고주파유도가열 연소합성에 의한 4.25 Co0.53Fe0.47-Al2O3 복합재료 제조
Fabrication of 4.25 Co0.53Fe0.47-Al2O3 Composite by High Frequency Induction Heated Combustion Synthesis
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Nanopowders of Co3O4 and FeAl were fabricated by high energy ball milling. Dense 4.25 Co0.53Fe0.47-Al2O3 composite was simultaneously synthesized and consolidated by high frequency induction heated combustion method within 2 min from mechanically activated powders. Consolidation was accomplished under the combined effects of a induced current and mechanical pressure of 80 MPa.
Abstract
Nanopowders of Co3O4 and FeAl were fabricated by high energy ball milling. Dense 4.25 Co0.53Fe0.47-Al2O3 composite was simultaneously synthesized and consolidated by high frequency induction heated combustion method within 2 min from mechanically activated powders. Consolidation was accomplished under the combined effects of a induced current and mechanical pressure of 80 MPa.
참고문헌 (18)
- L. Ceschini, , Composites Science and Technology, 66, pp.333~ (2006)
- S. C. Tjong, , Mater Sci Eng., 29, pp.49~ (2000)
- D. J. Lloyd, , Int Mater Rev., 39, pp.1~ (1994)
- J. M. Torralba, , J Mater Proce Tech., 133, pp.203~ (2006)
- R. Fan, , Mater. Chem. Phys., 91, pp.140~ (2005)
- S. K. Bae, , Scripta Materialia., 58, pp.425~ (2008)
- I. P. Borovinskaya, , Combust. Explos. Shock Waves., 10, pp.2~ (1974)
- A. G. Merzhanov, , Ko: Sov. Powder Metall. Met Ceram., 20, pp.709~ (1981)
- M. S. El-Eskandarany, , J. Alloys & Compounds., 305, pp.225~ (2000)
- L. Fu, , Scripta Materialia., 44, pp.1061~ (2001)
- I. J. Shon, , Materials Science Forum., 통권 : 534, pp.525~ (2007)
- Z. Fang, , Int. J. of Refractory Met. & Hard Mater., 31, pp.297~ (1995)
- A. I. Y. Tok, , Mater Sci Eng A., 383, pp.229~ (2004)
- C. Suryanarayana, , pp.207~ (1998), Plenum Press.
- Z. Shen, , J. Am. Ceram Soc., 85, pp.1921~ (2002)
- J. E. Garay, , Appl. Phys. Lett., 85, pp.573~ (2004)
- J. R. Friedman, , Intermetallics., 12, pp.589~ (2004)
- J. E. Garay, , Acta Mater., 51, pp.4487~ (2003)