Warm Compaction of Fe-Si/Fe Powder Mixture and its Magnetic Property
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
3-D shape soft magnetic composite parts can be formed by general compaction method of powder metallurgy. In this study, the results on the high density nanostructured Fe-Si/Fe composite prepared by a warm compaction method were presented. Ball-milled Fe-25 wt.%Si powder, pure Fe powder and Si-polymer were mixed and then the powder mixture was compacted at various temperatures and pressures. Pore free density of samples up to 95% theoretical value has been obtained. The warm compacted sample prepared at 650 ㎫ and 240℃ had highest compaction properties in comparison with other compacts prepared at 300, 400 ㎫ and room temperature and 120℃. The magnetic properties such as core loss, magnetization saturation and coercivity were measured by B-H curve analyzer and vibration sample magnetometer.
Abstract
3-D shape soft magnetic composite parts can be formed by general compaction method of powder metallurgy. In this study, the results on the high density nanostructured Fe-Si/Fe composite prepared by a warm compaction method were presented. Ball-milled Fe-25 wt.%Si powder, pure Fe powder and Si-polymer were mixed and then the powder mixture was compacted at various temperatures and pressures. Pore free density of samples up to 95% theoretical value has been obtained. The warm compacted sample prepared at 650 ㎫ and 240℃ had highest compaction properties in comparison with other compacts prepared at 300, 400 ㎫ and room temperature and 120℃. The magnetic properties such as core loss, magnetization saturation and coercivity were measured by B-H curve analyzer and vibration sample magnetometer.
참고문헌 (7)
- B. Zuo, , Materials Science and Engineering A, 371, pp.210~ (2004)
- H. Shokrollahi, , Materials Science and Engineering B, 134, pp.41~ (2006)
- S. H. Kim, , Journal of Alloys and Compounds, 424, pp.204~ (2006)
- I. Chicinas, , Journal of Magnetism and Magnetic Materials, 290, pp.1531~ (2005)
- Y. G. Guo, , Journal of Magnetism and Magnetic Materials, 302, pp.14~ (2006)
- Y. Ozaki, , Kawasaki Steel Technical Report, 47, pp.48~ (2002)
- 김세훈, "온간성형법으로 제조된 Fe 분말 코어의 자성특성", 한국분말야금학회지, 14(5), pp.298~302 (2007), 한국분말야금학회