단조 산화스케일로부터 철계분말 제조 기술개발 연구
Study on the Reduction of Forging Oxide Scale using Hydrogen
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
The study on the fabrication of iron powder from forging scales using hydrogen gas has been conducted on the effect of hydrogen partial pressure, temperature, and reactive time. The mechanism for the reduction of iron oxides was proposed with various steps, and it was found that reduction pattern might be different depending on temperature. The iron content in the scale and reduction ratio of oxygen were both increased with increasing reactive time at 0.1atm of hydrogen partial pressure. On the other hand, for over 30 minutes at 0.5 atm of hydrogen partial pressure,the values were found to be almost same. In the long run, iron metallic powder was obtained with over 90% of iron content and an average size of its powder was observed to be about 100 μm.
Abstract
The study on the fabrication of iron powder from forging scales using hydrogen gas has been conducted on the effect of hydrogen partial pressure, temperature, and reactive time. The mechanism for the reduction of iron oxides was proposed with various steps, and it was found that reduction pattern might be different depending on temperature. The iron content in the scale and reduction ratio of oxygen were both increased with increasing reactive time at 0.1atm of hydrogen partial pressure. On the other hand, for over 30 minutes at 0.5 atm of hydrogen partial pressure,the values were found to be almost same. In the long run, iron metallic powder was obtained with over 90% of iron content and an average size of its powder was observed to be about 100 μm.
참고문헌 (10)
- D. Wagner., , Sohn International Symposium, San Deigo, pp.111~ (2006)
- H. Rau, , J. Chem. Thermodynamics, 4, pp.57~ (1972)
- O. Kubascheweski., "Thermochemical Data of Alloys" (1956), Pergamon Press
- H. Baolin., , Chin. J. Chem. Eng, 20(1), pp.10~ (2012)
- W. K. Jozwiak., , Appl. Catal. A : Gen, 326, pp.17~ (2007)
- P. G. Coombs., , J. Mater. Sci, 25, pp.343~ (1990)
- M. V. C. Sastri., , Int. J. Hydrogen Energy, 7(12), pp.951~ (1982)
- H. Y. Lin., , Therm. Acta, 400, pp.61~ (2003)
- 이원석, "MoO3", camphene 슬러리의 동결건조 및 수소환원에 의한 Mo 다공체 제조, 2012, pp.19(6), 446~450[DOI]
- D. R. Lide, "Handbook of Chemistry and Physics" (2006), CRC Press