 평가에 관한 실험적 연구", 대한건축학회논문집 구조계, 25(01), pp.113~120 (2009), 대한건축학회
- H. Y. Moon, , Korea Concrete Institute, 10(6), pp.325~334 (1998)
- K. B. Shim, , JCPR, 16(1), pp.1~13 (2015)
- T. kishi, , Journal of Advanced Concrete Technology, 8(2), pp.171~186 (2008)
- F. R. Abro, , Materials, 12, pp.1865~ (2019)
- B. Van Belleghem, , Cement and Concrete Research, 113, pp.130~139 (2018)
- Dessi A. Koleva, , Materials, 11, pp.309~ (2018)
- P. Azarsa, , Cement and Concrete Composites, 99, pp.17~31 (2019)
- C. De Nardi, , Materials Structure, 50, pp.191~ (2017)
- B. Park, , Construction Building Materials, 184, pp.1~10 (2018)
- K.J. Shin, , Construction and Building Materials, 151, pp.907~915 (2017)
- H. X. D. Lee, , Cement and Concrete Research, 79, pp.194~208 (2016)
- G. Souradeep, , Journal of Materials in Civil Engineering, 28, pp.04016165~ (2016)
- E. Cuenca, , Construction and Building Materials, 179, pp.619~632 (2018)
- H. Mihashi, , Journal of Advanced Concrete Technology, 10, pp.170~184 (2012)
- S. H. Bae, , KIC, 23(5), pp.815~824 (2008)