Improved temperature stability of Ba0.5Sr0.5TiO3/ZnAl2O4 ceramics by controlling microstructure with sintering behavior
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
0.2ZnAl2O4/0.8Ba0.5Sr0.5TiO3 ceramics with good dielectric temperature stability were synthesized by controlling sinteringbehavior. The relationship between sintering conditions, microstructure, and dielectric properties of ceramics was studied. Cubic structures were confirmed in all ceramics. Double sintering (DS) behavior can effectively improve the density, and thegrain size has no obvious change compared with non-repeated sintering. The maximum dielectric permittivity (220 at 10 kHz)and minimum leakage current (3.98×10-6 A/cm2 at 0.25 kV/cm) are obtained in the DS ceramics, which is superior to thoseof the single sintering ceramics. This can be ascribed to the higher relative density of the DS ceramics in contrast to the singlesintering ceramics. More importantly, the temperature stability of the DS sample in all samples is optimal due to the highsurface energy at grain boundaries and improved density. This work demonstrates a route to produce ceramics with weaktemperature sensitivity for microwave applications.
Abstract
0.2ZnAl2O4/0.8Ba0.5Sr0.5TiO3 ceramics with good dielectric temperature stability were synthesized by controlling sinteringbehavior. The relationship between sintering conditions, microstructure, and dielectric properties of ceramics was studied. Cubic structures were confirmed in all ceramics. Double sintering (DS) behavior can effectively improve the density, and thegrain size has no obvious change compared with non-repeated sintering. The maximum dielectric permittivity (220 at 10 kHz)and minimum leakage current (3.98×10-6 A/cm2 at 0.25 kV/cm) are obtained in the DS ceramics, which is superior to thoseof the single sintering ceramics. This can be ascribed to the higher relative density of the DS ceramics in contrast to the singlesintering ceramics. More importantly, the temperature stability of the DS sample in all samples is optimal due to the highsurface energy at grain boundaries and improved density. This work demonstrates a route to produce ceramics with weaktemperature sensitivity for microwave applications.
참고문헌 (29)
- Wei Jin, "Effect of LiF addition on the sinterability, crystal structure and microwave dielectric properties of Li3Mg4NbO8 ceramics", Journal of Ceramic Processing Research, 22(6), pp.675~678 (2021), 청정에너지연구소[DOI]
- 윤상옥, "Phase evolution, microstructure, and microwave dielectric properties of Zn2-2xSi1+xO4", Journal of Ceramic Processing Research, 17(10), pp.1024~1027 (2016), 청정에너지연구소[DOI]
- 전은정, "Preparation of silicon oxycarbide amorphous ceramics from polymer precursors and the characterization of their high temperature stability", Journal of Ceramic Processing Research, 13(3), pp.239~242 (2012), 청정에너지연구소[DOI]
- R. -H. Liang, , Mater. Res. Bull, 41(7), pp.1295~1302 (2006)
- L. -B. Kong, , Prog. Mater. Sci, 55(8), pp.840~893 (2010)
- Koppole C. Sekhar, "Thickness-dependent tunable characteristics of (Ba0.5Sr0.5)0.925K0.075TiO3 thin films prepared by pulsed laser deposition", Current Applied Physics, 12(3), pp.654~658 (2012), 한국물리학회[DOI]
- H. Dong, , Mater. Lett, 135, pp.83~86 (2014)
- Xiao-Fei Zhang, "Electrically tunable dielectric properties of Ba0.6Sr0.4TiO3-MgO composite ceramics.", Journal of Ceramic Processing Research, 14(3), pp.430~435 (2013), 청정에너지연구소[DOI]
- J. Zhang, , Ceram. Int, 39(5), pp.5943~5948 (2013)
- R. Liang, , Ceram. Int, 41(1), pp.S551~S556 (2015)
- W. Wang, , J. Alloys Compd, 809, pp.151712~ (2019)
- Yun Sik Park, "Microwave dielectric properties of Mg2Ti1-x(Ni1", 3Sb2, Journal of Ceramic Processing Research, pp.2022, 23(6)[DOI]
- Liqi Cui, Ruifeng Niu, "Effects of sintering temperature on the dielectric and impedance properties of phase-pure titanium dioxide ceramics", Journal of Ceramic Processing Research, 23(1), pp.57~61 (2022), 청정에너지연구소[DOI]
- Dang Anh Tuan, "Dielectric and ferroelectric characteristics of doped BZT-BCT ceramics sintered at low temperature", Journal of Ceramic Processing Research, 19(1), pp.32~36 (2018), 청정에너지연구소[DOI]
- G.G. Yao, "Synthesis and microwave dielectric properties of Li2ZnTi3O8 ceramics by the reaction-sintering process", Journal of Ceramic Processing Research, 16(1), pp.41~44 (2015), 청정에너지연구소[DOI]
- A. Ozdogan, , J. Prosthet. Dent, 125(3), pp.527.e1~527.e7 (2021)
- Minsoo Kim, "Effect of sintering time on reactive templated grain growth and electromechanical properties of NKLNT ceramics", Journal of Ceramic Processing Research, 14(2), pp.260~264 (2013), 청정에너지연구소[DOI]
- X. -W. Ren, , J. Prosthet. Dent, 115(1), pp.109~114 (2016)
- H. -I. Meng, , J. Mech. Behav. Biomed. Mater, 88, pp.362~369 (2018)
- Y. Fang, , J. Eur. Ceram. Soc, 21(5), pp.2745~2750 (2001)
- Y. -X. Wang, , Solid. State. Commun, 135(5), pp.290~293 (2005)
- Y. Bi, , Science, 370(6522), pp.1313~1317 (2020)
- Y. -Z. Xue, , J. Electron. Mater, 48, pp.4806~4817 (2019)
- S. Liu, , Compos. Sci. Technol, 219, pp.109228~ (2022)
- C. Li, , Ceram. Int, 42(9), pp.11453~11458 (2016)
- Y. -G. Wang, , Solid. State. Commun, 92(6), pp.519~523 (1994)
- B. -W. Lee, , J. Ceram. Process. Res, 2(3), pp.134~138 (2001)
- T. Teranishi, , J. Am. Ceram. Soc, 100(3), pp.1037~1043 (2016)
- C. Zhou, , Mater. Chem. Phys, 258, pp.124001~ (2021)