초경소재 선정을 위한 고속가공의 엔드밀 성능 평가
Performance Evaluation on the Endmill of High Speed Machiningfor Selection of Tungsten Carbide (WC-Co) Material
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
To satisfy the demand of higher cutting performance, mechanical properties with tungsten carbide (WC-Co) tool materials were investigated. Hardness and transverse rupture strength with WC grain size, Co content and density were measured. Compared to H, K, and S manufacture maker as tungsten carbide (WC-Co) tool materials were used for high-speed machining of end-milling operation. The three tungsten carbide (WC-Co) tool materials were evaluated by cutting of STD11 cold-worked die steel (HRC25) under high-speed cutting condition. Also, tool life was obtained from measuring flank wear by CCD wear measuring system. Tool dynamometer was used to measure cutting force. The cutting force and tool wear are discussed along with tool material characteristics. Consequently, the end-mill of K, H manufacture maker showed higher wear-resistance due to its higher hardness, while the S maker endmill tool showed better performance for high metal removal.
Abstract
To satisfy the demand of higher cutting performance, mechanical properties with tungsten carbide (WC-Co) tool materials were investigated. Hardness and transverse rupture strength with WC grain size, Co content and density were measured. Compared to H, K, and S manufacture maker as tungsten carbide (WC-Co) tool materials were used for high-speed machining of end-milling operation. The three tungsten carbide (WC-Co) tool materials were evaluated by cutting of STD11 cold-worked die steel (HRC25) under high-speed cutting condition. Also, tool life was obtained from measuring flank wear by CCD wear measuring system. Tool dynamometer was used to measure cutting force. The cutting force and tool wear are discussed along with tool material characteristics. Consequently, the end-mill of K, H manufacture maker showed higher wear-resistance due to its higher hardness, while the S maker endmill tool showed better performance for high metal removal.
참고문헌 (17)
- S. Hogmark, , Wear, 246, pp.20~ (2000)
- W. Y. Bao, , Int. J. Mach. Tools Manuf, 40, pp.2155~ (2000)
- S. Ulvi, , J. of Mat. Proce. Technol, 173, pp.260~ (2006)
- S. Tomasz, , Surf Coat Technol, 194, pp.319~ (2005)
- M. Rahman, , J. Of MTM, 42, pp.539~ (2001)
- W. Maritzen, , Powder Metall, 17, pp.68~ (1985)
- Walid M. Daoush, "(W,Ti)C계 초경합금의 미세조직 및 경도에 미치는금속 결합재 조성의 영향", 한국분말야금학회지, 14(3), pp.208~214 (2007), 한국분말야금학회
- J. Almer, , Thin Solid Films, 385, pp.190~197 (2001)
- T. Cselle, , Surf. Coat. Technol, 76, pp.712~ (1995)
- E. Lardner, , Power Metall, 21, pp.65~ (1978)
- H. Juan, "Int", J. of Mach. Tools Manuf, 43, pp.679~ (2003)
- D. R. Kumar, , Indian Inst. of Technol, 45, pp.219~ (2002)
- S. W. Huang, , Wear, 252, pp.566~ (2002)
- 김진천, "기상응축법으로 제조한 나노 WC 및 WC-Co 분말의 후속 열처리에 의한 상 및 형상 변화", 한국분말야금학회지, 11(2), pp.124~129 (2004), 한국분말야금학회
- J. H. Kim, "Prototype tryout and die design for automotive parts using welded blank hydroforming", J. of Mat. Proce. Technol, 130-131, pp.126~ (2002)
- H. Saito, , Wear, 261, pp.132~ (2006)
- D. H. Kwon, , Surf. Coat. Technol, 200, pp.1933~ (2005)