Self-healing performance of coated slag aggregates in wheat straw ash blended cement composites
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
The cracks in the concrete structures permit the ingress of harmful ions which ultimately exacerbate the durability of the structures. In addition, the environmental concern of the cement production necessitates the utilization of pozzolanic materials. This study used wheat straw ash as cement replacement material. Sodium silicate impregnated in slag aggregate, an industrial by-product, was used as the self-healing agent. The impregnated slag aggregates were coated and used as a sand replacement. Mortar samples were analyzed for compressive strength. Self-healing performance of the mortar samples was investigated via ultrasonic pulse velocity, water permeability, and dynamic modulus of elasticity tests. The results demonstrate that the addition of coated slag aggregate significantly enhanced the self-healing performance of the mortar samples. Additionally, the incorporation of wheat straw ash resulted in an increased rate of crack filling.
Abstract
The cracks in the concrete structures permit the ingress of harmful ions which ultimately exacerbate the durability of the structures. In addition, the environmental concern of the cement production necessitates the utilization of pozzolanic materials. This study used wheat straw ash as cement replacement material. Sodium silicate impregnated in slag aggregate, an industrial by-product, was used as the self-healing agent. The impregnated slag aggregates were coated and used as a sand replacement. Mortar samples were analyzed for compressive strength. Self-healing performance of the mortar samples was investigated via ultrasonic pulse velocity, water permeability, and dynamic modulus of elasticity tests. The results demonstrate that the addition of coated slag aggregate significantly enhanced the self-healing performance of the mortar samples. Additionally, the incorporation of wheat straw ash resulted in an increased rate of crack filling.
참고문헌 (35)
- K. Van Tittelboom, , Materials, 6(6), pp.2182~2217 (2013)
- C. Ormerod, "Construction Statistics Annual", pp.34~49 (2006), Palgrave Macmillan Press
- M. De Rooij, "Self-Healing Phenomena in Cement-Based Materials: state-of-the-art report of RILEM technical committee 221-SHC: self-Healing phenomena in cement-Based materials", pp.9~ (2013), Springer Press
- H. Huang, , Mater. Des, 92, pp.499~511 (2016)
- V. C. Li, , J. Adv. Concr. Technol, 10(6), pp.207~218 (2012)
- V. Wiktor, , Cem. Concr. Compos, 33(7), pp.763~770 (2011)
- K. Sisomphon, , Heron, 56(1, pp.2) (2011), 13~32
- D.A. Morian, "Use of air-cooled blast furnace slag as coarse aggregate in concrete pavements", pp.1~15 (2012), Federal Highway Administration Press
- D. M. Sadek, , J. Cleaner Prod, 79, pp.134~141 (2014)
- İ. Yüksel, , Build. Environ, 42(7), pp.2651~2659 (2007)
- J. Escalante-Garcia, , Constr. Build. Mater, 23(8), pp.2851~2855 (2009)
- "Self-healing concrete with a microencapsulated healing agent"[URL]
- H. Huang, , International RILEM conference on advances in construction materials through science and engineering, pp.530~536 (2011), RILEM Publications SARL
- E. Mostavi, , J. Mater. Civ. Eng, 27(12), pp.04015035~ (2015)
- R. Alghamri, , Constr. Build. Mater, 124, pp.910~921 (2016)
- A. Qudoos, , Constr. Build. Mater, 193, pp.481~490 (2018)
- ASTM, "ASTM C150", C150M - 17, Standard Specification for Portland Cement, 2017
- Y.-S. Lee, "Study on crack-sealing of cement composite via encapsulating the granulated healing material, Structural engineering", pp.42~46 (2015), Hanyang University Press
- C. ASTM, "109. 2007, Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2 in. or (50-mm) Cube Specimens)", ~ (2007)
- C. ASTM, "348: 02, Standard test method for flexural strength of hydraulic-cement mortars", ~ (2002)
- C. ASTM, "597, Standard test method for pulse velocity through concrete, ASTM International", ~ (2009)
- S.A. Kumar, , Proceedings of the National Seminar on Non-Destructive Evaluation (2006), NDT Press
- T.R. Naik, "Handbook on nondestructive testing of concrete", pp.169~188 (2004), CRC Press
- C. ASTM, "215: 08, Standard Test Method for Fundamental Transverse, Longitudinal, and Torsional Frequencies of Concrete Specimens", ~ (2008)
- Y. -S. Lee, , Materials, 9(7), pp.555~ (2016)
- Y. -S. Lee, , Constr. Build. Mater, 71, pp.188~193 (2014)
- "RILEM II.4, Water Absorption Tube Test", ~ (2006)
- T. -H. Ahn, , Materials, 9(8), pp.654~ (2016)
- H. G. Kim, , Constr. Build. Mater, 188, pp.569~582 (2018)
- C. Edvardsen, , Mater. J, 196(4), pp.448~454 (1999)
- H.F. Taylor, "Cement chemistry", pp.113~125 (1997), Thomas Telford Press
- Ter Heide, Nynke, "Crack healing in hydrating concrete", pp.2005
- E. Gruyaert, , Proceedings of the 2nd International Conference on Microstructural-related Durability of Cementitious Composites, pp.1~8 (2012), RILEM Publications Press
- P. Termkhajornkit, , Cem. Concr. Compos, 31(3), pp.195~203 (2009)
- D. Jaroenratanapirom, , Proceedings of the 6th annual concrete conference, pp.551~556 (2010), University of MN Press