블록형 Ni-Cr-Al 분말 다공성 소재의 미세조직 및 인장 변형 거동
Microstructure and Tensile Deformation Behavior of Ni-Cr-Al Powder Porous Block Material
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
This study investigated the microstructure and tensile properties of a recently made block-type Ni-Cr-Al powder porous material. The block-type powder porous material was made by stacking multiple layers of powder porous thin plates with post-processing such as additional compression and sintering. This study used block-type powder porous materials with two different cell sizes: one with an average cell size of 1,200 μm (1200 foam) and the other with an average cell size of 3,000 μm (3000 foam). The γ-Ni and γ’-Ni3Al were identified as the main phases of both materials. However, in the case of the 1,200 foam, a β-NiAl phase was additionally observed. The relative density of each block-type powder porous material, with 1200 foam and 3000 foam, was measured to be 5.78% and 2.93%, respectively. Tensile tests were conducted with strain rates of 10−2~10−4 sec−1. The test result showed that the tensile strength of the 1,200 foam was 6.0~7.1 MPa, and that of 3,000 foam was 3.0~3.3 MPa. The elongation of the 3,000 foam was higher (~9%) than that (~2%) of the 1,200 foam. This study also discussed the deformation behavior of block-type powder porous material through observations of the fracture surface, with the results above.
Abstract
This study investigated the microstructure and tensile properties of a recently made block-type Ni-Cr-Al powder porous material. The block-type powder porous material was made by stacking multiple layers of powder porous thin plates with post-processing such as additional compression and sintering. This study used block-type powder porous materials with two different cell sizes: one with an average cell size of 1,200 μm (1200 foam) and the other with an average cell size of 3,000 μm (3000 foam). The γ-Ni and γ’-Ni3Al were identified as the main phases of both materials. However, in the case of the 1,200 foam, a β-NiAl phase was additionally observed. The relative density of each block-type powder porous material, with 1200 foam and 3000 foam, was measured to be 5.78% and 2.93%, respectively. Tensile tests were conducted with strain rates of 10−2~10−4 sec−1. The test result showed that the tensile strength of the 1,200 foam was 6.0~7.1 MPa, and that of 3,000 foam was 3.0~3.3 MPa. The elongation of the 3,000 foam was higher (~9%) than that (~2%) of the 1,200 foam. This study also discussed the deformation behavior of block-type powder porous material through observations of the fracture surface, with the results above.
참고문헌 (26)
- L. J. Gibson, "Cellular solids, Structure and Properties", pp.532~ (1997), Cambridge University Press
- T. J. Lu, , Acta Mater., 46, pp.3619~ (1998)
- C. Y. Zhao, , Int. J. Heat Mass Transfer., 55, pp.3618~ (2012)
- T. J. Lu, , Int. J. Heat Mass Transfer., 42, pp.2031~ (1998)
- H. Nakajima, , Progress in Mater. Science, 52, pp.1091~ (2007)
- W. Azzi, , Materials and Design, 28, pp.569~ (2007)
- 최내현, "금속 분말을 이용한 합금폼 제조 및 특성", 한국분말야금학회지, 17(6), pp.489~493 (2010), 한국분말야금학회
- M. F. Ashby, "Wadley: Metal Foams: A design Guide", pp.263~ (2000), Oxford Press
- M. F. Ashby, "Cellular metals and metal foaming technology", pp.519~ (2001), MIT Press
- J. G. Smeggil, , Metall. Trans., 17, pp.923~ (1986)
- R. A. Steven, , Mater. Sci. Eng., 37, pp.237~ (1979)
- G. H. Gessinger, "Powder metallurgy of superalloys" (1984), Butterworth & Co.
- E. Koza, , Mater. Lett., 58, pp.132~ (2004)
- E. Sáenz, , Bol. Soc. Esp. Ceram. Vidrio., 39, pp.506~ (2000)
- J. Bin, , Scr. Mater., 56, pp.169~ (2007)
- M. Hakamada, , J. Mater. Res., 20, pp.3387~ (2005)
- T. G. Nieh, , Mater. Sci. Eng. A., 283, pp.105~ (2000)
- J. Zhou, , Mater. Sci. Eng. A., 386, pp.118~ (2004)
- Y. Yamada, , Mater. Sci. Eng. A., 280, pp.225~ (2000)
- D. T. Queheillalt, , Scr. Mater., 50, pp.313~ (2004)
- X. badiche, , Mater. Sci. Eng. A., 289, pp.276~ (2000)
- Sung-Hwan Choi, "Effect of Pore Size on the High Temperature Oxidation of Ni-Fe-Cr-Al Porous Metal", Metals and Materials International, 17(2), pp.301~307 (2011), 대한금속·재료학회
- 임선희, "Fe-Cr-Al계 분말 다공체 금속과 박판재의 고온 산화 거동", 대한금속·재료학회지, 51(10), pp.743~751 (2013), 대한금속·재료학회[DOI]
- J. S. Oh, , Met. Mater. Int., 20, pp.931~ (2014)
- Kyu-Sik Kim, "Effect of the Pore Size on the Creep Deformation Behavior of Ni-Fe-Cr-Al Porous Metal", Metals and Materials International, 20(3), pp.507~513 (2014), 대한금속·재료학회[DOI]
- K.C. Russell, , J. Met. Sci., 6, pp.20~ (1972)