나노인덴테이션을 이용한 Ti(C0.7N0.3)-NbC-Ni 써멧 구성상의 경도평가
Measurement of Hardness of Constituent Phases in Ti(C0.7N0.3)-NbC-Ni Cermets Using Nanoindentation
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The indentation technique has been one of the most commonly used techniques for the measurement of the mechanical properties of materials due to its experimental ease and speed. Recently, the scope of indentation has been enlarged down to the nanometer range through the development of instrumentations capable of continuously measuring load and displacement. In addition to testing hardness, the elastic modulus of submicron area could be measured from an indentation load-displacement (P-h) curve. In this study, the hardness values of the constituent phases in Ti(C0.7N0.3)-NbC-Ni cermets were evaluated by nanoindentation. SEM observation of the indented surface was indispensable in order to separate the hardness of each constituent phase since the Ti(C0.7N0.3)-based cermets have relatively inhomogeneous microstructure. The measured values of hardness using nanoindentation were ~20 GPa for hard phase and ~10 GPa for binder phase. The effect of NbC addition on hardness was not obvious in this work.
Abstract
The indentation technique has been one of the most commonly used techniques for the measurement of the mechanical properties of materials due to its experimental ease and speed. Recently, the scope of indentation has been enlarged down to the nanometer range through the development of instrumentations capable of continuously measuring load and displacement. In addition to testing hardness, the elastic modulus of submicron area could be measured from an indentation load-displacement (P-h) curve. In this study, the hardness values of the constituent phases in Ti(C0.7N0.3)-NbC-Ni cermets were evaluated by nanoindentation. SEM observation of the indented surface was indispensable in order to separate the hardness of each constituent phase since the Ti(C0.7N0.3)-based cermets have relatively inhomogeneous microstructure. The measured values of hardness using nanoindentation were ~20 GPa for hard phase and ~10 GPa for binder phase. The effect of NbC addition on hardness was not obvious in this work.
참고문헌 (19)
- S. Y. Zhang, , Mater. Sci. & Eng. A, 163, pp.141~ (1993)
- P. Ettmayer, , Int. J. Ref. Met. & Hard Mater, 13, pp.343~ (1995)
- G. E. D'Errico, , J. Mater. Proc. Tech, 77, pp.337~ (1998)
- E. Rudy, , J. Less Com. Met, 33, pp.245~ (1973)
- D. Moskowitz, , Modern Dev. Pow. Met, 3, pp.83~ (1966)
- H. Suzuki, , J. Jap. Inst. Met, 35, pp.245~ (1981)
- L. E. Toth, "Transition Metal Carbides and Nitrides", pp.6~ (1971), Academic Press
- W. Lengauer, , J. Alloys & Comp, 217, pp.137~ (1995)
- M. F. Doerner, , J. Mater. Res, 1, pp.601~ (1986)
- G. M. Pharr, , MRS Bull, 17, pp.28~ (1992)
- W. C. Oliver, , J. Mater. Res, 7, pp.1564~ (1992)
- G. M. Pharr, , Mater. Sci. & Eng. A, 253, pp.151~ (1998)
- M. G. Gee, , Mater. Sci. & Eng. A, 253, pp.128~ (1996)
- S. Guicciardi, , Adv. Eng. Mater, 9, pp.389~ (2007)
- X. Shi, , Mater. Char, 59, pp.374~ (2008)
- F. Qi, , Mater. Sci. & Eng. A, 251, pp.276~ (1998)
- S. Y. Ahn, , J. Am. Ceram. Soc, 84, pp.843~ (2001)
- S. Kim, , J. Am. Ceram. Soc. submitted
- A. Grosjeana, , Surface and Coatings Technology, 137, pp.92~ (2001)