자외선을 처리한 목재 플라스틱 복합재의 물리 및 역학적 성질 평가
Evaluation on Physical and Mechanical Properties of Wood Plastic Composites Treated under Ultraviolet Irradiation
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this study, we received each wood plastic composites (WPC) from three manufacturers. These WPCs were evaluated regarding their physical and mechanical properties of both before and after accelerated weathering by ultraviolet (UV) irradiation. The total time of exposure of the WPCs to UV irradiation was 1800 h. The water absorption, volumetric swelling and shrinkage of WPCs did not affected by UV irradiation. Among the mechanical properties, there was no significant differences in bending strength and screw withdrawal resistance of UV treated WPCs compared with those of reference WPCs. However, surface hardness of WPCs showed decrease under UV irradiation. Stereoscopic microscopy observation revealed deterioration of the surface layer polymer in all weathered WPCs by UV. Exposure of the WPCs to UV irradiation caused decomposition and disappearance of the polymer layer. From this result, we can estimate that damage of polymer by UV led to a decrease in the surface hardness of the WPCs. The wood flours retained original shape after accelerated weathering by UV irradiation.
Abstract
In this study, we received each wood plastic composites (WPC) from three manufacturers. These WPCs were evaluated regarding their physical and mechanical properties of both before and after accelerated weathering by ultraviolet (UV) irradiation. The total time of exposure of the WPCs to UV irradiation was 1800 h. The water absorption, volumetric swelling and shrinkage of WPCs did not affected by UV irradiation. Among the mechanical properties, there was no significant differences in bending strength and screw withdrawal resistance of UV treated WPCs compared with those of reference WPCs. However, surface hardness of WPCs showed decrease under UV irradiation. Stereoscopic microscopy observation revealed deterioration of the surface layer polymer in all weathered WPCs by UV. Exposure of the WPCs to UV irradiation caused decomposition and disappearance of the polymer layer. From this result, we can estimate that damage of polymer by UV led to a decrease in the surface hardness of the WPCs. The wood flours retained original shape after accelerated weathering by UV irradiation.
참고문헌 (32)
- 강인애, "목분-폴리프로필렌 복합재의 기계적 특성: 목재수종, 충진제 입자크기 및 상용화제의 영향", 목재공학, 37(6), pp.505~516 (2009), 한국목재공학회
- 강인애, "목분-폴리프로필렌 복합재의 수분흡수율 : 목재수종, 충진제 입자크기 및 상용화제의 영향", 목재공학, 38(4), pp.298~305 (2010), 한국목재공학회
- 김범준, "유리섬유가 충전된 공압출 목재⋅플라스틱 복합재의 굽힘 특성에 관한 연구", 한국가구학회지, 24(4), pp.379~388 (2013), 한국가구학회
- 김철현, "폐지 복합재료의 물성", 펄프종이기술, 40(3), pp.48~52 (2008), 한국펄프·종이공학회
- 신백우, "목분-고밀도폴리에틸렌 복합체의 연소성 및 열적특성", 한국화재소방학회 논문지, 26(1), pp.89~95 (2012), 한국화재소방학회
- 이세나, "대나무 분말의 함량 및 입자크기에 따른 바이오복합재의 물성 평가", 목재공학, 37(4), pp.310~319 (2009), 한국목재공학회
- 전상진, "폴리인산염 첨가에 의한 폴리프로필렌 기반의 Wood Plastic Composites 열안정성", 목재공학, 42(6), pp.682~690 (2014), 한국목재공학회
- Adihikary Kamal B., "Dimensional stability and mechanical behaviour of wood-plastic composites based on recycled and virgin high-density polyethylene(HDPE)", Composite Part B : Engineering, 39(5), pp.807~815 (2008)
- Ashori Alireza, "Characteristics of wood-fiber plastic composites made of recycled materials", Waste Management, 29(4), pp.1291~1295 (2009)
- Ayrilmis Nadir, "Potential use of decayed wood in production of wood plastic composite", Industrial Crops and Products, 74(15), pp.279~284 (2015)
