Influences of the Eu Concentration and the Milling Time on Photoluminescence Properties of Y2O3-H3BO3:Eu3+ Powders Prepared by Mechanical Alloying
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Y2O3–H3BO3:Eu3+ powders are synthesized using a mechanical alloying method, and their photoluminescence (PL) properties are investigated through luminescence spectrophotometry. For samples milled for 300 min, some Y2O3 peaks ([222], [440], and [622]) and amorphous formations are observed. The 300-min-milled mixture annealed at 800°C for 1 h with Eu = 8 mol% has the strongest PL intensity at every temperature increase of 100°C (increasing from 700 to 1200°C in 100°C increments). PL peaks of the powder mixture, as excited by a xenon discharge lamp (20 kW) at 240 nm, are detected at approximately 592 nm (orange light, 5Do → 7F1), 613 nm, 628 nm (red light, 5Do → 7F2), and 650 nm. The PL intensity of powder mixtures milled for 120 min is generally lower than that of powder mixtures milled for 300 min under the same conditions. PL peaks due to YBO3 and Y2O3 are observed for 300-min-milled Y2O3–H3BO3 with Eu = 8 mol% after annealing at 800°C for 1 h.
Abstract
Y2O3–H3BO3:Eu3+ powders are synthesized using a mechanical alloying method, and their photoluminescence (PL) properties are investigated through luminescence spectrophotometry. For samples milled for 300 min, some Y2O3 peaks ([222], [440], and [622]) and amorphous formations are observed. The 300-min-milled mixture annealed at 800°C for 1 h with Eu = 8 mol% has the strongest PL intensity at every temperature increase of 100°C (increasing from 700 to 1200°C in 100°C increments). PL peaks of the powder mixture, as excited by a xenon discharge lamp (20 kW) at 240 nm, are detected at approximately 592 nm (orange light, 5Do → 7F1), 613 nm, 628 nm (red light, 5Do → 7F2), and 650 nm. The PL intensity of powder mixtures milled for 120 min is generally lower than that of powder mixtures milled for 300 min under the same conditions. PL peaks due to YBO3 and Y2O3 are observed for 300-min-milled Y2O3–H3BO3 with Eu = 8 mol% after annealing at 800°C for 1 h.
참고문헌 (18)
- E. Arzt, "New Materials Mechanical Alloying Techniques", pp.3~ (1988), DGM
- D. Roy, , J. Alloys Compd., 460, pp.320~ (2008)
- S. Kumaran, , Powder Technol., 185, pp.124~ (2008)
- H. G. Kim, , Inter. J. Non-Equilibrium Processing, 10, pp.305~ (1998)
- C. C. Koch, , Appl. Phys. Lett., 43, pp.1017~ (1983)
- R. B. Schwartz, , J. Non-Cryst. Solids, 76, pp.281~ (1985)
- M. K. Chong, , J. Phys. Chem. Solids, 66, pp.213~ (2005)
- S. J. Dhoble, , Nucl. Instrum. Methods Phys. Res. B, 266, pp.3437~ (2008)
- Y. Wang, , Mater. Lett., 60, pp.2645~ (2006)
- F.-S. Chen, , J. Alloys Compd., 505, pp.L1~ (2010)
- H. S. Gong, "Photoluminescence of Y2O3-H3BO3:Eu3+ Powders by Mechanical Alloying", M.S., pp.2011
- Hyun-Sic Gong, "Formation and photoluminescence of Y2O3-H3BO3:Eu3+ powders by mechanical alloying", Current Applied Physics, 13(3), pp.453~456 (2013), 한국물리학회
- A. Yousif, , Appl. Surf. Sci., 365, pp.93~ (2016)
- X. Guo, , J. Cryst. Growth, 311, pp.2409~ (2009)
- L. Muresan, , J. Alloys Compd., 483, pp.346~ (2009)
- J. Zhang, , J. Cryst. Growth, 271, pp.207~ (2004)
- W. Pan, , Thin Solid Films, 578, pp.69~ (2015)
- Y. Tian, , J. Alloys Compd., 590, pp.61~ (2014)