타이타늄 합금 분말 형상 및 치밀화 기구에 따른 미세조직 및 기 계적 물성 영향 연구
Effects of Powder Shape and Densification Mechanism on the Microstructures and Mechanical Properties of Ti-6Al-4V Components
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The objective of this study is to investigate the influence of powder shape and densification mechanism on the microstructure and mechanical properties of Ti-6Al-4V components. BE powders are uniaxially and isostatically pressed, and PA ones are injection molded because of their high strengths. The isostatically compacted samples exhibit a density of 80%, which is higher than those of other samples, because hydrostatic compression can lead to higher strain hardening. Owing to the higher green density, the density of BE-CS (97%) is found to be as high as that of other samples (BE-DS (95%) and P-S (94%)). Furthermore, we have found that BE powders can be consolidated by sintering densification and chemical homogenization, whereas PA ones can be consolidated only by simple densification. After sintering, BE-CS and P-S are hot isostatically pressed and BE-DS is hot forged to remove residual pores in the sintered samples. Apparent microstructural evolution is not observed in BE-CSH and P-SH. Moreover, BE-DSF exhibits significantly fine grains and high density of low-angle grain boundaries. Thus, these microstructures provide Ti-6Al-4V components with enhanced mechanical properties (tensile strength of 1179 MPa).
Abstract
The objective of this study is to investigate the influence of powder shape and densification mechanism on the microstructure and mechanical properties of Ti-6Al-4V components. BE powders are uniaxially and isostatically pressed, and PA ones are injection molded because of their high strengths. The isostatically compacted samples exhibit a density of 80%, which is higher than those of other samples, because hydrostatic compression can lead to higher strain hardening. Owing to the higher green density, the density of BE-CS (97%) is found to be as high as that of other samples (BE-DS (95%) and P-S (94%)). Furthermore, we have found that BE powders can be consolidated by sintering densification and chemical homogenization, whereas PA ones can be consolidated only by simple densification. After sintering, BE-CS and P-S are hot isostatically pressed and BE-DS is hot forged to remove residual pores in the sintered samples. Apparent microstructural evolution is not observed in BE-CSH and P-SH. Moreover, BE-DSF exhibits significantly fine grains and high density of low-angle grain boundaries. Thus, these microstructures provide Ti-6Al-4V components with enhanced mechanical properties (tensile strength of 1179 MPa).
참고문헌 (27)
- M. Peters, "Titanium and titanium alloys", pp.1~ (2003), Wilely-VCH GmnbH and Co.
- D. M. Bowden, "Near-net shape fabrication using low-cost titanium alloy powders", pp.28~ (2012), The Boeing Company
- K. Faller, , JOM, 53, pp.27~ (2001)
- F. H. Froes, , JOM, 32, pp.47~ (1980)
- F. H. Froes, , Powder Metall. Int, 17, pp.163~ (1985)
- V. Moxson, , JOM, 52, pp.24~ (2000)
- F. H. Froes, , JOM, 56, pp.46~ (2004)
- F. H. Froes, , JOM, 59, pp.28~ (2007)
- S. M. Abkowitz, , Met. Powder Rep, 66, pp.16~ (2011)
- T. Fujita, , Mater. Sci. Eng., A, 213, pp.148~ (1996)
- O. M. Ivasishin, , Key Eng. Mater, 188, pp.55~ (2000)
- O. M. Ivasishin, , Powder Metall. Met. Ceram, 41, pp.382~ (2002)
- L. Bolzoni, , J. Mech. Behav. Biomed. Mater, 15, pp.33~ (2012)
- Y. Kim, , Metall. Mater. Trans. A, 47, pp.4616~ (2016)
- D. P. Delo, , Acta Mater, 47, pp.2841~ (1999)
- K. Zhang, , Metall. Mater. Trans. A, 41, pp.1033~ (2010)
- Y. Kim, , J. Alloys Compd, 603, pp.207~ (2014)
- R. P. Guo, , Mater. Sci. Forum, 849, pp.760~ (2016)
- 곽지나, "플라즈마 공정으로 구상화된 티타늄 분말과 금속사출성형공정을 이용한 치과용 부품 제조", 한국분말재료학회지, 20(6), pp.467~473 (2013), 한국분말재료학회
- A. M. Beese, , JOM, 68, pp.724~ (2016)
- B. Dutta, "Titanium powder metallurgy", pp.477~ (2015), Butterworth-Heinemann
- T. Machry, , Powder Metall, 59, pp.41~ (2016)
- F. H. Froes, "Advances in powder metallurgy", pp.2021~ (2013), Woodhead Publishing
- S. Abkowitz, "Titanium powder metallurgy", pp.21~ (2015), Butterworth-Heinemann
- S. Abkowitz, "Titanium powder metallurgy", pp.299~ (2015), Butterworth-Heinemann
- 김영무, "Solid-state sintering mechanism of blended elemental Ti-6Al-4V powders", 한국분말재료학회지, 25(2), pp.109~119 (2018), 한국분말재료학회[DOI]
- K. T. Kim, , Int. J. Solids Struct, 24, pp.937~ (1988)