초음파 밀링 공정을 이용한 텅스텐 중합금 나노복합분말의 제조
Synthesis of Tungsten Heavy alloy Nanocomposite Powderby Ultrasonic-milling Process
0
조회
0
다운로드
1
인용
0
참고문헌
초록
Abstract
Ultrasonic-milling of metal oxide nanopowders for the preparation of tungsten heavy alloys was investigated. Milling time was selected as a major process variable. XRD results of metal oxide nanopowders ultrasonic-milled for 50 h and 100 h showed that agglomerate size reduced with increasing milling time and there was no evidence of contamination or change of composition by impurities. It was found that nanocomposite powders reduced at 800℃ in a hydrogen atmosphere showed a chemical composition of 93.1W-4.9Ni-2.0Fe from EDS analysis. Hardness of sintered part using 50 h and 100 h powder samples was 399 Hv and 463 Hv, respectively, which is higher than the that of commercial products (330-340 Hv).
참고문헌 (12)
- S.Eroglu, "J. Mater. Proc. Technol", 103, pp.288~ (2000)
- K.S.Churn, "Powder Metall", 22, pp.175~ (1979)
- K.T.Ramesh, "Metall. Trans. A", 23, pp.2625~ (1992)
- H.S.Song, "J.Mater. Proc. Technol", 63, pp.618~ (1997)
- H.J.Ryu, "Mater. Sci.Eng", A291, pp.91~ (2000)
- C.C.Koch, "Nanostructered Mater", 1, pp.207~ (1992)
- E.S.Yoon, "Ph.D Thesis, Hanyang Univ", ~ (2002)
- P.M.Kanthale, "Ultrasonics Sonochemistry", 12, pp.441~452 (2005)
- T.H.Kim, "Nanostruct.Mater", 9, pp.213~ (1997)
- D.S.Venables, "Thermochim. Acta", 285, pp.361~ (1996)
- A.K.Basu, "J. Mater. Sci", 13, pp.2703~ (1978)
- P.Walkden, "Powder Metall", 28, pp.36~ (1985)