W92-Ni-Fe 소결툴을 이용한 Cu-Ni 합금의 용접부 미세조직과 경도 특성
Investigation for Microstructure and Hardness of Welded Zone of Cu-Ni Alloy using W92-Ni-Fe Sintering Tool
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, the effect of the friction stir welding (FSW) was compared with that of the gas tungsten arc welding (GTAW) on the microstructure and microhardness of Cu-Ni alloy weldment. The weldment of 10 mm thickness was fabricated by FSW and GTAW, respectively. Both weldments were compared with each other by optical microstructure, microhardness test and grain size measurement. Results of this study suggest that the microhardness decreased from the base metal (BM) to the heat affected zone (HAZ) and increased at fusion zone (FZ) of GTAW and stir zone (SZ) of FSW. the minimum Hv value of both weldment was obtained at HAZ, respectively, which represents the softening zone, whereas Hv value of FSW weldment was little higher than that of GTAW weldment. These phenomena can be explained by the grain size difference between HAZs of each weldment. Grain size was increased at the HAZ during FSW and GTAW. Because FSW is a solid-state joining process obtaining the lower heat-input generated by rotating shoulder than heat generated in the arc of GTAW.
Abstract
In this study, the effect of the friction stir welding (FSW) was compared with that of the gas tungsten arc welding (GTAW) on the microstructure and microhardness of Cu-Ni alloy weldment. The weldment of 10 mm thickness was fabricated by FSW and GTAW, respectively. Both weldments were compared with each other by optical microstructure, microhardness test and grain size measurement. Results of this study suggest that the microhardness decreased from the base metal (BM) to the heat affected zone (HAZ) and increased at fusion zone (FZ) of GTAW and stir zone (SZ) of FSW. the minimum Hv value of both weldment was obtained at HAZ, respectively, which represents the softening zone, whereas Hv value of FSW weldment was little higher than that of GTAW weldment. These phenomena can be explained by the grain size difference between HAZs of each weldment. Grain size was increased at the HAZ during FSW and GTAW. Because FSW is a solid-state joining process obtaining the lower heat-input generated by rotating shoulder than heat generated in the arc of GTAW.
참고문헌 (14)
- C. S. Dimbylow, , 46, pp.461~ (1978)
- M. S. Wiener, , Corrosion Eng Sci Tech, 40, pp.137~ (2005)
- 서한길, "CuO-NiO 혼합분말의 동결건조 및 수소환원에 의한 Cu-Ni 다공체 제조", 한국분말야금학회지, 21(1), pp.34~38 (2014), 한국분말야금학회
- S. H. Gutierrez, , Weld J., pp.76~ (1991)
- M. G. Collins, , Proc. of 6th International Trends in Welding Research Conference ASM International, pp.586~ (2003)
- S. A. Gavin, , Met Tech., 5, pp.397~ (1978)
- R. S. Mishra, , Mater. Sci. Eng. R., 50, pp.1~ (2005)
- 윤태진, "A5J32", A5052 이종 알루미늄 합금 겹치기 마찰교반접합부의 인장성질에 미치는 재료배열 및 접합조건의 영향, 2013, pp.20(4), 302~307[DOI]
- R. T. Lee, , J. Mater. Proccess Tech., 213, pp.69~ (2013)
- T.-J. Yoon, , Mater. Lett., 142, pp.253~ (2015)
- 이아름, "SAC 305솔더와 ENIG 기판의 접합강도에 미치는 저주파 수소라디칼처리의 영향", 대한용접접합학회지, 29(1), pp.99~106 (2011), 대한용접접합학회
- E.O. Hall, , Proc. Phys Soc. B, 64, pp.747~ (1951)
- N. J. Petch, , J. Iron. Steel Res Inst., 174, pp.25~ (1953)
- Tomotake Hirata, , Mater. Sci. Eng. A, 456, pp.344~ (2007)