수소 첨가 열처리에 따른 Ti-6Al-4V 합금 분말의 격자 변형 및 내산화성 향상
Lattice Deformation and Improvement Oxidation Resistance of Ti-6Al-4V Alloy Powders Prepared by Hydrogen Added Argon Heat Treatment
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In the present work, a new hydrogen added argon heat treatment process that prevents the formation of hydrides and eliminates the dehydrogenation step, is developed. Dissolved hydrogen has a good effect on sintering properties such as oxidation resistance and density of greens. This process can also reduce costs and processing time. In the experiment, commercially available Ti-6Al-4V powders are used. The powders are annealed using tube furnace in an argon atmosphere at 700oC and 900oC for 120 min. Hydrogen was injected temporarily during argon annealing to dissolve hydrogen, and a dehydrogenation process was performed simultaneously under an argon-only atmosphere. Without hydride formation, hydrogen was dissolved in the Ti-6Al-4V powder by X-ray diffraction and gas analysis. Hydrogen is first solubilized on the beta phase and expanded the beta phases’ cell volume. TGA analysis was carried out to evaluate the oxidation resistance, and it is confirmed that hydrogen-dissolved Ti-6Al-4V powders improves oxidation resistance more than raw materials.
Abstract
In the present work, a new hydrogen added argon heat treatment process that prevents the formation of hydrides and eliminates the dehydrogenation step, is developed. Dissolved hydrogen has a good effect on sintering properties such as oxidation resistance and density of greens. This process can also reduce costs and processing time. In the experiment, commercially available Ti-6Al-4V powders are used. The powders are annealed using tube furnace in an argon atmosphere at 700oC and 900oC for 120 min. Hydrogen was injected temporarily during argon annealing to dissolve hydrogen, and a dehydrogenation process was performed simultaneously under an argon-only atmosphere. Without hydride formation, hydrogen was dissolved in the Ti-6Al-4V powder by X-ray diffraction and gas analysis. Hydrogen is first solubilized on the beta phase and expanded the beta phases’ cell volume. TGA analysis was carried out to evaluate the oxidation resistance, and it is confirmed that hydrogen-dissolved Ti-6Al-4V powders improves oxidation resistance more than raw materials.
참고문헌 (14)
- J. S. Choe, , Kor. J. Mater. Res, 10, pp.464~ (2000)
- L. Mei, , Int. J. Hydrogen Energy, 43, pp.7102~ (2018)
- P. Sun, , Adv Eng Mater, 15, pp.1007~ (2013)
- W. B. Kim, , Kor. J. Mater. Res, 9, pp.282~ (1999)
- J. M. Oh, , Mater Trans, 54, pp.119~ (2013)
- D. W. Lee, , Procedia Manuf, 2, pp.550~ (2015)
- Z. Z. Fang, , Adv Eng Mater, 14, pp.383~ (2012)
- J. G. Ku, , Int. J. Hydrogen Energy, 42, pp.2139~ (2017)
- 신기승, "Ti-10wt.%Al-xMn 분말합금의 Mn첨가에 따른 소결특성 평가", 한국분말재료학회지, 24(3), pp.235~241 (2017), 한국분말재료학회[DOI]
- R. L. Coble, , J. Am. Ceram. Soc, 45, pp.123~ (1962)
- T. Zhu, , Mater Charact, 62, pp.724~ (2011)
- O. N. Senkov, , Mater. Res Bull, 36, pp.1431~ (2001)
- J. I. Qazi, , Metall. Mater. Trans. A, 32, pp.2453~ (2001)
- P. Sun, , Acta Mater, 84, pp.29~ (2015)