중적외선 영역의 DLC 코팅 된 ZnS 기판의 광학 특성
Optical Properties of DLC-coated ZnS Substrates in the Mid-infrared Region
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
ZnS substrates with excellent transmittance in the mid-infrared region (3-5 µm) were prepared using hot pressing instead of conventional chemical vapor deposition (CVD). Diamond-like carbon(DLC) was coated on either one or both sides of the ZnS substrates to improve their mechanical properties and transmittance. More specifically DLC was coated using CVD with an Ar and C2H2 mixed gas, and Ge was used as the bonding layer. During CVD, the bias voltage was fixed to 500 V and analyzed by Fourier transform infrared spectroscopy (FT-IR), nanoindenter, scanning electron microscope and energy dispersive spectrometry. Results of hardness analysis using the nanoindenter, showed that DLC coating increased from 5.9 to 17.7 GPa after deposition. The FT-IR spectroscopy results showed that, in the mid-infrared region (3-5 µm), the average transmittance of the samples with DLC coating on one and both sides increased by approximately 6% and approximately 11.2% respectively. In conclusion, the DLC coating improved the durability and transmittance of the ZnS substrates.
Abstract
ZnS substrates with excellent transmittance in the mid-infrared region (3-5 µm) were prepared using hot pressing instead of conventional chemical vapor deposition (CVD). Diamond-like carbon(DLC) was coated on either one or both sides of the ZnS substrates to improve their mechanical properties and transmittance. More specifically DLC was coated using CVD with an Ar and C2H2 mixed gas, and Ge was used as the bonding layer. During CVD, the bias voltage was fixed to 500 V and analyzed by Fourier transform infrared spectroscopy (FT-IR), nanoindenter, scanning electron microscope and energy dispersive spectrometry. Results of hardness analysis using the nanoindenter, showed that DLC coating increased from 5.9 to 17.7 GPa after deposition. The FT-IR spectroscopy results showed that, in the mid-infrared region (3-5 µm), the average transmittance of the samples with DLC coating on one and both sides increased by approximately 6% and approximately 11.2% respectively. In conclusion, the DLC coating improved the durability and transmittance of the ZnS substrates.
참고문헌 (14)
- Y. Li, "Transparent and luminescent ZnS ceramic consolidated by vacuum hot pressing method", J. Am. Ceram. Soc., 98(10), pp.2872~2975 (2015)
- 여서영, "수열합성 공정 변화에 따른 ZnS 나노분말의 구조 특성과 소결체의 광학적 특성", 전기전자재료학회논문지, 31(6), pp.392~397 (2018), 한국전기전자재료학회[DOI]
- S. Y. Yeo, "Sintering and optical properties of transparent ZnS ceramics by pre-heating treatment temperature", J. Electroceram, 41(1-4), pp.1~8 (2018)
- X. Fang, "ZnS nanostructures : From synthesis to applications", Prog. Mater. Sci., 56(2), pp.175~287 (2011)
- G. F. Zhang, "Optical transmittance of antireflective diamond-like coatings on ZnS substrates", Sur. Coat. Technol., 82(1-2), pp.110~113 (1996)
- Q. He, "Deposition of HfO2 thin films on ZnS substrates", Thin Solid Films, 516(15), pp.4695~4699 (2008)
- C. Hu, "Effects of the chemical bonding on the optical and mechanical properties for germanium carbide films used as antireflection and protection coating of ZnS windows", Condens. Matter., 8(17), pp.4231~4241 (2006)
- C. R. Lin, "Optical propeties of diamond-like carbon films for antireflection coating by RF magnetron sputtering method", Phys. Procedia, 18, pp.46~50 (2011)
- G. F. Zhang, "Studies on diamond like carbon films for antireflection coatings of infrared optical materials", J. Appl. Phys, 76(2), pp.705~707 (1994)
- P. Manivel, "Graphene nanosheets by low-temperature thermal reduction of graphene oxide using RF-CVD", J. Exp. Nanosci, 8(3), pp.1~9 (2012)
- E. Dervishi, "Low-temperature(150oC)carbon nanotube growth on a catalytically active iron oxide-graphene nano-structural system", J. Catal., 299, pp.307~315 (2013)
- M. Gilo, "Low reflectance DLC coatings on various IR substrates", Proc. SPIE, 8353(835320), pp.20~28 (2012)
- R. Zarei Moghadam, "Design and fabrication of multi-layers infrared antirlection coating coasisting of ZnS and Ge on ZnS substrate", Infrared Phy. Technol., 75, pp.18~21 (2016)
- Johannes J. Moes, "Application of process analytical technology in tablet process development using NIR spectroscopy : Blend uniformity, cotent uniformity and coating thickness measurements", Int. J. Pharm., 357(1-2), pp.108~118 (2008)