다층 산화주석(SnO)의 합성 및 열처리를 통한 리튬이온 이차전지 음극 소재의 성능 향상
Synthesis of the Multi-layered SnO Nanoparticles and Enhanced Performance of Lithium-Ion Batteries by Heat treatment
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, multilayered SnO nanoparticles are prepared using oleylamine as a surfactant at 165oC. The physical and chemical properties of the multilayered SnO nanoparticles are determined by transmission electron microscopy (TEM), scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). Interestingly, when the multilayered SnO nanoparticles are heated at 400oC under argon for 2 h, they become more efficient anode materials, maintaining their morphology. Heat treatment of the multilayered SnO nanoparticles results in enhanced discharge capacities of up to 584 mAh/g in 70 cycles and cycle stability. These materials exhibit better coulombic efficiencies. Therefore, we believe that the heat treatment of multilayered SnO nanoparticles is a suitable approach to enable their application as anode materials for lithium-ion batteries.
Abstract
In this study, multilayered SnO nanoparticles are prepared using oleylamine as a surfactant at 165oC. The physical and chemical properties of the multilayered SnO nanoparticles are determined by transmission electron microscopy (TEM), scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). Interestingly, when the multilayered SnO nanoparticles are heated at 400oC under argon for 2 h, they become more efficient anode materials, maintaining their morphology. Heat treatment of the multilayered SnO nanoparticles results in enhanced discharge capacities of up to 584 mAh/g in 70 cycles and cycle stability. These materials exhibit better coulombic efficiencies. Therefore, we believe that the heat treatment of multilayered SnO nanoparticles is a suitable approach to enable their application as anode materials for lithium-ion batteries.
참고문헌 (32)
- J. H. Shim, , ACS Appl. Mater. Interfaces, 11, pp.4017~ (2019)
- F. Wang, , ACS Nano, 13, pp.12219~ (2019)
- J. G. Han, , Adv. Mater, 31, pp.1804822~ (2019)
- J. Zhang, , J. Electroanal. Chem, 767, pp.49~ (2016)
- X. Li, , Appl. Surf. Sci, 412, pp.170~ (2017)
- B. Xu, , Appl. Surf. Sci, 546, pp.148814~ (2021)
- H. Zhang, , J. Mater. Chem. A, 4, pp.10585~ (2016)
- L. Peng, , Nat. Commun, 8, pp.15139~ (2017)
- W. Yue, , Electrochim. Acta, 92, pp.412~ (2013)
- Chen, , J. Mater. Chem. A, 2, pp.9345~ (2014)
- H. Zhang, , Adv. Funct. Mater, 27, pp.1606023~ (2017)
- A. Shukla, , Chem. Phys. Lett, 754, pp.137717~ (2020)
- L. Liu, , J. Power Sources, 321, pp.11~ (2016)
- D. Aurbach, , Chem. Mater, 14, pp.4155~ (2002)
- W. Jiang, , RSC Adv, 4, pp.41281~ (2014)
- X. T. Chen, , Dalton Trans, 43, pp.3137~ (2014)
- Shin Jeong Ho, "Electrochemical properties of Sn-decorated SnO nanobranches as an anode of Li-ion battery", Nano Convergence, 3(9), pp.1~7 (2016), 나노기술연구협의회[DOI]
- Y. Cheng, , Micro &Nano Lett, 13, pp.257~ (2018)
- J. Zeng, , Ceram. Int, 45, pp.19404~ (2019)
- Q. Ren, , Sens. Actuators. B, 340, pp.129940~ (2021)
- K. H. Park, , Chem. Mater, 19, pp.3861~ (2007)
- J. Choi, , Chem. Mater, 22, pp.3586~ (2010)
- J. Choi, , J. Mater. Chem, 22, pp.11107~ (2012)
- W. Li, , Microelectron Reliab, 55, pp.402~ (2015)
- F. Li, , Electrochim. Acta, 178, pp.34~ (2015)
- J. Zeng, , Ceram. Int, 45, pp.1246~ (2019)
- Q. Zhao, , Ceram. Int, 45, pp.17529~ (2019)
- L. Meng, , Sens. Actuators. B, 342, pp.130018~ (2021)
- Y. Zhang, , J. Mater. Chem. A, 5, pp.512~ (2017)
- P. T. Hung, , ACS Appl. Mater. Interfaces, 12, pp.34274~ (2020)
- Y. Hu, , Chem. Eng. J, 242, pp.220~ (2014)
- L. Li, , Nanoscale, 7, pp.12133~ (2015)