- Azuma Y., "Outdoor and accelerated weathering tests for polypropylene and polypropylene", talc composites : A comparative study of their weathering behavior, 2009, pp.94(12), 2267~2274
- Bengtsson Magnus, "Durability and mechanical properties of silane cross-linked wood thermoplastic composites", Composites Science and Technology, 67(15), pp.2728~2738 (2007)
- Benthien Jan T., "Thickness swelling and water absorption of WPC after immersion in cold anc boiling water", Eur. J. Wood Prod, 71, pp.437~442 (2013)
- Butylina Svetiana, "Accelerated weathering of wood-polypropylene composites containing minerals", Applied Science and Manufacturing, 43(11), pp.2087~2094 (2012)
- Fabiyi James S., "Wood plastic composites weathering : Visual appearance and chemical changes", Polymer Degradation and Stability, 93(8), pp.1405~1414 (2008)
- Gozdecki C., "Mechanical properties of woodpolymer composites with different polymers", Ann. WULS-SGGW, Forestry and Wood Technology, 74, pp.82~85 (2011)
- Gwon Jae Gyoung, "Effects of chemical treatments of hybrid fillers on the physical and thermal properties of wood plastic composites", Composites : Part A, 41, pp.1491~1497 (2010)
- H’ng Pak San, "Physical and bending properties of injection moulded wood plastic composites boards", ARPN Journal of Engineering and Applied Sciences, 3(5), pp.13~19 (2008)
- Islam M. N., "Study of water absorption behavior in wood plastic composites by using neutron radiography techniques", Polymer-Plastic Technology and Engineering, 42(5), pp.925~934 (2003)
- Kamdem D. Pascal, "Properties of wood plastic composites made of recycled HDPE and wood flour from CCA-treated wood removed from service", Composites Part A : Applied Sciecne and Manufacturing, 36(3), pp.347~355 (2004)
- Kim Tae-Woo, "Effect of silane coupling on the fundamental properties of wood flour reinforced polypropylene composites", Journal of Composite Materials, 45(15), pp.1595~1605 (2010)
- La Mantia F. P., "Accelerated weathering of polypropylene", wood flour composites, 2008, pp.33(7), 1252~1258
- Lee Chia-Huang, "Effects of polymeric matrix on accelerated UV weathering properties of wood-plastic composites", Holzforschung, 66, pp.981~987 (2012)
- Lei Yong, "Wood plastic composites based on microfibrillar blends of high density polyethylene", poly(ethylene terephthalate), 2010, pp.101(10), 3665~3671
- Li Rongzhi, "Environmental degradation of wood-HDPE composite", Polymer Degradation and Stability, 70(2), pp.135~145 (2000)
- Liu Yang, "Study on the surface properties of wood", polyethylene composites treated under plasma, 2010, pp.257(3), 1112~1118
- Lomeli-Ramirez M. G., "Evaluation of accelerated decay of wood plastic composites by Xylophagus fungi", International Biodeterioration & Biodegradation, 63(8), pp.1030~1035 (2009)
- Mankowski Mark, "Patterns of fungal attack in wood-plastic compisites following exposure in a soil block test", Wood and Fiber Science, 32(3), pp.340~345 (2000)
- Naumann Annette, "Material resistance of weathered wood-plastic composites against fungal decay", International Biodeterioration & Biodegradation, 75, pp.28~35 (2012)
- Stark Nicole M., "Influence of photostabilizers on wood flour-HDPE composites exposed to xenon-arc radiation with and without water spray", Polymer degradation and Stability, 91(12), pp.3048~3056 (2006)
- Wechsler Andrea, "Some of the properties of wood-plastic composites", Building and Environment, 12(7), pp.2637~2644 (2007)
- Yang Te-Hsin, "Characterization of the property changes of extruded wood-plastic composits during yeat roung subtropical weathering", Construction and building Materials, 88(30), pp.159~168 (2015)