Fabrication of Fe Foam using Slurry Coating Process
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Metal foams have a cellular structure consisting of a solid metal containing a large volume fraction of pores. In particular, open pores which are penetrable pores are necessary for industrial applications such as in high temperature filters and as support for catalysts. In this study, Fe foam with greater than 90% porosity and 2-mm pore size was successfully fabricated using a slurry coating process and the pore properties were characterized. The Fe and Fe2O3 powder mixing ratios were controlled to produce Fe foam samples with different pore sizes and porosity. First, the slurry was prepared through the uniform mixing of powders, distilled water, and polyvinyl alcohol(PVA). The amount of slurry coated with the PU foam increased with increasing Fe2O3 mixing powder ratio, but the shrinkage and porosity of the Fe foams decreased, respectively, with increasing Fe2O3 mixing powder ratio.
Abstract
Metal foams have a cellular structure consisting of a solid metal containing a large volume fraction of pores. In particular, open pores which are penetrable pores are necessary for industrial applications such as in high temperature filters and as support for catalysts. In this study, Fe foam with greater than 90% porosity and 2-mm pore size was successfully fabricated using a slurry coating process and the pore properties were characterized. The Fe and Fe2O3 powder mixing ratios were controlled to produce Fe foam samples with different pore sizes and porosity. First, the slurry was prepared through the uniform mixing of powders, distilled water, and polyvinyl alcohol(PVA). The amount of slurry coated with the PU foam increased with increasing Fe2O3 mixing powder ratio, but the shrinkage and porosity of the Fe foams decreased, respectively, with increasing Fe2O3 mixing powder ratio.
참고문헌 (8)
- J. Banhart, , Prog. Mater. Sci., 46, pp.559~ (2001)
- M. A. Alvin, , Ceram. Bull., 70, pp.1491~ (1991)
- J. H. Choi, , Powder Technol., 140, pp.98~ (2004)
- J. Banhart, , Adv. Eng. Mater., 2, pp.188~ (2000)
- Y. M. Jo, , Powder Technol., 91, pp.55~ (1997)
- C. Y. Zhao, , Mater. Sci. Eng. A., 367, pp.123~ (2004)
- Y. Boonyongmaneerat, , Adv. Eng. Mater., 10, pp.379~ (2008)
- O. Andersen, , Adv. Eng. Mater., 2, pp.192~ (2000)