반경방향의 모서리 균열을 갖고 내면이 경사기능재료(FGM)로 코팅된 두꺼운 실린더의 겉보기 파괴인성해석
Analysis of Apparent Fracture Toughness of a Thick-Walled Cylinder with an FGM Coating at the Inner Surface Containing a Radial Edge Crack
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
This study analyzes the apparent fracture toughness of a thick-walled cylinder with a functionally graded material (FGM) coating at the inner surface of the cylinder. The cylinder is assumed to have a single radial edge crack emanating from its inner surface. The crack surfaces and the inner surface of the cylinder are subjected to an internal pressure. The incompatible eigenstrain developed in the cylinder due to nonuniform coefficient of thermal expansion as a result of cooling from sintering temperature is taken into account. Based on a method of evaluating stress intensity factor introduced in our previous study, an approach is developed to calculate apparent fracture toughness. The approach is demonstrated for a cylinder with a TiC/Al2O3 FGM coating and some numerical results of apparent fracture toughness are presented graphically. The effects of material distribution profile, cylinder wall thickness, application temperature, and coating thickness on the apparent fracture toughness are investigated in details. It is found that all of these factors play an important role in controlling the apparent fracture toughness of the cylinder.
Abstract
This study analyzes the apparent fracture toughness of a thick-walled cylinder with a functionally graded material (FGM) coating at the inner surface of the cylinder. The cylinder is assumed to have a single radial edge crack emanating from its inner surface. The crack surfaces and the inner surface of the cylinder are subjected to an internal pressure. The incompatible eigenstrain developed in the cylinder due to nonuniform coefficient of thermal expansion as a result of cooling from sintering temperature is taken into account. Based on a method of evaluating stress intensity factor introduced in our previous study, an approach is developed to calculate apparent fracture toughness. The approach is demonstrated for a cylinder with a TiC/Al2O3 FGM coating and some numerical results of apparent fracture toughness are presented graphically. The effects of material distribution profile, cylinder wall thickness, application temperature, and coating thickness on the apparent fracture toughness are investigated in details. It is found that all of these factors play an important role in controlling the apparent fracture toughness of the cylinder.
참고문헌 (22)
- Yamanouchi,M, , Proceedings of the First International Symposium on Functionally Gradient Materials (1990)
- Holt, J.B, "Ceramic Transactions: Functionally Gradient Materials, Vol. 34" (1993), The American Ceramic Society
- Ilschner B, , Proceedings of the Third International Symposium on Structural and Functional Gradient Materials (1994), Presses Polytechniques et Universitaires Romands
- Chen Y.F, "The Interface Crack Problem for a Nonhomogeneous Coatings Bonded to a Homogeneous Substrate", Journal of the Mechanics and Physics of Solids, 44, pp.771~787 (1996)
- Gu P, "Cracks in Functionally Graded Materials", International Journal of Solids and Structures, 34, pp.1~17 (1997)
- Ozturk M, "An Axisymmetric Crack in Bonded Materials with a Nonhomogeneous Interfacial Zone under Torsion", ASME Journal of Applied Mechanics, 62, pp.116~125 (1995)
- Ozturk M, "Axisymmetric Crack Problem in Bonded Materials with a Graded Interfacial Region", International Journal of Solidsand Structures, 33, pp.193~219 (1996)
- Choi H.J, "Bonded Dissimilar Strips with a Crack Perpendicular to the Functionally Graded Interface", International Journal of Solids and Structures, 33, pp.4101~4117 (1996)
- Bao G, "Multiple Cracking in Functionally Graded Ceramic", Metal Coatings, 1995, pp.32, 2853~2871
- Hassan H.A.Z, "Torsion of a Nonhomogeneous Infinite Elastic Cylinder Slackened by a Circular Cut", Journal of Engineering Mathematics, 30, pp.547~555 (1996)
- Zuiker J.R, "Functionally Graded Materials: Choice of Micromechanics Model and Limitations in Property Variation", Composites Engineering, 5, pp.807~819 (1995)
- Sekine H, "Composition Profile for Improving the Brittle Fracture Characteristics in Semi-Infinite Functionally Graded Materials", JSME International Journal, Series A, 42, pp.592~600 (1999)
- Afsar A.M, "Crack Spacing Effect on the Brittle Fracture Characteristics of Semi-Infinite Functionally Graded Materials with Periodic Edge Cracks", International Journal of Fracture, 102, pp.L61~L66 (2000)
- Mura T, "Micromechanics of Defects in Solids: Mechanics of Elastic and Inelastic Solids" (1987), Kluwer Academic Publishers
- Afsar A.M, "Optimum Material Distributions for Prescribed Apparent Fracture Toughness in Thick-Walled FGM Circular Pipes", International Journal of Pressure Vessels and Piping, 78, pp.471~484 (2001)
- Afsar A.M, "Inverse Problems of Material Distributions for Prescribed Apparent Fracture Toughness in FGM Coatings Around a Circular Hole in Infinite Elastic Media", Composites Science and Technology, 62, pp.1063~1077 (2002)
- Afsar A.M, "Stress Intensity Factors of Two Diametrically Opposed Edge Cracks in a Thick-Walled Functionally Graded Material Cylinder", Engineering Fracture Mechanics, 74, pp.1617~1636 (2007)
- Afsar A.M, "Inverse Problem of Material Distribution for Desired Fracture Characteristics in a Thick-Walled Functionally Graded Material Cylinder with Two Diametrically-Opposed Edge Cracks", Engineering Fracture Mechanics, 76, pp.845~855 (2009)
- Afsar A.M, "Analysis of Apparent Fracture Toughness of a Thick-Walled FGM Cylinder with Two Diametrically Opposed Edge Cracks", Fracture and Fatigue of Engineering Materials and Structures
- Ceramic Functionally Gradient Materials. Ceramic Transaction: Functionally Gradient Materials Vol. 34, "The Physics of Metal", pp.1993, Nan C.W
- Bowie O.L, "Elastic Analysis for a Radial Crack in a Circular Ring", Engineering Fracture Mechanics, 4, pp.315~321 (1972)
- Nair S.V, "Crack-Wake Debonding and Toughness in Fiber-or Whisker-Reinforced Brittle-Matrix Composites", Journal of American Ceramic Society, 73, pp.2839~2847 (1990)