콘크리트 단면복구용 보수재료의 굵은 골재 최대치수 및 조립률에 따른 재료적 특성

Abstract

Re-damage is frequently occurring for various reasons, including material factors, external factors, and factors caused by poor construction in concrete cross-section restoration work, so it is necessary to identify the cause and improve it. Cement-based materials are the most commonly used maintenance materials for concrete structures, and in particular, additional cross-sectional restoration work may be carried out due to re-damage such as cracks and excitement due to dry contraction of the repair material. In this study, a basic study was conducted to identify the characteristics of concrete while diversifying the maximum dimensions and assembly rate of thick aggregates to examine the effects of using thick aggregates in repair materials. As a result, the slump of concrete increased as the maximum size of thick aggregates increased, and the amount of air content was measured 1.88 to 2.35 times higher in the mixing using aggregates with a maximum aggregate size of 5 mm or more compared to the mixing group with a maximum aggregate size of 10 mm or more. It was found that compressive strength was greatly affected by the performance rate of thick aggregates. The compressive strength was measured the highest in the mixture using thick aggregates with the highest performance rate of 20 mm, and the compressive strength of the mixture with the lowest performance rate was more than 45%. As a result of the dry shrinkage measurement, the dry shrinkage was the lowest as the performance rate of the thick aggregate increased according to the change in the maximum dimensions and assembly rate of the thick aggregate, and the lowest performance rate was the largest in the mix. Through this study, it was confirmed that adjusting the particle size by diversifying the maximum dimensions and assembly rate of thick aggregates used in concrete structure repair materials can improve strength and workability and reduce dry shrinkage.