숄더 지름과 회전 속도에 따른 AZ31 마그네슘합금의 마찰교반접합 특성
Characteristics of Friction Stir Welded AZ31 Mg Alloys with Shoulder Diameter and Rotating Speed
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Friction stir welding (FSW) is a relatively new joining technique particularly for magnesium and aluminum alloys that are difficult to fusion weld. In this study, AZ31 Mg alloys were joined by FSW with shoulder diameter 11, 19 mm and rotating speed 900, 1200, 1500, 1800 rpm. The shoulder diameter and welding speed depended on the heat input during FSW process. As a result, the microstructures of stir zone were a fine grain by dynamic recrystallization. According to the larger shoulder diameter and the higher rotating speed, refined grain sizes of stir zone were grown by higher heat input, and the microhardness of stir zone was lower. The tensile strength at the shoulder diameter 19 mm, rotating speed 900 rpm was obtained maximum value. This value compared with the base metal was over 93%.
Abstract
Friction stir welding (FSW) is a relatively new joining technique particularly for magnesium and aluminum alloys that are difficult to fusion weld. In this study, AZ31 Mg alloys were joined by FSW with shoulder diameter 11, 19 mm and rotating speed 900, 1200, 1500, 1800 rpm. The shoulder diameter and welding speed depended on the heat input during FSW process. As a result, the microstructures of stir zone were a fine grain by dynamic recrystallization. According to the larger shoulder diameter and the higher rotating speed, refined grain sizes of stir zone were grown by higher heat input, and the microhardness of stir zone was lower. The tensile strength at the shoulder diameter 19 mm, rotating speed 900 rpm was obtained maximum value. This value compared with the base metal was over 93%.
참고문헌 (10)
- Richard Johnson, , 4th FSW Symposium (2003)
- Michael M. Avedesian, "ASM Specialty Handbook", 12~ (1999)
- W. M. Thomas, "International Patent Application No. PCT", GB92 Patent Application No. 9125978.8, 1991
- Φ. Frigaard, , 1st FSW Symposium (1999)
- 고영봉, "프루브 길이에 따른 A5052 겹치기 마찰교반접합 특성", 한국표면공학회지, 42(6), pp.294~300 (2009), 한국표면공학회
- Y. -B. Ko, , Journal of KWJS, 27, pp.595~ (2009)
- Z. W. Chen, , Materials Science and Engineering A, 474, pp.312~ (2008)
- 고영봉, "A5052-H112 합금의 겹치기 마찰교반접합 건전성", 대한용접접합학회지, 28(1), pp.34~40 (2010), 대한용접접합학회
- 고영봉, "5052 알루미늄 합금에서 접합변수에 따른 겹치기 마찰교반접합부의 특성", 한국표면공학회지, 45(5), pp.181~187 (2012), 한국표면공학회[DOI]
- L. Cederqvist, , The Welding Journal Research Supplement, 80, pp.281~ (2001)