가스응축장치 캐리어가스 공급속도 및 압력변화를 통한 비스무스 나노분말 입도제어
Size Control of Bismuth Nanoparticles by Changes in Carrier-Gas Flow Rate and Chamber Pressure of Gas Condensation Apparatus
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In the present work, bismuth nanopowders with various particle size distributions were synthesized by controlling argon (Ar) gas flow rate and chamber pressure of a gas condensation (GC) apparatus. From the analyses of transmission electron microscopy (TEM) images and nitrogen gas adsorption results, it was found that as Ar gas flow rate increased, the specific surface area of bismuth increased and the average particles size decreased. On the other hand, as the chamber pressure increased, the specific surface area of bismuth decreased and the average particles size increased. The optimum gas flow rate and chamber pressure for the maximized electrochemical active surface area were determined to be 8 L/min and 50 torr, respectively. The bismuth nanopowders synthesized at the above condition exhibit 13.47 m2g−1 of specific surface area and 45.6 nm of average particles diameter.
Abstract
In the present work, bismuth nanopowders with various particle size distributions were synthesized by controlling argon (Ar) gas flow rate and chamber pressure of a gas condensation (GC) apparatus. From the analyses of transmission electron microscopy (TEM) images and nitrogen gas adsorption results, it was found that as Ar gas flow rate increased, the specific surface area of bismuth increased and the average particles size decreased. On the other hand, as the chamber pressure increased, the specific surface area of bismuth decreased and the average particles size increased. The optimum gas flow rate and chamber pressure for the maximized electrochemical active surface area were determined to be 8 L/min and 50 torr, respectively. The bismuth nanopowders synthesized at the above condition exhibit 13.47 m2g−1 of specific surface area and 45.6 nm of average particles diameter.
참고문헌 (19)
- J. Wang, , Anal. Chem, 72, pp.3218~ (2000)
- J. Wang, , Electroanal, 13, pp.13~ (2001)
- J. Wang, , Anal. Chim. Acta, 434, pp.29~ (2001)
- S. B. Hocevar, , Electroanal, 17, pp.1707~ (2002)
- G. Kefala, , Talanta, 61, pp.603~ (2003)
- G. Kefala, , Analyst, 129, pp.1082~ (2004)
- J. Kruusma, , Anal.Bioanal. Chem, 379, pp.700~ (2004)
- C. E Banks, , Talanta, 65, pp.423~ (2005)
- J. Wang, , Electroanal, 17, pp.1341~ (2005)
- R. Pauliukaitë, , Electroanal, 17, pp.1354~ (2005)
- I. Svancara, , Electroanal, 18, pp.177~ (2006)
- G.-J. Lee, , Electrochem.Commun, 9, pp.2514~ (2007)
- G.-J. Lee, , Electrochem. Commun, 10, pp.1920~ (2008)
- H. M. Lee, , J. Nanosci. Nanotechnol, 10, pp.309~ (2010)
- A. Y. Yermakov, , Mater. Sci. Forum, 455, pp.386~388 (2002)
- Y. R. Uhm, , Phys. Stat. Sol, 201, pp.1934~ (2004)
- B. S. Han, , IEEE Trans. Magnetics, 42, pp.3779~ (2006)
- Y. R. Uhm, , Mater. Sci. and Eng, 813, pp.449~451 (2007)
- Chang Kyu Rhee, "Fabrication of Al Nano Powders by Pulsed Wire Evaporation (PWE) Method", Journal of Industrial and Engineering Chemistry, 9(1), pp.71~75 (2003), 한국공업화학회