Bath-type 超音波 洗滌器를 利用한 태양전지모듈 接着劑 EVA(Ethylene Vinyl Acetate) 分解特性

Abstract

Using ultrasonic irradiation, the separation and recovery of PV cell, made of silicon wafer, from PV module was carried out through selective decomposition of EVA used as an interlaminated binder. The ultrasonic cleaner of bath-type (Output: 130 W, Frequency: 40 kHz) was used as an ultrasonic apparatus in this research. With the fixed distance of 2 cm, from ultrasonic generator to PV cell, the experiment of EVA decomposition was performed in various organic solvents such as Toluene, Trichloroethylene, O-dichlorobenzene, Benzene. And also their concentrations and temperature was changed to survey the optimum conditions. However EVA can be decomposed perfectly at 55℃ within 160 min in 5 M of all kinds of solvent, PV cell may be recovered with being damaged or broken severely. This damage may be resulted from the swelling of EVA in the process of decomposition. Whereas, at the condition of 5 M at 65℃, PV cell can be recovered with the state of minor damage or crack. This implies that the decomposition rate of EVA increases with an increase of temperature, thereby EVA can be decomposed before the swelling of EVA layer. Conclusively, it is possible for PV cell to be recovered within 40 min, at 65℃ in 5 M, with less damage.