W-Cu 나노분말 합성을 위해 비드밀에서 고에너지 볼밀링 공정에 의해 제조된 WO3-CuO 혼합분말의 특성 연구
Characteristics of WO3-CuO Powder Mixture Prepared by High-Energy Ball Milling in a Bead Mill for the Synthesis of W-Cu Nanocomposite Powder
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
A Nanosized WO3 and CuO powder mixture is prepared using novel high-energy ball milling in a bead mill to obtain a W-Cu nanocomposite powder, and the effect of milling time on the structural characteristics of WO3-CuO powder mixtures is investigated. The results show that the ball-milled WO3-CuO powder mixture reaches at steady state after 10 h milling, characterized by the uniform and narrow particle size distribution with primary crystalline sizes below 50 nm, a specific surface area of 37 m2/g, and powder mean particle size (D50) of 0.57 μm. The WO3-CuO powder mixtures milled for 10 h are heat-treated at different temperatures in H2 atmosphere to produce W-Cu powder. The XRD results shows that both the WO3 and CuO phases can be reduced to W and Cu phases at temperatures over 700oC. The reduced W-Cu nanocomposite powder exhibits excellent sinterability, and the ultrafine W-Cu composite can be obtained by the Cu liquid phase sintering process.
Abstract
A Nanosized WO3 and CuO powder mixture is prepared using novel high-energy ball milling in a bead mill to obtain a W-Cu nanocomposite powder, and the effect of milling time on the structural characteristics of WO3-CuO powder mixtures is investigated. The results show that the ball-milled WO3-CuO powder mixture reaches at steady state after 10 h milling, characterized by the uniform and narrow particle size distribution with primary crystalline sizes below 50 nm, a specific surface area of 37 m2/g, and powder mean particle size (D50) of 0.57 μm. The WO3-CuO powder mixtures milled for 10 h are heat-treated at different temperatures in H2 atmosphere to produce W-Cu powder. The XRD results shows that both the WO3 and CuO phases can be reduced to W and Cu phases at temperatures over 700oC. The reduced W-Cu nanocomposite powder exhibits excellent sinterability, and the ultrafine W-Cu composite can be obtained by the Cu liquid phase sintering process.
참고문헌 (25)
- K. V. Sebastian, , Int. J. Powder Metall., 17, pp.297~ (1981)
- B. L. Mordike, , Powder Metall. Int., 23, pp.91~ (1991)
- R. M. German, , Int. J. PowderMetall., 30, pp.205~ (1994)
- T. B. Massalski, "Binary Phase Diagram", pp.1503~ (1990), ASM
- W. D. Kingery, , J. Appl. Phys., 30, pp.301~ (1959)
- W. J. Huppmann, , Powder Metall, 18, pp.249~ (1975)
- I. H. Moon, , Powder Metall., 22, pp.5~ (1979)
- J. L. Johnson, , Proceedings of the International Conference & Exhibition on Powder Metallurgy & Particulate Materials, 3, pp.35~46 (1992), Advances in Powder Metallurgy and Particulate Materials
- J. S. Lee, , Nanostruc. Mater., 6, pp.691~ (1996)
- I. H. Moon, , Powder Metall., 41, pp.51~ (1998)
- S. H. Hong, , Mater. Lett., 57, pp.2761~ (2003)
- J. Cheng, , Mater. Sci. Eng. A, 488, pp.453~ (2008)
- M. Hashempour, , Mater. Charact., 60, pp.1232~ (2009)
- J. C. Kim, , Nanostruct. Mater., 10, pp.283~ (1998)
- T. Aboud, , Nanostruct. Mater., 6, pp.405~ (1995)
- M. H. Maneshian, , Mater Sci. Eng. A, 445-446, pp.86~ (2007)
- D. G. Kim, , Mater. Lett., 58, pp.1199~ (2004)
- E. Ahmadi, , Int. J. Refract. Met. Hard Mater., 28, pp.445~ (2010)
- Lei Wan, , Int. J. Refract. Met. Hard Mater., 29, pp.429~ (2011)
- P. K. Sahoo, , Int. J. Refract. Met. Hard Mater., 29, pp.547~ (2011)
- K. S. Hwang, , Powder Metall., 46, pp.113~ (2003)
- S. S. Ryu, , J. Electroceram., 18, pp.243~ (2007)
- M. Inkyo, , J. Colloid Interface, 304, pp.535~ (2006)
- S. S. Ryu, "On sinterability of Cu-coated W nanocomposite powder prepared by a hydrogen reduction of a high-energy ball-milled WO3-CuO mixture", Journal of Materials Science, 47(20), pp.7099~7109 (2012), Springer Nature[DOI]
- S. S. Ryu, , Int. J. Refract. Met. Hard Mater., 65, pp.39~ (2017)