복합고분자용액법에 의한 가시광에 반응하는 TiO₂:Zr,N 광촉매의 제조 및 NO 광분해 특성
Preparation of Visible-light Responsive TiO₂:Zr,N Photocatalysts by Polymer Complex Solution Method and Photo-degradation of NO
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Visible-light responsive TiO₂:Zr, N powders were prepared by polymer complex solution methodand the particle properties were characterized by using transmission electron microscope, BET method, X-ray dif-fractometer and UV-Vis spectrophotometer. The photocatalytic reactivity of the catalysts was also estimated byanalyzing NO degradation. Polyhedral TiO₂ powder having about 20 nm in the average particle diameter was suc-cessfully prepared. The XRD analysis revealed that the as-prepared powder consisted of anatase and rutile phases.The light absorption of the as-prepared TiO₂:Zr, N powder was shifted to the visible light. In addition, the as-pre-2:Zr, N nanoparticles showed the higher photocatalytic activity than the commercial TiO₂ under both UVand visible lights.
Abstract
Visible-light responsive TiO₂:Zr, N powders were prepared by polymer complex solution methodand the particle properties were characterized by using transmission electron microscope, BET method, X-ray dif-fractometer and UV-Vis spectrophotometer. The photocatalytic reactivity of the catalysts was also estimated byanalyzing NO degradation. Polyhedral TiO₂ powder having about 20 nm in the average particle diameter was suc-cessfully prepared. The XRD analysis revealed that the as-prepared powder consisted of anatase and rutile phases.The light absorption of the as-prepared TiO₂:Zr, N powder was shifted to the visible light. In addition, the as-pre-2:Zr, N nanoparticles showed the higher photocatalytic activity than the commercial TiO₂ under both UVand visible lights.
참고문헌 (13)
- M. Kaneko, "Photocatalysis Science and Technology" (2002), Springer-Verlag
- A. Fuerte, , J. Catal, 212, pp.1~9 (2002)
- H. D. Chun, , J. Kor. Soc. Environ. Eng, 16(7), pp.809~818 (1994)
- B. A. Roe, , J. Environ. Sci. Health. B, 32, pp.261~281 (1997)
- X. Fu, , Environ. Sci. Tech, 30, pp.647~653 (1996)
- C. Wu, , J. Mol. Catal. A, 229, pp.233~239 (2005)
- S. Sato, , Chem. Phys. Lett, 123, pp.126~128 (1986)
- T. Ibusuki, , J. Mol. Cat, 88, pp.93~102 (1994)
- Z. Toth, , React. Kinet. Catal. Lett, 56, pp.185~190 (1995)
- Y. Hori, , Chem. Lett, 15, pp.1845~1848 (1986)
- N. Cant, , J. Catal, 134, pp.317~330
- P. Pichat, , Can. J. Chem. Eng, 60, pp.27~32
- J. W. Jang, , J. Korean Power Metall. Inst, 12(4), pp.249~254 (2005)