MoO3-CuO 혼합분말의 볼 밀링 및 수소분위기 열처리에 의한 Mo-Cu 복합분말 제조
Fabrication of Mo-Cu Powders by Ball Milling and Hydrogen Reduction of MoO3-CuO Powder Mixtures
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
The hydrogen reduction behavior of MoO3-CuO powder mixture for the synthesis of homogeneous Mo-20 wt% Cu composite powder is investigated. The reduction behavior of ball-milled powder mixture is analyzed by XRD and temperature programmed reduction method at various heating rates in Ar-10% H2 atmosphere. The XRD analysis of the heat-treated powder at 300oC shows Cu, MoO3, and Cu2MoO5 phases. In contrast, the powder mixture heated at 400oC is composed of Cu and MoO2 phases. The hydrogen reduction kinetic is evaluated by the amount of peak shift with heating rates. The activation energies for the reduction, estimated by the slope of the Kissinger plot, are measured as 112.2 kJ/mol and 65.2 kJ/mol, depending on the reduction steps from CuO to Cu and from MoO3 to MoO2, respectively. The measured activation energy for the reduction of MoO3 is explained by the effect of pre-reduced Cu particles. The powder mixture, hydrogen-reduced at 700oC, shows the dispersion of nano-sized Cu agglomerates on the surface of Mo powders.
Abstract
The hydrogen reduction behavior of MoO3-CuO powder mixture for the synthesis of homogeneous Mo-20 wt% Cu composite powder is investigated. The reduction behavior of ball-milled powder mixture is analyzed by XRD and temperature programmed reduction method at various heating rates in Ar-10% H2 atmosphere. The XRD analysis of the heat-treated powder at 300oC shows Cu, MoO3, and Cu2MoO5 phases. In contrast, the powder mixture heated at 400oC is composed of Cu and MoO2 phases. The hydrogen reduction kinetic is evaluated by the amount of peak shift with heating rates. The activation energies for the reduction, estimated by the slope of the Kissinger plot, are measured as 112.2 kJ/mol and 65.2 kJ/mol, depending on the reduction steps from CuO to Cu and from MoO3 to MoO2, respectively. The measured activation energy for the reduction of MoO3 is explained by the effect of pre-reduced Cu particles. The powder mixture, hydrogen-reduced at 700oC, shows the dispersion of nano-sized Cu agglomerates on the surface of Mo powders.
참고문헌 (19)
- 황창규, "Heat Sink용 Mo-Cu 합금 재료의 열적 특성", 열처리공학회지, 16(6), pp.311~314 (2003), 한국열처리공학회
- Y.-L. Shen, , Metall. Mater. Trans. A, 25, pp.839~ (1994)
- J.A. Shields Jr., , JOM, 52, pp.37~ (2000)
- G.-Q. Chen, , Trans. Nonferr. Metal Soc., 17, pp.s580~ (2007)
- J.L. Johnson, , Metall. Mater. Trans. A, 32, pp.605~ (2001)[DOI]
- J.L. Johnson, , Int. J. Powder Metall., 35, pp.39~ (1999)
- A. Sun, , J. Alloys Compd., 505, pp.588~ (2010)[DOI]
- 이한찬, "유성볼밀링 및 스파크 플라즈마 소결법으로 제조한 Mo-5∼20 wt%. Cu 합금의 열적 특성", 전기전자재료학회논문지, 29(8), pp.516~521 (2016), 한국전기전자재료학회[DOI]
- D.-G. Kim, , J. Alloys Compd., 354, pp.239~ (2003)[DOI]
- 권나연, "텅스텐 산화물의 환원을 이용한 나노", 마이크로 크기 텅스텐 혼합분말 제조, 2017, pp.27(10), 513~517[DOI]
- G. Fierro, , J. Catal., 148, pp.709~ (1994)[DOI]
- A. Sun, , J. Alloys Compd., 509, pp.L74~ (2011)[DOI]
- W.V. Schulmeyer, , Int. J. Refract. Met. Hard Mater., 20, pp.261~ (2002)[DOI]
- G.-S. Kim, , J. Alloys Compd., 454, pp.327~ (2008)[DOI]
- D.-G. Kim, , Mater. Sci. Eng. A, 399, pp.326~ (2005)[DOI]
- H.E. Kissinger, , Anal. Chem., 29, pp.1702~ (1957)[DOI]
- P. Malet, , J. Chem. Soc., Faraday Trans. 1, 84, pp.2369~ (1988)[DOI]
- L. Wang, , Int. J. Refract. Met. Hard Mater., 54, pp.342~ (2016)[DOI]
- J. Dang, , Int. J. Refract. Met. Hard Mater., 41, pp.216~ (2013)[DOI]