Fe-Cr-Mo 합금 분말의 성형 및 소결특성에 미치는 입도분포 영향
Influence of Particle Size Distribution on Green and Sintered Properties of Fe-Cr-Mo Prealloy Powder
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
The effect of particle size distribution on green and sintered properties of Fe-Cr-Mo prealloy powder was investigated in this study. For the study, prealloyed Fe-Cr-Mo powders with different particle sizes were mixed as various ratios and cold compacted at various pressure and sintered at 1250oC for 30 min, 90%N2 + 10%H2 atmosphere in the continuous sintering furnace. The results shows that the powders with large particle size distribution have high compressibility and low ejection force. However the green strength are much less than those with small particle size distribution. Tensile prperties of the sintered specimes with large particles size also have high strength and elongation.
Abstract
The effect of particle size distribution on green and sintered properties of Fe-Cr-Mo prealloy powder was investigated in this study. For the study, prealloyed Fe-Cr-Mo powders with different particle sizes were mixed as various ratios and cold compacted at various pressure and sintered at 1250oC for 30 min, 90%N2 + 10%H2 atmosphere in the continuous sintering furnace. The results shows that the powders with large particle size distribution have high compressibility and low ejection force. However the green strength are much less than those with small particle size distribution. Tensile prperties of the sintered specimes with large particles size also have high strength and elongation.
참고문헌 (9)
- R. M. German, "Powder Metallurgy of Iron and Steel", pp.29~ (1997), John Wiley and Sons
- A. D. Romin. Jr., "ASM Handbook Vol. 7 Powder Metal and Technologies and Applications", pp.751~ (1998), ASM International
- I. Jekins., "Powder Metallurgy-an Overview", pp.287~ (1991), The Institute of Metal
- M. W. Wu., , Mater. Sci. Eng. A, 538, pp.135~ (2012)
- L Ciripova., , Mater. Design, 35, pp.619~ (2012)
- M. Azadbed., , Curr. Apli. Phys, 9, pp.777~ (2009)
- K. S. Narasinham, , Mater. Chem. Phys, 67, pp.56~ (2001)
- D. Shamugasundaram., , Mater. Design, 30, pp.3444~ (2009)